CN103128251A - 组合式离心浇注金属模具 - Google Patents

组合式离心浇注金属模具 Download PDF

Info

Publication number
CN103128251A
CN103128251A CN 201110397259 CN201110397259A CN103128251A CN 103128251 A CN103128251 A CN 103128251A CN 201110397259 CN201110397259 CN 201110397259 CN 201110397259 A CN201110397259 A CN 201110397259A CN 103128251 A CN103128251 A CN 103128251A
Authority
CN
China
Prior art keywords
embedded sleeve
mold body
embedded
heat
casting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201110397259
Other languages
English (en)
Inventor
徐金兰
贾维静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201110397259 priority Critical patent/CN103128251A/zh
Publication of CN103128251A publication Critical patent/CN103128251A/zh
Pending legal-status Critical Current

Abstract

本发明如图示，镶套(3)是镶嵌在模具体(1)内，因镶套(3)是和浇铸铁水接触较近，在浇铸过程中，模具体(1)里镶套(3)频繁受到铁水的热冲击，但是镶套(3)壁厚薄，其内部收到热冲击产生的应力较小。应力的裂纹扩展受到镶套结构的限制。同样模具体(1)因为不是直接和铁水接触，但是因收到镶套(3)传递的热量，也是频繁受到热冲击，但是相对镶套(3)来说，程度较轻，也阻止了镶套(3)裂纹的扩展的。模具体(1)采用45钢，镶套用45钢需按照一定的周期进行热处理，消除镶套(3)的内应力，防止裂纹的扩展。如果镶套(3)损坏，就可以通过更换方法来解决，整个模具体(1)还可以重复使用，所以生产成本减低。

Description

组合式离心浇注金属模具
所属技术领域
本发明涉及气缸套离心浇铸用金属浇铸模具的结构设计及材质。
背景技术
目前，气缸套行业多采用离心浇铸，离心浇铸所使用的模具都是金属模具，通常都是采用普通灰铸铁的材质，但是因为浇铸过程多采用水冷却，金属模具频繁的受到热冲击，模具的断裂现象很严重，使用寿命很短，模具成本占生产成本的很大的比重。
发明内容
本发明提供一种模具结构及材质，这种这种材质的模具耐热冲击，同时这结构也可以更换耐热圈，便于及时的修复。
本发明解决其技术问题所采用的技术方法是：浇铸时金属模具壁虽然有隔热的涂料，但是浇铸时，金属液体是很高的热量传递模具，同时模具外壁采用水冷却，造成了模具内外有很大的温差，这样的频繁的热冲击使模具的内应力不断增加，内应力存在致使模具的表面产生裂纹，气缸套离心浇铸模具多是断裂失效。本发明就是选择特定材质的镶套，来解决模具的断裂问题。
本发明的有益效果是，降低生产制造成本，延长使用寿命。
附图说明。
下面结合附图对本发明的模具结构作进一步的说明。
图中1.模具体，2.挡圈，3.镶套。
具体实施方式
如图所示，挡圈(2)在模具体(1)里起固定隔热垫片的作用，镶套(3)是镶嵌在模具体(1)内，因镶套(3)是和浇铸铁水接触较近，在浇铸过程中，模具体(1)里镶套(3)频繁受到铁水的热冲击，但是镶套(3)壁厚薄，其内部收到热冲击产生的应力较小。应力的裂纹扩展受到镶套结构的限制。同样模具体(1)因为不是直接和铁水接触，但是因收到镶套(3)传递的热量，也是频繁受到热冲击，但是相对镶套(3)来说，程度较轻，也阻止了镶套(3)裂纹的扩展的。模具体(1)采用45钢，镶套用45钢需按照一定的周期进行热处理，消除镶套(3)的内应力，防止裂纹的扩展。如果镶套(3)损坏，就可以通过更换方法来解决，整个模具体(1)还可以重复使用，所以生产成本减低。

Claims (2)

  1. 模具结构及材质其特征是：
    1.模具体采用45钢，镶套用45钢需按照一定的周期进行热处理。
  2. 2.采用镶套结构。
CN 201110397259 2011-11-30 2011-11-30 组合式离心浇注金属模具 Pending CN103128251A (zh)