CN103112306A - Coloring and sand dyeing process for polyvinyl alcohol/water glass composite silicone product - Google Patents
Coloring and sand dyeing process for polyvinyl alcohol/water glass composite silicone product Download PDFInfo
- Publication number
- CN103112306A CN103112306A CN2013100510762A CN201310051076A CN103112306A CN 103112306 A CN103112306 A CN 103112306A CN 2013100510762 A CN2013100510762 A CN 2013100510762A CN 201310051076 A CN201310051076 A CN 201310051076A CN 103112306 A CN103112306 A CN 103112306A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl alcohol
- sand
- internal mold
- silica gel
- base substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention aims to solve the defects in the prior art and provides a coloring and sand dyeing process for a polyvinyl alcohol/water glass composite silicone product. The manufacturing method has the advantages of simple and practical process, accessible production materials, low energy consumption and no pollution; and the silicone product can be produced on a large scale in an environment-friendly and low-carbon manner, is similar to a jade in color and shape, is natural and vivid, and has high ornamental value and home decoration value.
Description
One, technical field
The present invention relates to a kind of process technology of silica gel product, more particularly, relate to a kind of colored sand dyeing technique method of polyvinyl alcohol water solution and water glass solution compound silica gel goods.
Two, background technology
At present, silica gel product extensively adopts silicon plastic cement reverse mould technique to make, and it is the indispensable production link of its formed product that reversing mould is made.Reverse mould copies silica gel product, and raw material and mould input cost are high, and type product is stereotyped, and the design of goods form is dull stiff, and is vividly unnatural, not environmental protection of low-carbon (LC) of energy-consuming consumptive material.
The present invention is directed to the deficiencies in the prior art, a kind of colored sand dyeing technique method of polyvinyl alcohol waterglass compound silica gel goods is provided, its process for making is simple and practical, and raw materials for production are easy to get, and low energy consumption is pollution-free, environmental protection low-carbon (LC) large-scale production silica gel product; The lively jadeization of quality natural shape has sight and home decoration.
Three, summary of the invention
Purpose employing of the present invention is achieved through following technical scheme.
The first step, humidifying base material base substrate (internal mold) preparation: complete lightweight moulding base material coarse sand base substrate (internal mold) by design and make, after its workpiece solid by polyvinyl alcohol water solution dip-coating processing humidifying.Second step, prefabricated polyvinyl alcohol aqueous color paste slurry: use mill base or be watered toner and polyvinyl alcohol water solution is transferred standby; In the 3rd step, colored sand is dyed: polyvinyl alcohol aqueous color paste slurry showering or draw paintedly on humidifying base material base substrate (internal mold), and at once carry out nature sand by extra dry white wine stone sand (powder) spreading and dye even look and solidify; In the 4th step, the half congealed compound silica gel of moulding of overflow: successively alternately water glass solution and polyvinyl alcohol water solution are watered (spray) pouring dip-coating by the period and dye on curing substrate base substrate (internal mold) in colored sand, forming physical reaction silica gel is the half congealed composite bed of moulding; In the 5th step, sealing brightening finished product: the solid silica-based waterproof of one-piece machine member or pickling processes, polishing, varnish lacquer painting wait at last.
In a word, the present invention is not limited to apparent size variation in shape, and all close designs of doing according to the content of specification of the present invention and claims or be equal to replacement all belong to scope of patent protection of the present invention
Four, the specific embodiment
The beautiful half congealed color Rock Penjing goods of embodiment 1
The first step, prepare the 550mmx350mmx15mm blanket and contaminate the paper internal mold material through water glass solution by designing requirement, mold materials kneading Cheng Shanshi shape in papery is solidified, the white rubble sand of its 35 order sand is placed on blanket, and solid rear integral body waters by polyvinyl alcohol water solution drenching; Second step, prefabricated green and large red polyvinyl alcohol aqueous color paste slurry: be in harmonious proportion separately preparation with 5 gram water soluble greens and large red mill base and 50 gram polyvinyl alcohol water solutions; In the 3rd step, polyvinyl alcohol water soluble green and red mill base branch are painted on internal mold and blanket, and spreading 85 orders 95 degree white spirit quartz sands carry out sand and dye; The 4th step, alternately watered in every 24 hours through water glass solution and polyvinyl alcohol water solution and drench sand and dye internal mold and blanket 2 times, namely form the half congealed comprehensive silicon glue-line of moulding of overflow; The 5th step, treat that internal mold and blanket surface are solid, silica-based waterproof, varnish lacquer painting.
