CN103120534B - Method of weaving multi-layer carpet with polybutylece terephthalate (PBT) filament - Google Patents
Method of weaving multi-layer carpet with polybutylece terephthalate (PBT) filament Download PDFInfo
- Publication number
- CN103120534B CN103120534B CN201310048471.5A CN201310048471A CN103120534B CN 103120534 B CN103120534 B CN 103120534B CN 201310048471 A CN201310048471 A CN 201310048471A CN 103120534 B CN103120534 B CN 103120534B
- Authority
- CN
- China
- Prior art keywords
- yarn
- pbt
- carpet
- long filament
- twist
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a method of weaving multi-layer carpet with polybutylece terephthalate (PBT) filaments. The method comprises the following steps: (1) entwisting a single PBT filament to a PBT yarn with degree of twist of 250 to 270 twists per meter; (2) combining the twisted PBT yarns into a double-thread yarn, and the degree of twist is 175 to 196 twists per meter; (3) processing the PBT yarn by dying and heat shaping; (4) weaving the PBT yarn which is processed by the step (3) and a yarn without contractility on a Wilton carpet machine to get the multi-layer carpet. The multi-layer carpet is good in third dimension effect, artificial flower-cutting is not necessary during the preparation process, the problems that the quality is not stable and mass production cannot be achieved are avoided due to the artificial flower-cutting, and the cost is reduced. The method is simple, the materials used are easy to buy, and the method can be popularized and used in a wide range.
Description
Technical field
The present invention relates to a kind of method of weaving carpet, be specifically related to a kind of method with PBT long filament weaving multiple layer time carpet.
Background technology
Carpet in the market, seldom has high close mowing Wilden piece blanket.Along with the fast development of World Economics, improving constantly of living standards of the people, more and more has personalized demand to carpet product.Originally carpet is all generally plane, just on material and pattern, changes more greatly, there is no high and low layered modelling effect, and the third dimension carpet recently rising is subject to market favor.Existing stereo carpet mainly contains following several, and 1, there is relief carved carpet, 2, adopt that acrylic is high receives the stereo carpet that yarn method obtains.
Existing stereo carpet Shortcomings part: 1, there is relief carved carpet, third dimension clipping and carving is in output and limited definitely qualitatively, owing to being artificial clipping and carving, labour intensity is large, so output is not high, clipping and carving price is also very high, and everyone clipping and carving level difference, so cut dividing of next effect quality, the uniformity of property is restricted in batches, and have a V-shape angle, with the third dimension carpet of high close mowing or different.2, adopt the high yarn method of receiving of acrylic, rare, major defect is that acrylic requirement look spins contraction yarn, and disposable amount is large, has more than 20 tons, but also wants import, is difficult for finding yarn provider, and the color that carpet requires is many, and look spins acrylic and is more difficult for having bought.
Summary of the invention
The object of the present invention is to provide the method for weaving of the carpet with multilayer stereo sense that a kind of quality is good, cost is low, can apply on a large scale.
Concrete technical scheme of the present invention is as follows:
By a method for PBT long filament weaving multiple layer time carpet, comprise step: 1) yarn pretreatment; 2) yarn obtaining with pretreatment is weaved on Wilden carpet knitter; 3) gluing obtains carpet after processing;
In the present invention, the concrete steps of described step 1) are as follows:
1.1) PBT long filament list twisted weave is become to PBT yarn silk, the twist is 250～270 twists/m;
1.2) get step 1.1) the PBT yarn silk doubling twisting that obtains is made into PBT yarn 300D/2 thigh, and the twist is 175～196 twists/m;
1.3) by step 1.2) the PBT yarn that obtains carries out thermal finalization (as needs obtain coloured yarn, dyeing before thermal finalization), finally obtains contractile yarn;
Described step 2) weave carpet: be by there is no inotropic yarn and through step 1.3) shrinkage that has that obtains weaves on Wilden board, according to the layout of carpet, respectively with having shrinkage and there is no the part in inotropic yarn weaving pattern.In the layout of carpet, the part that contractile yarn is made into bounces back naturally, and does not have the part that inotropic yarn is made into not bounce back, form multi-level, have a relief carpet.
