CN106543564A - A kind of preparation method of the water plated material that can be roughened with water - Google Patents
A kind of preparation method of the water plated material that can be roughened with water Download PDFInfo
- Publication number
- CN106543564A CN106543564A CN201611047548.7A CN201611047548A CN106543564A CN 106543564 A CN106543564 A CN 106543564A CN 201611047548 A CN201611047548 A CN 201611047548A CN 106543564 A CN106543564 A CN 106543564A
- Authority
- CN
- China
- Prior art keywords
- water
- plated material
- roughened
- preparation
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of the water plated material that can be roughened with water, belongs to water power plating field of material preparation.After soluble oligomeric compound is taken using surfactant process, drying, then with resin agitating mixed processing, subsequently by double screw extruder pelletize, the water plated material is obtained;The soluble oligomeric compound can be dispersed in resin surface layer in granulation process, form 0.5 ~ 3 micron of particle.Water plated material obtained in of the invention can be directly roughened with water, 10 ~ 30min of certain hour is soaked in 50 ~ 80 DEG C of water, make to be dispersed in the soluble oligomer dissolving of resin surface, so as to " back-off " pit is formed in resin surface, reach effect of original ABS-like using the roughening of the strong acid such as chromic acid, so as to reach the target of Chrome-free roughening, the pollution to environment is reduced, and greatly reduces production cost.
Description
Technical field
The invention belongs to water power plating field of material preparation, and in particular to a kind of water plated material that can be roughened with water
Preparation method.
Background technology
Existing water plated material is mainly based on ABS and ABS/PC alloy material classes, and in its water electroplating process, roughening is
Important step, its roughening principle are material to be corroded using the mixing of the strong acid such as chromic acid, the butadiene on surface wherein in material
Composition is corroded completely by strong acid, so as to " back-off " pit is formed on surface, provides good combination power for follow-up plating.However, thick
Change the Cr VI contained by the chromic acid in liquid and can cause severe contamination to environment, therefore, invent and a kind of can be roughened with water
Water plated material has great significance.
The content of the invention
Present invention aims to prior art is not enough, there is provided a kind of water plated material that can be roughened with water
Preparation method.
For achieving the above object, the present invention is adopted the following technical scheme that:
A kind of preparation method of the water plated material that can be roughened with water:Take soluble oligomeric compound and utilize surfactant
After process, drying, then with resin agitating mixed processing, subsequently by double screw extruder pelletize, the water plated material is obtained;
The soluble oligomeric compound, it is better than Resin Flow, and addition is low, and resin surface layer can be dispersed in granulation process,
Form 0.5 ~ 3 micron of particle.
In double screw extruder granulation process, 140 ~ 270 DEG C of temperature control, rotating speed during screw rod shearing are 200 ~ 600r/
min。
The soluble oligomeric compound is any one in PVP, PEG and PVA.
The resin is any one in PP, PE, PA and PPO.
Resin is 100 with the mass ratio of soluble oligomeric compound:3~10.
The beneficial effects of the present invention is:Water plated material obtained in of the invention can be directly roughened with water, 50 ~
10 ~ 30min of certain hour is soaked in 80 DEG C of water, makes to be dispersed in the soluble oligomer dissolving of resin surface, so as in resin
Surface forms 0.5 ~ 3 micron " back-off " pit, reaches effect of original ABS-like using the roughening of the strong acid such as chromic acid, so as to reach
To the target of Chrome-free roughening, the pollution to environment is reduced, and greatly reduces production cost.
Description of the drawings
SEM figures of the Fig. 1 for resin surface after water plated material immersion obtained in embodiment 1;
SEM figures of the Fig. 2 for resin surface after water plated material immersion obtained in embodiment 2;
SEM figures of the Fig. 3 for resin surface after water plated material immersion obtained in embodiment 3;
SEM figures of the Fig. 4 for resin surface after water plated material immersion obtained in embodiment 4.
Specific embodiment
Below in conjunction with specific embodiment, the present invention will be further described, but the present invention is not limited only to these embodiments.
Embodiment 1
A kind of preparation method of the water plated material that can be roughened with water:After PVP is taken using surfactant process, dry
It is dry, then with PP resin agitating mixed processing, PP resins are 100 with the mass ratio of PVP:3;Subsequently made by double screw extruder
Grain, 160 DEG C of temperature control, rotating speed is 200r/min, and the water plated material is obtained;PVP can be dispersed in PP in granulation process
Resin surface layer, forms 0.5 ~ 3 micron of particle.
