CN103132024A - Surface metallization process for plastic products - Google Patents
Surface metallization process for plastic products Download PDFInfo
- Publication number
- CN103132024A CN103132024A CN2013100772360A CN201310077236A CN103132024A CN 103132024 A CN103132024 A CN 103132024A CN 2013100772360 A CN2013100772360 A CN 2013100772360A CN 201310077236 A CN201310077236 A CN 201310077236A CN 103132024 A CN103132024 A CN 103132024A
- Authority
- CN
- China
- Prior art keywords
- plastic
- metallization process
- base body
- surface metallization
- plastic products
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a surface metallization process for plastic products. The surface metallization process comprises the following steps of: firstly, cleaning a plastic base body and removing the impurity on the surface of the plastic base body; then, putting the plastic base body to hydrogen peroxide for roughening treatment for 30-40 minutes; and finally, putting the roughened plastic base body to a vacuum environment and forming a metal film on the surface of the plastic base body through evaporation and condensation of metal filaments. The surface metallization process has the beneficial effects that the process is delicate and the treated products are excellent; the operation is convenient by improving the conventional surface metallization process of the plastic products; the use and residues of the heavy metal ions are avoided; the pollution is reduced; and the resources are saved.
Description
Technical field
The present invention relates to field of plastic products, specifically, specially refer to a kind of surface of plastic products metallization process.
Background technology
Plastics are synthetic macromolecular compound { polymkeric substance (polymer) }, can be described as again polymer or giant molecule (macromolecules), be also plastics (plastics) or the resin (resin) that generally is commonly called as, can freely change the body pattern.Be the material that utilizes raw material monomer to be polymerized with synthetic or condensation reaction, formed by additives such as synthetic resins and filler, softening agent, stablizer, lubricant, colorants.
The main component of plastics is synthetic resins.This noun of resin is to be gained the name by the oozy lipid of animals and plants at first, and as rosin, shellac etc., resin refers to not yet the superpolymer that mixes with various additives.Resin accounts for 40%～100% of plastics gross weight.The fundamental property of plastics depends mainly on the person's character of resin, but additive also plays an important role.Some plastics is comprised of synthetic resins basically, does not contain or contain less additive, as organic glass, polystyrene etc.
Application number is a kind of method that the patent application document of 201210089232.X discloses plastic-metal.Its purpose is to provide a kind of use and remnants that reduce heavy metal ion, reduce pollute, economize on resources, the method for plastic-metal easy and simple to handle.The present invention adopts following technical proposals to realize, it comprises the following steps: A) plastic substrate is inserted roughening treatment in H2O2 and H2SO4 solution; B) after the plastics after roughening treatment being carried out ultrasonic wave water washing, drying up, insert activation treatment in metal nanoparticle solution; C) will insert plating in copper electrolyte by the plastics after activation treatment.The defective of this technique is the pollution of environment comparatively serious.
In sum, for the defective of prior art, need especially a kind of surface of plastic products metallization process, to solve the deficiencies in the prior art.
Summary of the invention
The object of the present invention is to provide a kind of surface of plastic products metallization process, by traditional plastic product surface metallization process is improved, easy and simple to handle, use and the remnants of heavy metal ion have been avoided, reduce and pollute, economize on resources, thereby realized purpose of the present invention.
Technical problem solved by the invention can realize by the following technical solutions:
A kind of surface of plastic products metallization process, he comprises the steps:
1) at first plastic substrate is cleaned, remove its surface with impurity;
2) then plastic substrate is inserted and carry out roughening treatment 30-40 minute in hydrogen peroxide;
3) plastic substrate that roughening treatment is complete is as in vacuum environment at last, and evaporation and Ning Jie ﹐ by filament form metallic film at plastic surface.
In one embodiment of the invention, described filament is one or more in aluminium, tin, copper and mickel.
In one embodiment of the invention, the thickness of described metallic film is the 0.1-0.2 millimeter.
Beneficial effect of the present invention is: technique is ingenious, and product is superior, and is easy and simple to handle by traditional plastic product surface metallization process is improved, and avoided use and the remnants of heavy metal ion, reduces and pollute, and economizes on resources.
Embodiment
For technique means, creation characteristic that the present invention is realized, reach purpose and effect is easy to understand, below in conjunction with embodiment, further set forth the present invention.
A kind of surface of plastic products metallization process of the present invention, he comprises the steps:
1) at first plastic substrate is cleaned, remove its surface with impurity;
2) then plastic substrate is inserted and carry out roughening treatment 30-40 minute in hydrogen peroxide;
3) plastic substrate that roughening treatment is complete is as in vacuum environment at last, and evaporation and Ning Jie ﹐ by filament form metallic film at plastic surface.
It should be noted that described filament can be to be one or more in aluminium, tin, copper and mickel, by adopting this kind design, has realized the variation of product.
Especially the thickness that it is pointed out that described metallic film is the 0.1-0.2 millimeter, under the prerequisite that does not affect the plastic prod lightness, has realized the surface metalation of plastic prod.
Beneficial effect of the present invention is: technique is ingenious, and product is superior, and is easy and simple to handle by traditional plastic product surface metallization process is improved, and avoided use and the remnants of heavy metal ion, reduces and pollute, and economizes on resources.
Above demonstration and described ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; that describes in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (3)
1. a surface of plastic products metallization process, is characterized in that, he comprises the steps:
1) at first plastic substrate is cleaned, remove its surface with impurity;
2) then plastic substrate is inserted and carry out roughening treatment 30-40 minute in hydrogen peroxide;
3) plastic substrate that roughening treatment is complete is as in vacuum environment at last, and evaporation and Ning Jie ﹐ by filament form metallic film at plastic surface.
2. a kind of surface of plastic products metallization process according to claim 1, is characterized in that, described filament is one or more in aluminium, tin, copper and mickel.
3. a kind of surface of plastic products metallization process according to claim 1, is characterized in that, the thickness of described metallic film is the 0.1-0.2 millimeter.