CN103132610A - Double-face composite-mortar intensified heat retaining panel

Info

Publication number: CN103132610A
Application number: CN2011103717864A
Authority: CN
Inventors: 苏畅
Original assignee: Individual
Current assignee: Individual
Priority date: 2011-11-22
Filing date: 2011-11-22
Publication date: 2013-06-05

Abstract

A double-face composite-mortar intensified heat retaining panel comprises a substrate. The substrate is formed by splicing of multiple vertical fiber rock wool plates. A glass fiber cloth layer is adhered to the upper end face of the substrate, a glass fiber cloth layer is adhered to the lower end face of the substrate, a mortar layer is uniformly coated on the glass fiber cloth layer on the upper end face of the substrate, a mortar layer is uniformly coated on the glass fiber cloth layer on the lower end face of the substrate, and each vertical fiber rock wool plate is formed through the practice that a flat fiber rock wool big plate is cut along the vertical direction of a fiber. According to the heat retaining panel, the wholeness is strong, strength requirements of adhesive bonding of an external wall are met, and the adhesive bonding is firm.

Description

The warming plate that a kind of two-sided composite mortar strengthens

Technical field

The present invention relates to the warming plate that a kind of two-sided composite mortar strengthens.

Background technology

existing rock wool heat-preservation sheet material, because its processing method is laminate adhesive, it has in fiber parallel direction pulling capacity minimum, the characteristics that material is loose, mostly be applied in interlayer, as clog dry-hang stone inside etc., as not adopting filling technique, and adopt the thin technique of wiping one's face, flat fiber bulk sheet material is in the bonding application of metope, general bonding insecure, be difficult to reach the requirement of exterior wall adhesive strength, therefore adopt the rock cotton board of the thin technique of wiping one's face to adopt the vertical bonding mode of fiber, can only produce the thick flat fibrous plate of 150 mm but in international coverage, existing production technology is the thickest, therefore vertical fibrous plate can only be made the wide batten of 150 mm, globality is not strong, because vertical fiber is not easy with mortar bonding, cause bonding process and loaded down with trivial details and be not easy to control quality.

Summary of the invention

Purpose of the present invention is to provide the warming plate that a kind of two-sided composite mortar strengthens.

The technical scheme that adopts is:

The warming plate that a kind of two-sided composite mortar strengthens comprises substrate, and substrate is to be made of many vertical fiber rock wool plates or block of glass wool amalgamation;

Be pasted with the glass fiber layer of cloth in the upper surface of substrate, be pasted with the glass fiber layer of cloth in the lower surface of substrate, be coated with uniformly screed on the glass fiber layer of cloth of upper surface, be coated with uniformly screed on the glass fiber layer of cloth of lower surface;

Above-mentioned vertical fiber rock wool plate or block of glass wool are to be cut into along the fiber vertical direction by the large plate of flat fiber rock wool or the large plate of glass rock wool;

Above-mentioned screed is the anticracking grout that can buy on market.

Owing to doing sand finish with machine on vertical fiber rock wool plate or block of glass wool before dispatching from the factory, can guarantee constant temperature and the operation that conforms, can guarantee that mortar and vertical fiber rock wool plate or block of glass wool are bonding firmly evenly, and the sheet material after compound can be cut into the large plate the same with common warming plates such as XPS plates and need not one little bonding with one little, thereby can raise the efficiency greatly, and improve construction quality.

The invention has the advantages that:

The present invention's size of sheet material as required cuts out sheet material, and globality is strong, has eliminated simultaneously the impact of job site environment, has satisfied the bonding requirement of strength of exterior wall, and is bonding firm.

Description of drawings

Fig. 1 is cross section view schematic diagram of the present invention.

The specific embodiment

The warming plate that a kind of two-sided composite mortar strengthens comprises substrate 1, and substrate 1 is to be made of many vertical fiber rock wool plates or block of glass wool amalgamation;

Be pasted with glass fiber layer of cloth 2 in the upper surface of substrate 1, be pasted with glass fiber layer of cloth 3 in the lower surface of substrate 1, be coated with uniformly screed 4 on the glass fiber layer of cloth 2 of upper surface, be coated with uniformly screed 5 on the glass fiber layer of cloth 3 of lower surface;

Above-mentioned vertical fiber rock wool plate or block of glass wool are to be cut into along the fiber vertical direction by the large plate of flat fiber rock wool or the large plate of glass wool;

The anticracking grout of above-mentioned screed 4 and 5 for having bought on market.

Claims

1. the warming plate that two-sided composite mortar strengthens, comprise substrate (1), and it is characterized in that: substrate (1) is to be made of many vertical fiber rock wool plates or block of glass wool amalgamation;

Be pasted with glass fiber layer of cloth (2) in the upper surface of substrate (1), be pasted with glass fiber layer of cloth (3) in the lower surface of substrate (1), be coated with uniformly screed (4) on the glass fiber layer of cloth (2) of upper surface, be coated with uniformly screed (5) on the glass fiber layer of cloth (3) of lower surface;

Above-mentioned vertical fiber rock wool plate or block of glass wool are to be cut into along the fiber vertical direction by the large plate of flat fiber rock wool or the large plate of glass wool.