Obtained water plated material is soaked into certain hour 30min in 50 DEG C of water, makes to be dispersed in PP resin surfaces
Soluble oligomer PVP dissolvings, so as to " back-off " pit is formed in resin surface, reach roughening effect, roughening aperture is 0.5
~ 3 microns.
Embodiment 2
A kind of preparation method of the water plated material that can be roughened with water:After PEG is taken using surfactant process, dry
It is dry, then with PE resin agitating mixed processing, PE resins are 100 with the mass ratio of PEG:10;Subsequently made by double screw extruder
Grain, 140 DEG C of temperature control, rotating speed is 600r/min, and the water plated material is obtained;PEG can be dispersed in PE in granulation process
Resin surface layer, forms 0.5 ~ 3 micron of particle.
Obtained water plated material is soaked into certain hour 10min in 80 DEG C of water, makes to be dispersed in PE resin surfaces
Soluble oligomer PEG dissolvings, so as to " back-off " pit is formed in resin surface, reach roughening effect, roughening aperture is 0.5
~ 1.5 microns.
Embodiment 3
A kind of preparation method of the water plated material that can be roughened with water:After PVA is taken using surfactant process, dry
It is dry, then with PA6 resin agitating mixed processing, PA6 resins are 100 with the mass ratio of PVA:5;Subsequently made by double screw extruder
Grain, 200 DEG C of temperature control, rotating speed is 300r/min, and the water plated material is obtained;PVA can be dispersed in PA6 in granulation process
Resin surface layer, forms 0.5 ~ 3 micron of particle.
Obtained water plated material is soaked into certain hour 25min in 60 DEG C of water, makes to be dispersed in PA resin surfaces
Soluble oligomer PVA dissolvings, so as to " back-off " pit is formed in resin surface, reach roughening effect, roughening aperture is 0.5
~ 2 microns.
Embodiment 4
A kind of preparation method of the water plated material that can be roughened with water:After PEG is taken using surfactant process, dry
It is dry, then with PPO resin agitating mixed processing, PPO resins are 100 with the mass ratio of PEG:6;Subsequently made by double screw extruder
Grain, 270 DEG C of temperature control, rotating speed is 400r/min, and the water plated material is obtained;PEG can be dispersed in PPO in granulation process
Resin surface layer, forms 0.5 ~ 3 micron of particle.
Obtained water plated material is soaked into certain hour 20min in 70 DEG C of water, makes to be dispersed in PPO resin surfaces
Soluble oligomer PEG dissolvings, so as to " back-off " pit is formed in resin surface, reach roughening effect, roughening aperture is 0.5
~ 2 microns.
The roughening effect of water plated material obtained in 1 embodiment 1 ~ 4 of table
The foregoing is only presently preferred embodiments of the present invention, all impartial changes done according to scope of the present invention patent with repair
Decorations, should all belong to the covering scope of the present invention.
Claims (5)
1. a kind of preparation method of the water plated material that can be roughened with water, it is characterised in that:Take soluble oligomeric compound
After surfactant process, drying, then with resin agitating mixed processing, subsequently by double screw extruder pelletize, be obtained
The water plated material;The soluble oligomeric compound can be dispersed in resin surface layer in granulation process, form 0.5 ~ 3 micron
Particle.
2. a kind of preparation method of the water plated material that can be roughened with water as claimed in claim 1, it is characterised in that:
In double screw extruder granulation process, 140 ~ 270 DEG C of temperature control, rotating speed during screw rod shearing are 200 ~ 600r/min.
3. a kind of preparation method of the water plated material that can be roughened with water as claimed in claim 1, it is characterised in that:
The soluble oligomeric compound is any one in PVP, PEG and PVA.
4. a kind of preparation method of the water plated material that can be roughened with water as claimed in claim 1, it is characterised in that:
The resin is any one in PP, PE, PA and PPO.
5. a kind of preparation method of the water plated material that can be roughened with water as claimed in claim 1, it is characterised in that:
Resin is 100 with the mass ratio of soluble oligomeric compound:3~10.