CN103146040A - Special poly-wedge belt for vehicle - Google Patents
Special poly-wedge belt for vehicle Download PDFInfo
- Publication number
- CN103146040A CN103146040A CN 201310115398 CN201310115398A CN103146040A CN 103146040 A CN103146040 A CN 103146040A CN 201310115398 CN201310115398 CN 201310115398 CN 201310115398 A CN201310115398 A CN 201310115398A CN 103146040 A CN103146040 A CN 103146040A
- Authority
- CN
- China
- Prior art keywords
- percent
- wedge belt
- agent
- poly
- special poly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a special poly-wedge belt for a vehicle. The poly-wedge belt consists of the following mixed ingredients in weight percentages: 65 percent of chloroprene rubber; 5 percent of short fiber; 6 percent of bonding agent; 2 percent of anti-aging agent; 6 percent of reinforcing agent; 1 percent of zinc oxide; 2 percent of magnesium oxide; 1 percent of calcium oxide; 1 percent of sodium borate; 3 percent of active agent; and the balance of engine oil. By the adoption of the special poly-wedge belt, chemical reagents in raw materials are fewer, the special poly-wedge belt is more friendly to people, the operating noise is small, and the service life under high-speed transmission is long. After forming of polyurethane, the compactness is excellent, and thus the service life of the wedge belt is further prolonged.
Description
Technical field
The present invention relates to a kind of wedge band, relate in particular to the multi-wedge band on a kind of transmission belt that can be applicable on automobile.
Background technology
Development along with technology, growth in the living standard, people also improve day by day to the requirement of household electrical appliance used in everyday, life appliance and the condition of going out, except satisfy its functional, the aesthetics of the size of its volume, the length in work-ing life, outward appearance, the comfortableness of use etc. all become the important element of competition of product.And the importance of transmission belt in household electrical appliance, body-building apparatus and automobile that plays the transferring power effect also more and more comes into one's own, except satisfying the transmission requirement, to pursue also that its quality is light, long service life, operation noise are little, energy-conserving and environment-protective etc., transmission belt has become the important indicator of weighing the product quality.
The main glue kind that the tradition transmission belt uses is the glue kinds such as natural rubber, chloroprene rubber, terpolymer EP rubber, for satisfying the transmission requirement, need to add various chemical reagent and reinforced filling in rubber, and these chemical reagent and reinforced filling are not suitable for and the human body Long contact time; And its quality is heavier, wear resistance is relatively poor, and the work-ing life that (turns above rotating speed 6000) during high-speed cruising is also not very long; Mainly because mostly adopting the mode of polishing after moulding, it produces, due to the matrix of emery wheel through angle after sandblasting have change, add the inevitably mechanical workout factor such as when polishing machine vibration, cause angle and the belt wheel angle of transmission belt can not be in full accord, can send the noise that is difficult to accept when transmission, particularly evident when high-speed cruising.
Summary of the invention
For the deficiency that prior art exists, technical problem to be solved by this invention is that when a kind of work is provided, noise is little, wear resistance is good and the automobile specified multi-wedge band of long service life.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of automobile specified multi-wedge band, mixed by the composition of following weight percent and form:
Chloroprene rubber 65%;
Staple fibre 5%;
Tackiness agent 6%;
Anti-aging agent 2%;
Strengthening agent 6%;
Zinc oxide 1%;
Magnesium oxide 2%;
Calcium oxide 1%;
Borax 1%;
Promoting agent 3%;
The machine oil surplus.
The advantage of automobile specified multi-wedge band of the present invention is: in raw material, chemical reagent is less, and is more friendly to the people, and the operation noise is little, and the high-speed drive life-span is long.Polyurethane moulded rear density is good, has further improved the work-ing life of wedge band.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further details;
Embodiment 1:
A kind of automobile specified multi-wedge band, mixed by the composition of following weight percent and form:
Chloroprene rubber 65%;
Staple fibre 5%;
Tackiness agent 6%;
Anti-aging agent 2%;
Strengthening agent 6%;
Zinc oxide 1%;
Magnesium oxide 2%;
Calcium oxide 1%;
Borax 1%;
Promoting agent 3%;
The machine oil surplus.
Certainly, above-mentioned explanation is not to be limitation of the present invention, and the present invention also is not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, remodeling, interpolation or replacement all should belong to protection scope of the present invention.
Claims (1)
1. automobile specified multi-wedge band is characterized in that: mixed by the composition of following weight percent and form:
Chloroprene rubber 65%;
Staple fibre 5%;
Tackiness agent 6%;
Anti-aging agent 2%;
Strengthening agent 6%;
Zinc oxide 1%;
Magnesium oxide 2%;
Calcium oxide 1%;
Borax 1%;
Promoting agent 3%;
The machine oil surplus.