CN103159466A - Environment-friendly wood-grain linear stone polished tile and production method for same - Google Patents
Environment-friendly wood-grain linear stone polished tile and production method for same Download PDFInfo
- Publication number
- CN103159466A CN103159466A CN 201110408112 CN201110408112A CN103159466A CN 103159466 A CN103159466 A CN 103159466A CN 201110408112 CN201110408112 CN 201110408112 CN 201110408112 A CN201110408112 A CN 201110408112A CN 103159466 A CN103159466 A CN 103159466A
- Authority
- CN
- China
- Prior art keywords
- environment
- stone polished
- environmental protection
- clay
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an environment-friendly wood-grain linear stone polished tile and a production method for the same. The environment-friendly wood-grain linear stone polished tile is characterized in that the components needed by blank preparation comprise potassium feldspar A, potassium feldspar B, soda feldspar A, soda feldspar B, soda feldspar C, potassium-soda feldspar A, pyrophyllite, talcum, flint clay, clay A, clay B and pigment. The production method for the environment-friendly wood-grain linear stone polished tile comprises the working procedures of raw material selection, powder preparation, material distribution, press-forming, drying, roller kiln once-firing and the like. According to the production process disclosed by the invention, a longitudinally vertical distribution technology and a nonlinear circular distribution technology are additionally adopted on the basis of the traditional process, so that the surface of the product presents beautiful, graceful and smooth strip-shaped grains, and lines with different thicknesses, thus reducing a natural linear stone formation environment, and ensuring the stable physical indexes of the product simultaneously. The environment-friendly wood-grain linear stone polished tile is compact in structure, hard in tile surface, more anti-wear, pressure-resistant, free from edge-chipping and corner-chipping, and longer in service life.
Description
Technical field
The present invention relates to a kind of vitrified tile and preparation method thereof, particularly relate to a kind of environmental protection woodgrain lines stone polished brick and preparation method thereof.
Background technology
Wood texture is a kind of native texture that liked by the human consumer, be usually used in household cloth art and relevant ornaments, be common in ceramics and series modelled after an antique on architectural pottery, limited to a certain extent the use range of product, find by market study, the polished tile product development is gone out wood grain series texture the larger market requirement is arranged, the development trend that also meets simultaneously consumer personality. larger demand is also arranged on ostentatious project simultaneously, be the satisfying the market consumers demand, people are in the urgent need to more environmental protection woodgrain lines stone polished brick series product.
Summary of the invention
The object of the invention is to solve the technical bottleneck of this series products of domestic production, and developed a kind of environmental protection woodgrain lines stone polished brick and preparation method thereof.This environmental protection woodgrain lines stone series product of the present invention's exploitation are on the basis of traditional technology, increase to adopt and pass through vertical material-distributing and non-linear samsara Strand Feeding Technique, product surface is presented elegant in appearance, smooth linear marking, the decorative pattern that thickness is alternate, the natural linear stone material that reduced become the stone ring border, guaranteed simultaneously the stable of product physical index, compact structure, brick face cause firmly, and more wear-resisting, resistance to compression is not collapsed the corner, longer service life is of a specified duration.
Technical solution of the present invention is: this environmental protection woodgrain lines stone polished brick is characterized in that the blank of this environmental protection woodgrain lines stone polished brick is prepared required component and weight percent thereof:
A potassium felspar sand sand 15-22%;
B potassium felspar sand sand 6-11%;
A albite 9-10%;
The long 10-12% of B sodium;
C albite 8-11%;
A potassium albite 7-10%;
Agalmatolite 18-22%;
Talcum 0.9-2.5%;
Flint clay 3-5%;
A clay 18-26%;
B clay 12-15%;
Colorant 1.0-2.5%.
The blank required Chemical Composition of preparation and the content of this environmental protection woodgrain lines stone polished brick
SiO
2
70.00--75.00%;
AL
2
O
3
20.00-25.00%;
Fe
2
O
3
<1%;
TiO
3
<0.9%;
CaO <1.50%;
MgO 1.5-1.9%;
K
2
O 2.80-3.30%;
Na
2
O 2.00-2.60%;
I.L <6.8%。
The preparation method of this environmental protection woodgrain lines stone polished brick that the present invention provides, be characterized in being formed by operations such as picking of raw material, preparation, cloth, press forming, drying, roller kiln once-firings, vertical material-distributing and non-linear samsara cloth are passed through in employing, be shaped through all-hydraulic automatic brick pressing machine, pass through the roller kiln once-firing, edging is according to the demand of product again, select glossing, obtain at last finished product.
