CN103122173A - Expansive fire-retardant paint - Google Patents
Expansive fire-retardant paint Download PDFInfo
- Publication number
- CN103122173A CN103122173A CN2012105749243A CN201210574924A CN103122173A CN 103122173 A CN103122173 A CN 103122173A CN 2012105749243 A CN2012105749243 A CN 2012105749243A CN 201210574924 A CN201210574924 A CN 201210574924A CN 103122173 A CN103122173 A CN 103122173A
- Authority
- CN
- China
- Prior art keywords
- parts
- retardant paint
- paint
- water
- fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides expansive fire-retardant paint which comprises the following raw materials in parts by weight: 21.0 parts of ammonium polyphosphate, 11.5 parts of pentaerythritol, 11.5 parts of melamine, 4.7 parts of titanium white, 1.0 part of 10% sodium hexametaphosphate, 3.7 parts of 3% hexamethyl cellulose, 11.2 parts of chlorinated paraffin wax, 18.2 parts of water and 7.2 parts of trichloroethyl phosphate toughened polyvinyl acetate emulsion. The paint provided by the invention is non-toxic and harmless, has zero radioactivity, is high in weather resistance and light fastness and favorable in environment-friendly adsorption capacity, and can not be decolorized when being used for a long time.
Description
Technical field
The present invention relates to a kind of coating, be specifically related to a kind of expanding fire-proof paint.
Background technology
So-called coating is to be coated in protected or decorated body surface; and can form with coated article the continuous film of firm attachment, normally take resin or oil or emulsion as main, add or do not add pigment, filler; add corresponding additive, with organic solvent or the formulated thick liquid of water.Expanding fire-proof paint in the market, or contain the harmful organic solvent such as benzene, otherwise the coating adhesive ability is not strong, easily comes off with rear for a long time, does not have effective decoration and protection effect.
Summary of the invention
The invention provides a kind of expanding fire-proof paint.
The present invention is achieved by the following technical solutions:
A kind of expanding fire-proof paint, raw material and the weight part of described coating are as follows:
21.0 parts of polyphosphoric acid amine
11.5 parts of tetramethylolmethanes
11.5 parts of trimeric cyanamides
4.7 parts of titanium dioxides
10% 1.0 parts of Sodium hexametaphosphate 99s
3% 3.7 parts of hexamethyl Mierocrystalline celluloses
11.2 parts of clorafins
18.2 parts, water
7.2 parts of trichloroethyl phosphate toughened polymer acetate emulsions
Beneficial effect of the present invention is: coating of the present invention is nontoxic, harmless, "dead", and weather resisteant, photostabilization are strong, and the environmental-protection adsorption ability is strong, uses for a long time nondiscoloration.
Embodiment
The invention provides a kind of expanding fire-proof paint, the raw material and the weight part that adopt are as follows:
21.0 parts of polyphosphoric acid amine
11.5 parts of tetramethylolmethanes
11.5 parts of trimeric cyanamides
4.7 parts of titanium dioxides
10% 1.0 parts of Sodium hexametaphosphate 99s
3% 3.7 parts of hexamethyl Mierocrystalline celluloses
11.2 parts of clorafins
18.2 parts, water
7.2 parts of trichloroethyl phosphate toughened polymer acetate emulsions.
Claims (1)
1. expanding fire-proof paint is characterized in that the raw material of described coating and weight part are as follows:
21.0 parts of polyphosphoric acid amine
11.5 parts of tetramethylolmethanes
11.5 parts of trimeric cyanamides
4.7 parts of titanium dioxides
10% 1.0 parts of Sodium hexametaphosphate 99s
3% 3.7 parts of hexamethyl Mierocrystalline celluloses
11.2 parts of clorafins
18.2 parts, water
7.2 parts of trichloroethyl phosphate toughened polymer acetate emulsions.