CN103131200B - 一种耐高温电线电缆料及制备方法 - Google Patents
一种耐高温电线电缆料及制备方法 Download PDFInfo
- Publication number
- CN103131200B CN103131200B CN201110382866.XA CN201110382866A CN103131200B CN 103131200 B CN103131200 B CN 103131200B CN 201110382866 A CN201110382866 A CN 201110382866A CN 103131200 B CN103131200 B CN 103131200B
- Authority
- CN
- China
- Prior art keywords
- electric wire
- parts
- screw extrusion
- thermostable
- cable material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种耐高温电线电缆料及制备方法，各主辅原料组成按质量份数为：聚合度2500树脂：100份，高分子增塑剂：45-80份，复合稳定剂：10份，碳酸钙：20份，聚乙烯蜡：0.8份，色粉：根据用户需要颜色配。本发明生产耐高温达125℃的电线电缆，且绝缘层不容易开裂，导体不容易断裂，提高了电线电缆的使用寿命和安全性。
Description
技术领域：
本发明涉及电线电缆料领域，具体涉及一种耐高温电线电缆料及制备方法。
背景技术：
在高温条件下使用的电线电缆上，比如微波炉，空调，配电房，电视机内部用线，灯座用线，汽车用线，由于电线较软，扭曲和弯曲性能好 ，绝缘层部容易开裂，一般PVC料最高使用条件为：国标为90℃，美国为105℃，欧洲为90℃，超过这个温度一般使用PE交联和EVA+PE交联料，这些料的缺点为硬度很高，电线电缆在使用中不方便，电线电缆生产后需要福照，幅照交联过程不好控制，电线电缆性能得不到保证。现有的耐高温电线电缆比较硬，在使用时由于弯曲等外力作用下，绝缘层容易开裂，导体容易断裂，安全性能不好。
发明内容：
本发明的目的是提供一种耐高温电线电缆料及制备方法，能生产耐高温达125℃的电线电缆，且绝缘层不容易开裂，导体不容易断裂，能提高电线电缆的使用寿命和安全性。
本发明的目的是这样实现的，一种耐高温电线电缆料，其特征在于： 其组成按质量份数为：
聚合度2500树脂： 100份
高分子增塑剂： 45-80份
复合稳定剂： 10份
碳酸钙： 20份
聚乙烯蜡： 0.8份
色粉： 根据用户需要颜色配。
2、根据权利要求1所述的一种耐高温电线电缆料的制备方法，其特征在于：包括以下步骤：配料→搅拌机搅拌均匀→密练机密练→双螺杆挤出→单螺杆挤出→切粒→冷却→包装。
本发明能生产耐高温达125℃的电线电缆，且绝缘层不容易开裂，导体不容易断裂，提高了电线电缆的使用寿命和安全性。
具体实施方式：
一种耐高温电线电缆料，其特征在于： 其组成按质量份数为：
聚合度2500树脂： 100份
高分子增塑剂： 45-80份
复合稳定剂： 10份
碳酸钙： 20份
聚乙烯蜡： 0.8份
色粉： 根据用户需要颜色配。
本发明包括以下步骤：配料→搅拌机搅拌均匀→密练机密练→双螺杆挤出→单螺杆挤出→切粒→冷却→包装。具体实施时，根据配方准确称取各种原料，投入到500升搅拌机,高速搅拌3分钟；将搅拌均匀的物料投入密练机升温度到150℃，双螺杆挤出机挤出造粒，温度控制在180-200℃之间，再单螺杆挤出机挤出造粒，控制在180-190℃之间，切粒、冷却、包装。
Claims (2)
1.一种耐高温电线电缆料，其特征在于：各主辅原料组成按质量份数为：
聚合度2500树脂： 100份
高分子增塑剂： 45-80份
复合稳定剂： 10份
碳酸钙： 20份
聚乙烯蜡： 0.8份
色粉： 根据用户需要颜色配；
配料通过搅拌机搅拌→密练机密练→双螺杆挤出→单螺杆挤出→切粒→冷却→包装的加工步骤完成生产。
2.根据权利要求1所述的一种耐高温电线电缆料的制备方法，其特征在于：所述的加工步骤：配料→搅拌机搅拌均匀，高速搅拌3分钟→密练机密练，升温度到150℃→双螺杆挤出，温度控制在180-200℃之间→单螺杆挤出，温度控制在180-190℃之间，→切粒→冷却→包装。