CN103144307A - 一种高温树脂高耐磨摩擦块的制作方法 - Google Patents

一种高温树脂高耐磨摩擦块的制作方法 Download PDF

Info

Publication number
CN103144307A
CN103144307A CN2013100539436A CN201310053943A CN103144307A CN 103144307 A CN103144307 A CN 103144307A CN 2013100539436 A CN2013100539436 A CN 2013100539436A CN 201310053943 A CN201310053943 A CN 201310053943A CN 103144307 A CN103144307 A CN 103144307A
Authority
CN
China
Prior art keywords
wear
temperature resin
friction block
high temperature
brake pad
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013100539436A
Other languages
English (en)
Other versions
CN103144307B (zh
Inventor
贾明昌
贾正
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Gucheng pneumatic friction sealing material Co., Ltd.
Original Assignee
贾明昌
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 贾明昌 filed Critical 贾明昌
Priority to CN201310053943.6A priority Critical patent/CN103144307B/zh
Publication of CN103144307A publication Critical patent/CN103144307A/zh
Application granted granted Critical
Publication of CN103144307B publication Critical patent/CN103144307B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高温树脂高耐磨摩擦块的制作方法，其特征在于：采用高温树脂40％-60％、200目铜粉10％-15％、二硫化钼2％-5％、碳纤维3％-5％、耐磨碳黑3％-5％、玻纤粉20％-30％作为原料，依次经混料、称重、高压冷压成型、加温烧结、自然降温、高压定型、表面加工制做工艺生产高温树脂高耐磨摩擦块。其大大提高了摩擦块的摩擦系数、冲击强度及使用温度等参数，降低了磨损率，延长了摩擦块在设备上的使用周期，减少了企业的设备维护成本，环保无污染。

Description

一种高温树脂高耐磨摩擦块的制作方法
技术领域
本发明涉及一种制动摩擦块，尤其涉及一种高温树脂高耐磨摩擦块的制作方法。
背景技术
摩擦块采用耐磨材料制成，主要用于离合器及制动器上。目前的酚醛树脂摩擦块通常采用酚醛树脂、石棉等材料经高温热固、热处理、表面加工等工艺制成，摩擦系数0.36-0.38，冲击强度4-5公斤，耐温100℃-160℃，磨耗率0.58-1.23，硬度HR118。当酚醛树脂摩擦块应用于锻压设备、冲压设备、摩擦压力机等大型压力设备时，磨损较快，更换周期短，增加了企业的运行成本；且其容易破碎，对离合器和制动器的花盘造成损伤，给企业带来经济损失。由于酚醛树脂中含有石棉材料，随着摩擦块的磨损，会产生含有石棉的细小粉尘，易致呼吸系统疾病，危害车间人员的人身健康。
发明内容
本发明的目的在于提供一种耐磨性能好，使用周期长，不含石棉，安全环保的高温树脂高耐磨摩擦块。
为实现上述技术目的，本发明采用以下技术方案：一种高温树脂高耐磨摩擦块的制作方法，其特征在于：采用高温树脂40％-60％、200目铜粉10％-15％、二硫化钼2％-5％、碳纤维3％-5％、耐磨碳黑3％-5％、玻纤粉20％-30％作为原料，依次经混料、称重、高压冷压成型、加温烧结、自然降温、高压定型、表面加工制做工艺生产高温树脂高耐磨摩擦块。
本发明具有以下有益效果：其大大提高了摩擦块的摩擦系数、冲击强度及使用温度等参数，降低了磨损率，延长了摩擦块在设备上的使用周期，是以往同类产品的5倍以上，尤其适用于大型的锻压设备和冲压设备，减少了企业对设备维护成本。由于其原料中不含石棉，且耐磨性较好，在设备运行中不会产生大量石棉粉尘，环保无污染，可避免对车间人员造成呼吸系统病害。
具体实施方式
实施例一
将高温树脂40kg、200目铜粉15kg、二硫化钼5kg、碳纤维5kg、耐磨碳黑5kg、玻纤粉30kg作为原料，依次经混料，称重，高压冷压成型，加温烧结，自然降温，高压定型，表面加工工艺制成高温树脂高耐磨摩擦块。
经检验，其摩擦系数0.40，冲击强度16公斤，耐温160℃，磨耗率0.08，硬度HR90。
实施例二
将高温树脂60kg、200目铜粉10kg、二硫化钼2kg、碳纤维4kg、耐磨碳黑4kg、玻纤粉20kg作为原料，依次经混料，称重，高压冷压成型，加温烧结，自然降温，高压定型，表面加工工艺制成高温树脂高耐磨摩擦块。
经检验，其摩擦系数0.45，冲击强度18公斤，耐温280℃，磨耗率0.08，硬度HR90。
实施例三
将高温树脂53kg、200目铜粉12kg、二硫化钼4kg、碳纤维3kg、耐磨碳黑3kg、玻纤粉25kg作为原料，依次经混料，称重，高压冷压成型，加温烧结，自然降温，高压定型，表面加工工艺制成高温树脂高耐磨摩擦块。
经检验，其摩擦系数0.38，冲击强度15公斤，耐温100℃，磨耗率0.08，硬度HR90。
用户案例
1、XX锻造(长春)有限公司
该单位的WTP315压床采用原酚醛树脂摩擦块，使用周期为两周到三个月不等，摩擦块更换频繁。2010年3月份，采用高温树脂高耐磨摩擦块后(离合器、制动器均使用)，每天双班生产，使用一年多，未进行过更换或调整，设备仍正常运行，显著降低维护成本，目前正向锻压机推广使用。
2、XX锻造有限公司
该单位于2008年3月份，分别在25MN锻压机及20MN锻压机离合器上选用高温树脂高耐磨摩擦块，两台设备双班连续生产，使用近8个月后进行验证，该产品表现出磨损小(8个月磨损仅为1mm)，无碎裂，发热量低等优点，预计使用寿命可达1年以上。降低了设备停机时间，减少了维护费用，最终提高了生产效率。
3、广东XX机床厂有限公司
该单位之前使用进口摩擦块，于2009年7月份选用高温树脂高耐磨摩擦块，经技术检测及装机实验，其高耐磨、环保型，各项技术指标达到或超过国外同类产品，可满足设备需要，代替同类进口产品，节省外汇。
4、山东XX转向节总厂
该单位2008年10月份在锻造设备上选用高温树脂高耐磨摩擦块，双班连续生产，使用寿命在七个月以上，效果良好，降低了设备维护成本，提高了生产效率，节省了资源。

Claims (1)

1.一种高温树脂高耐磨摩擦块的制作方法，其特征在于：采用高温树脂40％-60％、200目铜粉10％-15％、二硫化钼2％-5％、碳纤维3％-5％、耐磨碳黑3％-5％、玻纤粉20％-30％作为原料，依次经混料、称重、高压冷压成型、加温烧结、自然降温、高压定型、表面加工制做工艺生产高温树脂高耐磨摩擦块。
CN201310053943.6A 2013-01-17 2013-01-17 一种高温树脂高耐磨摩擦块的制作方法 Active CN103144307B (zh)