Also comprise step 4), the carpet that step 3) is obtained is lockstitched a border, the wide 0.5～1cm that lockstitches a border, and piece blanket specification is 1.4 × 2 meters～1.6 × 2.3 meters.
Described step 1.1) in sth. made by twisting to be " Z " twist with the fingers to; Described step 1.2) in sth. made by twisting to be " S " twist with the fingers to.
Described step 1.1) in, PBT long filament list twist with the fingers time, and line process in add mineral oil, the addition of mineral oil accounts for 0.5～1% of PBT long filament gross weight.While adding mineral oil in order to increase the inclusion power of yarn.
Described step 1.3) in, by step 1.2) to carry out thermal finalization be to carry out in oven heat for the PBT yarn that obtains, and the baking temperature of oven heat is controlled at 70 ℃～90 ℃, and baking time is 30 minutes～40 minutes shrinkage yarns that obtain; The shrinkage factor of PBT yarn is 21～30%.The thermal finalization of PBT yarn requires very high, through test of many times, finally decides and carries out thermal finalization by oven heat method, temperature is controlled at 90 ℃, if higher than 90 ℃, contractive effect resilience is very poor, if temperature is lower than 70 ℃, the shrinkage of yarn is not reflected, and can not use.Finally confirm that 90 ℃ is optimum, shrinkage factor reaches 21～30%.Meet production requirement.
Described step 1.1) in, the PBT monofilament that PBT long filament is 300D/72F; Described step 1.2) in, then while twisting, be the twisting of 300D/2 thigh rubber alloy;
Described step 2) be to carry out on Wilden carpet loom, woven requirement is as follows:
The 300D/2 thigh PBT yarn obtaining by step 1) and for polypropylene fiber yarn the mono-twisted filament of 800 dtexs/150F mix and knit, controlling weft density is 512 warp × (420～700) latitudes; The tension force of controlling all yarns is between 20N～25N; Suede is high is that 3.5 ~ 6.5mm weaves suede high (be preferably 4.5mm or 6mm weave suede high), then carries out gluing.
Gluing in step 3) is on Wilden gluing machine, to carry out gluing, and is undertaken by Steam Heating, and gluing speed is 1～1.5 m/min, and bake out temperature is 130 ℃ ~ 140 ℃, and drying time is 15～20 minutes, and baking oven length is 20 meters.
Be woven into after three-dimensional blanket, gluing is also a crucial process, and as gluing can make full use of the thermal contraction performance of yarn, the modelling effect of blanket will be more outstanding.The baking oven length that the present invention uses in gluing process is 20 meters, increases steam course, and controlling gluing speed is 1～1.5 m/min, and bake out temperature is 130 ℃ ~ 140 ℃, and drying time is 15～20 minutes.Make so originally to only have the high drop of 1mm suede to be increased to 1.5mm between 2mm.
In PBT long filament list sth. made by twisting process of the present invention, because single twisting has elasticity definitely, so we determine that the monofilament twist is not too high, but can not be too low, as too low embodiment does not go out elasticity, be chosen between monofilament 250～270 twists with the fingers, twist with the fingers to being that " Z " twists with the fingers to the most suitable.
PBT long filament plying process: PBT yarn silk doubling twisting; PBT yarn silk, if do not carried out 2 twisting, there will be in yarn and littlely debates sub-yarn, thereby do not produce, the twist when twist can not be higher than single twisting when PBT yarn silk doubling twisting, the twist is chosen as 175～196 twists/m, twist with the fingers to be decided to be " S " twist with the fingers to.Twisting technical requirement is higher, and twist deviation is preferably controlled in 3%, otherwise the yarn contractive effect of making is undesirable.
The yarn that there is no shrinkage that the present invention uses, as long as not having the use that can match together with PBT yarn of the yarn of shrinkage.
Along with carpet weaving technical development, can, according to thinking of the present invention, weave the carpet that obtains multiple level pattern with the yarn of different shrinkage factors.In step 1), obtain the yarn of different shrinkage factors; Step 2) in, the yarn of the different shrinkage factors that there is no inotropic yarn and obtain through step 1) is weaved on Wilden carpet knitter.