Compared with prior art, the invention has the beneficial effects as follows:
1, the texture that possesses lithotome: the linear texture of reduction lithotome true to nature.
2, fine quality: through the great tonnage press compacting, high-temperature calcination forms, and has excellent physicochemical property, and the product density is high, and water-intake rate is low, and antifouling ability is strong, product hard wear resistant, acidproof, alkaline-resisting, good weatherability, long service life.
3, environmental protection: environmental protection raw material preparation that selected high purity is radiationless, stop radiation and pollution substance, simultaneously the outstanding ability of its anti-soil rot-resistant, can allow the space that is covered with keep clean, safety and environmental protection is effectively safeguarded the cleaning of domestic environment, ensures household's physical and mental health.
4, applied range: product integrates practicality, artistry, and lay on the decorating inner and external walls and the ground that are widely used in hotel, villa mountain villa, hotel lobby, room, office space, restaurant, recreation center, market.
Description of drawings
Fig. 1 is process flow sheet of the present invention.
Embodiment
Embodiment
The blank required component of preparation and the weight percent thereof of this environmental protection woodgrain lines stone polished brick:
A potassium felspar sand sand 15%, B potassium felspar sand sand 8%, A albite 10%, talcum 0.9-2.5%,
Long 10%, the C albite 8% of B sodium, A potassium albite 10%, agalmatolite 18%,
Flint clay 3-5%, the clay surplus.
The blank required Chemical Composition of preparation and the content of this environmental protection woodgrain lines stone polished brick
AL
2
O
3
20.00%,Fe
2
O
3
0.6%,TiO
3
0.4%,CaO 1.20%,
MgO 1.5%, K
2
O 2.80%, Na
2
O 2.00%, and I.L 6.0%, SiO
2
Surplus.
Each component ponding and the additive of blank are added the ball mill grinding and mix by pulp storage tank, carry out spray method powder process, powder enters filler bin, pass through vertical material-distributing and non-linear samsara cloth, be shaped through the all-hydraulic automatic brick pressing machine of industry maximum (KD7800 ton), then pass through the roller kiln once-firing, edging, according to the demand of product, select glossing, obtain at last finished product.
The technical indicator of this environmental protection woodgrain lines stone polished brick that the present invention provides sees the following form:
The technical indicator contrast table
Claims (3)
1. environmental protection woodgrain lines stone polished brick is characterized in that the blank required component of preparation and the weight percent thereof of this environmental protection woodgrain lines stone polished brick:
A potassium felspar sand sand 15-22%,
B potassium felspar sand sand 6-11%,
A albite 9-10%,
The long 10-12% of B sodium,
C albite 8-11%,
A potassium albite 7-10%,
Agalmatolite 18-22%,
Talcum 0.9-2.5%,
Flint clay 3-5%,
A clay 18-26%,
B clay 12-15%,
Colorant 1.0-2.5%.
2. environmental protection woodgrain lines stone polished brick according to claim 1 is characterized in that the blank required Chemical Composition of preparation and the content of this environmental protection woodgrain lines stone polished brick:
SiO
2 70.00--75.00%,
AL
2O
3 20.00-25.00%,
Fe
2O
3 <1%,
TiO
3 <0.9%,
CaO <1.50%,
MgO 1.5-1.9%,
K
2O 2.80-3.30%,
Na
2O 2.00-2.60%,
I.L <6.8%。
3. the preparation method of environmental protection woodgrain lines stone polished brick claimed in claim 1, it is characterized in that being formed by operations such as picking of raw material, preparation, cloth, press forming, drying, roller kiln once-firings, vertical material-distributing and non-linear samsara cloth are passed through in employing, be shaped through all-hydraulic automatic brick pressing machine, pass through the roller kiln once-firing, edging is according to the demand of product again, select glossing, obtain at last finished product.