The beautiful half congealed color fire-retardant decorative slab products of embodiment 2
The first step, preparing the 500mmx500mmx25mm perlite and cement by designing requirement is that 35 order coarse sand face substrates are through 60 seconds humidifyings of polyvinyl alcohol water solution immersion treatment; Second step, prefabricated blue polyvinyl alcohol aqueous color paste slurry: be in harmonious proportion preparation with the 5 blue mill bases of gram water-baseds and 50 gram polyvinyl alcohol water solutions; The 3rd step, the blue mill base spray printing of polyvinyl alcohol water-based green sheets, and spreading 85 orders 95 degree white marble dry sand powder carry out sand and dye; The 4th step, alternately watered the pouring green sheets in every 12 hours 1 time through water glass solution and polyvinyl alcohol water solution, namely form the half congealed comprehensive silicon glue-line of moulding of overflow; The 5th step, until the solid rear watery hydrochloric acid pickling of green sheets, more solid, polishing, bound edge, varnish lacquer painting.
The beautiful half congealed firework alms bowl of embodiment 3 and fish jar goods
The first step, preparing 450mmx350mmx200mm perlite and cement base material cylinder alms bowl by designing requirement is that 35 order coarse sand face base substrates are through 60 seconds humidifyings of polyvinyl alcohol water solution immersion treatment; Second step, prefabricated green and large red polyvinyl alcohol aqueous color paste slurry: be in harmonious proportion separately preparation with 5 gram water soluble greens and bright red mill base and 50 gram polyvinyl alcohol water solutions; The 3rd step, polyvinyl alcohol water soluble green and large red mill base specking cylinder alms bowl base substrate, and the spreading 75 white Tourmaline dry sands of orders 90 degree carry out sand and dye; The 4th step alternately sprayed cylinder alms bowl base substrate 3 times in every 48 hours through water glass solution and polyvinyl alcohol water solution, namely formed the half congealed comprehensive silicon glue-line of moulding of overflow; The 5th step, after cylinder alms bowl body drying again by No. 3 waterproofing agent immersion treatment, more solid, polishing,, varnish lacquer painting, accessories.
Claims (1)
1. the colored sand dyeing technique method of polyvinyl alcohol waterglass compound silica gel goods, is characterized in that comprising the steps:
A. humidifying base material base substrate (internal mold) preparation: complete lightweight moulding base material coarse sand face base substrate (internal mold) by design and make, soak the spray treatment humidifying by polyvinyl alcohol water solution;
B. prefabricated polyvinyl alcohol aqueous color paste slurry: use mill base or be watered toner and polyvinyl alcohol water solution carries out mixing preparation and makes;
C. colored sand is dyed: polyvinyl alcohol aqueous color paste slurry showering or draw paintedly on base material base substrate (internal mold) humidifying layer, and on spreading, extra dry white wine stone sand (powder) carries out nature sand and dyes even look and solidify at once;
D. the half congealed compound silica gel of moulding of overflow: successively alternately water glass solution and polyvinyl alcohol water solution are watered to spray by the period and be coated in colored sand and dye on curing substrate base substrate (internal mold), forming physical reaction silica gel is the half congealed composite bed of moulding;
E. sealing brightening finished product: in good time solid, after silica-based waterproof or pickling processes, dry polishing bound edge, lacquer painting accessories.