The present invention by PBT long filament through after twisting sizing, make yarn there is certain elasticity, knit with the yarn that there is no shrinkage is mixed thering is flexible PBT yarn, because the pile that does not have the yarn of shrinkage to form can not shrink, and PBT yarn has elasticity (shrinkage), its pile can shrink; Make the pile of PBT yarn formation lower than the pile that does not have the yarn of shrinkage to form, thereby form the multi-level carpet that height rises and falls.
The multi-level carpet that the present invention obtains, its modelling effect is good, in preparation process, without artificial clipping and carving, has avoided the quality that causes because of artificial clipping and carving unstable, and has been difficult to accomplish large-scale production, thereby reduced cost; And the inventive method is simple, its material using is easily buied, and can apply on a large scale.
The present invention uses PBT shrinkage yarn in carpet, changes the shortcoming of clipping and carving blanket and acrylic contraction yarn, and tool has the following advantages:
1, can spin by look, it is large that amount is not necessarily wanted, and approximately 1～2 ton just can be spun by look, and color is unrestricted;
2, form because PBT yarn can dye, if measure little, look many, yarn can dye with general colouring method, has guaranteed like this supply of the color of yarn, has reduced loss simultaneously, has reduced cost.
3, modelling effect is good, can accomplish drop at the slim silk rug of our Wilden.
Accompanying drawing explanation
Fig. 1 is schematic flow sheet of the present invention.
The specific embodiment
By a method for PBT long filament weaving multiple layer time carpet, comprise step: 1) yarn pretreatment; 2) yarn obtaining with pretreatment is weaved on Wilden loom; 3) carpet obtaining after gluing.
The concrete steps of described step 1) are as follows:
1.1) PBT long filament list is added and is twisted PBT yarn silk, the monofilament twist is 250～270 twists/m;
1.2) get step 1.1) the PBT yarn silk doubling twisting that obtains becomes 300D/2 thigh PBT yarn, and the twist is (180～190) × (103%) twist/m～(180～190) × (+103%) twist/m;
1.3) by step 1.2) the PBT yarn that obtains dyes and thermal finalization, finally obtains contractile yarn;
Described step 2) weave carpet: be by there is no inotropic yarn and through step 1.3) the contractile yarn that obtains weaves on Wilden loom, according to the layout of carpet, respectively with weaving in two kinds of yarn weaving patterns.In pattern, the part that contractile yarn is made into bounces back naturally, and does not have the part that inotropic yarn is made into not bounce back, form multi-level, have a relief carpet.
Also comprise step 4), the carpet that step 3) is obtained carries out gluing and thermal finalization.
Also comprise step 5), the carpet that step 4) is obtained is lockstitched a border, with three line machine lock seamings, and the wide 0.5～1cm that lockstitches a border, piece blanket specification is 1.4 × 2～1.6 × 2.3 meters.
Described step 1.1) in sth. made by twisting to be " Z " twist with the fingers to; Described step 1.2) in sth. made by twisting to be " S " twist with the fingers to.
Described step 1.1) in, when PBT long filament list is twisted with the fingers, in also line process mineral oil in fluid agent, the main middle inclusion power that increases yarn, addition accounts for 0.5～1% of PBT long filament gross weight.
Described step 1.3) in, by step 1.2) to carry out thermal finalization be to carry out in oven heat for the PBT yarn that obtains, and the baking temperature of oven heat is 70 ℃～90 ℃, and baking time is 30 minutes～40 minutes; The shrinkage factor 21～30% of PBT yarn.
Described step 1.1) in, the PBT monofilament that PBT long filament is 300D/72F; Described step 1.2) in, then while twisting, be the twisting of 300D/2 thigh rubber alloy.
Described step 2) be to carry out on Wilden carpet loom, woven requirement is as follows:
The 300D/2 thigh PBT yarn obtaining by step 1) and for polypropylene fiber yarn the mono-twisted filament of 800 dtexs/150F mix and knit; Controlling weft density is 512 warp × (420～700) latitudes; Controlling yarn tension is between 20N～25N, shrinks material amount and on-shrinking material and all will reach such standard; Suede is high be 4.5 and 6mm to weave suede high.
Gluing in step 3) is on Wilden gluing machine, carry out gluing and undertaken by Steam Heating, and gluing speed is 1～1.5 m/min, and the setting temperature of sizing is 130 ℃ ~ 140 ℃; The time of drying is 15～20 minutes, and baking oven length is 20 meters.
Further illustrate the present invention below in conjunction with embodiment.
Embodiment 1
1) twist and be made into PBT yarn silk with 100 kilograms of 300D/72F PBT monofilament, the twist is 250 twists/m, twist with the fingers to be " Z " twist with the fingers to, in line process also, add 0.5% the mineral oil that accounts for PBT long filament gross weight;
2) doubling twisting again, the PBT yarn silk obtaining in above-mentioned steps is twisted again, 300D/2 thigh yarn doubling twisting, the twist is 180 twists/m, twist with the fingers to be decided to be " S " twist with the fingers to.Twisted technical requirement higher, twist deviation must be controlled in 2%;
3) yarn dyeing and sizing: dyeing is determined color according to carpet pattern, the thermal finalization of yarn requires very high, adopts oven heat method to carry out thermal finalization, and oven temperature is controlled at 70 ℃, and the baking oven time is 40 minutes, and shrinkage factor reaches 28%;
4) carpet weaving operation: selected the slim blanket of Wilden board to weave.By 300D/2 thigh PBT yarn and for polypropylene fiber yarn the mono-twisted filament of 800 dtexs/150F mix and knit, control weft density and be 512 through × 700 latitudes; The tension force of controlling all yarns is 20N; Suede height is high for 6mm weaves suede; Door width is 2 meters, and length is 10 meters, 7 carpets, in pattern, contractile yarn is made into and naturally bounces back afterwards, and does not have the part that inotropic yarn is made into not bounce back, form multi-level, have a relief carpet.
5) gluing thermal finalization: carry out gluing on Wilden gluing machine, first use Steam Heating, gluing machine linear resonance surface velocity is 1.5 ms/min, and bake out temperature is controlled at 130 ℃, and drying time is 15 minutes, and baking oven length is 20 meters;
6) lock seaming: lockstitch a border with Three-thread chain stitch machine, the wide 0.5cm that lockstitches a border, piece blanket specification is 1.4 × 2 meters.
Embodiment 2
1) twist and be made into PBT yarn silk with 100 kilograms of 300D/72F PBT monofilament, the twist is 270 twists/m, twist with the fingers to be " Z " twist with the fingers to, in line process also, add 1% the mineral oil that accounts for PBT long filament gross weight;
2) doubling twisting again, the PBT yarn silk obtaining in above-mentioned steps is twisted again, 300D/2 thigh yarn doubling twisting, the twist is 190 twists/m, twist with the fingers to be decided to be " S " twist with the fingers to.Twisted technical requirement higher, twist deviation must be controlled in 3%;
3) yarn sizing: the thermal finalization of yarn requires very high, adopts oven heat method to carry out thermal finalization, and oven temperature is controlled at 90 ℃, and the baking oven time is 30 minutes, and shrinkage factor reaches 21%;
4) carpet weaving operation: selected the slim blanket of Wilden board to weave.By 300D/2 thigh PBT yarn and for polypropylene fiber yarn the mono-twisted filament of 800 dtexs/150F mix and knit, control weft density and be 512 through × 500 latitudes; The tension force of controlling all yarns is 25N; Suede height is high for 4mm weaves suede; Door width is 1.6 meters, and length is 10 meters, 7 carpets.In pattern, the part that contractile yarn is made into bounces back naturally, and does not have the part that inotropic yarn is made into not bounce back, form multi-level, have a relief carpet;
5) gluing thermal finalization: carry out gluing on Wilden gluing machine, first use Steam Heating, gluing machine linear resonance surface velocity is 1 m/min, and bake out temperature is controlled at 135 ℃, and drying time is 20 minutes, and baking oven length is 20 meters;
6) lock seaming: lockstitch a border with Three-thread chain stitch machine, lockstitch a border wide by 0.8, piece blanket specification is 1.6 × 2.3 meters.
Embodiment 3
1) twist and be made into PBT yarn silk with 100 kilograms of 300D/72F PBT monofilament, the twist is 260 twists/m, twist with the fingers to be " Z " twist with the fingers to, in line process also, add 0.7% the mineral oil that accounts for PBT long filament gross weight;
2) doubling twisting again, the PBT yarn silk obtaining in above-mentioned steps is twisted again, 300D/2 thigh yarn doubling twisting, the twist is 175 twists/m, twist with the fingers to be decided to be " S " twist with the fingers to.Twisted technical requirement higher, twist deviation must be controlled in 3%;
3) yarn sizing: the thermal finalization of yarn requires very high, adopts oven heat method to carry out thermal finalization, and oven temperature is controlled at 80 ℃, and the baking oven time is 35 minutes, and shrinkage factor reaches 30%;
4) weave operation: selected the slim blanket of Wilden board to weave.By 300D/2 thigh PBT yarn and for polypropylene fiber yarn the mono-twisted filament of 800 dtexs/150F mix and knit, control weft density and be 512 through × 420 latitudes; The tension force of controlling all yarns is 23N; Suede height is high for 3.5mm weaves suede; Door width is 1.7 meters, and length is 10 meters, 7 carpets.In pattern, the part that contractile yarn is made into bounces back naturally, and does not have the part that inotropic yarn is made into not bounce back, form multi-level, have a relief carpet;
5) gluing thermal finalization: carry out gluing on Wilden gluing machine, first use Steam Heating, gluing machine linear resonance surface velocity is 1 m/min, and bake out temperature is controlled at 140 ℃, and drying time is 18 minutes, and baking oven length is 20 meters;
6) lock seaming: lockstitch a border with Three-thread chain stitch machine, lockstitch a border wide by 0.8, piece blanket specification is 1.6 × 2.3 meters.
Embodiment 4
1) twist and be made into PBT yarn silk with 100 kilograms of 300D/72F PBT monofilament, the twist is 270 twists/m, twist with the fingers to be " Z " twist with the fingers to, in line process also, add 0.8% the mineral oil that accounts for PBT long filament gross weight;
2) doubling twisting again, the PBT yarn silk obtaining in above-mentioned steps is twisted again, 300D/3 thigh yarn doubling twisting, the twist is 196 twists/m, twist with the fingers to be decided to be " S " twist with the fingers to.Twisted technical requirement higher, twist deviation must be controlled in 3%;
3) yarn sizing: the thermal finalization of yarn requires very high, adopts oven heat method to carry out thermal finalization, and oven temperature is controlled at 85 ℃, and the baking oven time is 40 minutes, and shrinkage factor reaches 28%;
4) weave operation: selected the slim blanket of Wilden board to weave.By 300D/2 thigh PBT yarn and for polypropylene fiber yarn the mono-twisted filament of 800 dtexs/150F mix and knit, control weft density and be 512 through × 600 latitudes; The tension force of controlling all yarns is 22N; Suede height is high for 5mm weaves suede; Door width is 1.9 meters, and length is 10 meters, 7 carpets.In pattern, the part that contractile yarn is made into bounces back naturally, and does not have the part that inotropic yarn is made into not bounce back, form multi-level, have a relief carpet;
5) gluing thermal finalization: carry out gluing on Wilden gluing machine, first use Steam Heating, gluing machine linear resonance surface velocity is 1 m/min, and bake out temperature is controlled at 140 ℃, and drying time is 15 minutes, and baking oven length is 20 meters;
6) lock seaming: lockstitch a border with Three-thread chain stitch machine, lockstitch a border wide by 1, piece blanket specification is 1.4 × 2 meters.
Claims (11)
1. by a method for PBT long filament weaving multiple layer time carpet, comprise step: 1) yarn pretreatment; 2) yarn obtaining with pretreatment is weaved on Wilden carpet knitter; 3) gluing obtains carpet after processing; It is characterized in that:
Described step 1) concrete steps as follows:
1.1) PBT long filament is added and is twisted PBT long filament, the twist is 250 twists/m～270 twists/m;
1.2) get step 1.1) the synthetic bifilar PBT strand of the PBT long filament that obtains, the twist is 175 twists/m～196 twists/m;
1.3) by step 1.2) the PBT yarn that obtains carries out thermal finalization processing, finally obtains having inotropic yarn;
Described step 2) be by there is no inotropic yarn and through step 1) the contractile yarn that obtains weaves on Wilden carpet knitter: according to the layout of carpet, respectively with having shrinkage and there is no inotropic yarn weaving carpet pattern; In pattern, by the part that has shrinkage yarn to manufacture, yarn natural shrinking, and the part that does not have shrinkage yarn to manufacture, yarn does not shrink, thereby obtains pattern and have the carpet of stereovision.
2. the method with PBT long filament weaving multiple layer time carpet according to claim 1, it is characterized in that also comprising step 4), to step 3) carpet that obtains lockstitches a border, the wide 0.5cm～1cm that lockstitches a border, piece blanket specification is 1.4 meters × 2 meters～1.6 meters × 2.3 meters.
3. the method with PBT long filament weaving multiple layer time carpet according to claim 1, is characterized in that: described step 1.1) in sth. made by twisting to twist with the fingers for " Z " to; Described step 1.2) in sth. made by twisting to be " S " twist with the fingers to.
4. the method with PBT long filament weaving multiple layer time carpet according to claim 1, it is characterized in that: described step 1.1) in, PBT long filament list twist with the fingers time, and line process in add mineral oil, the addition of mineral oil accounts for 0.5%～1% of PBT long filament gross weight.
5. the method with PBT long filament weaving multiple layer time carpet according to claim 1, it is characterized in that described step 1.3) in, by step 1.2) to carry out thermal finalization be to carry out in oven heat for the PBT yarn that obtains, the temperature of oven heat is controlled at 70 ℃～90 ℃, and baking time is 30 minutes～40 minutes; The shrinkage factor of PBT yarn is controlled at 21%～30%.
6. the method with PBT long filament weaving multiple layer time carpet according to claim 1, is characterized in that: described step 1.1) in, the PBT monofilament that PBT long filament is 300D/72F; Described step 1.2) in, then while twisting, be the twisting of 300D/2 thigh rubber alloy.
7. the method with PBT long filament weaving multiple layer time carpet according to claim 1, is characterized in that: described step 2) requirements of weaving process as follows:
By step 1) the 300D/2 thigh PBT yarn that obtains and for polypropylene fiber yarn the mono-twisted filament of 800 dtexs/150F mix and knit;
Controlling weft density is 512 warp × (420～700) latitudes;
The tension force of controlling all yarns is controlled between 20N～25N;
Suede is high, and to be that 3.5～6.5mm weaves suede high.
8. the method with PBT long filament weaving multiple layer time carpet according to claim 2, it is characterized in that: step 3) in: the technological requirement of gluing is, on Wilden gluing machine, carry out, use Steam Heating simultaneously, gluing speed is 1 m/min～1.5 ms/min, bake out temperature is 130 ℃～140 ℃, and drying time is 15 minutes～20 minutes, and baking oven length is 20 meters.
9. the method with PBT long filament weaving multiple layer time carpet according to claim 1, is characterized in that: described step 1.3) in, by step 1.2) processing of first dyeing of the PBT yarn that obtains, then carry out thermal finalization.
10. the method with PBT long filament weaving multiple layer time carpet according to claim 1, is characterized in that: described step 1) in, the shrinkage factor difference of yarn obtained; Step 2) in, by there is no inotropic yarn and through step 1) yarn of the different shrinkage factors that obtain weaves on Wilden carpet knitter.
11. methods with PBT long filament weaving multiple layer time carpets according to claim 7, is characterized in that: described step 2) requirements of weaving process in, suede is high, and for 4.5mm or 6mm, to weave suede high.