CN111018431A - Preparation method of colorful high-brightness concrete handicraft ornament - Google Patents
Preparation method of colorful high-brightness concrete handicraft ornament Download PDFInfo
- Publication number
- CN111018431A CN111018431A CN201911004443.7A CN201911004443A CN111018431A CN 111018431 A CN111018431 A CN 111018431A CN 201911004443 A CN201911004443 A CN 201911004443A CN 111018431 A CN111018431 A CN 111018431A
- Authority
- CN
- China
- Prior art keywords
- concrete
- mould
- brightness
- raw materials
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a preparation method of a colorful high-brightness concrete handicraft ornament, which comprises the following raw materials in parts by weight: thin cement (700 kg/m-1300 kg/m), sand (1000 kg/m-1500 kg/m), pigment (20 kg/m-50 kg/m), brightener (30 kg/m-50 kg/m), water-reducing agent (6 kg/m-10 kg/m), and water (170 kg/m-240 kg/m). The invention has the advantages that the surface of the concrete can be made into the effect similar to a mirror surface, the color of the concrete handicraft decorative article becomes lively and bright, and the concrete handicraft decorative article has the beneficial effect of jade-like texture, and the decorative article is mainly used for manufacturing the concrete handicraft decorative article.
Description
Technical Field
The invention relates to the technical field of concrete manufacturing processes, in particular to a preparation method of a colorful high-brightness concrete handicraft ornament.
Background
At present, along with the development of the concrete industry, more and more building enterprises generate strong interest in modeling concrete and decorative concrete products, along with the continuous improvement of modeling concrete product technology and decorative concrete product technology, various concrete artware is continuously produced, the concrete products also get rid of the inherent template image of brick and tile sand stone, the high-end image is displayed in the front of people, the concrete artware swing parts existing in the market are mostly fair-faced concrete products, the surface is relatively simple, people have very low-adjustment feeling, some colored concrete artware are mostly plain surfaces, or the concrete artware is directly painted with paint during the post-treatment of the artware, and the natural color of the concrete is covered.
Disclosure of Invention
The invention provides a color high-brightness concrete handicraft ornament which can make the surface of concrete into a mirror-like effect through reasonable concrete proportioning and improvement of a mould, so that the color of the ornament becomes lively and bright and has jade-like texture, and aims to solve the problems that most of the concrete handicraft ornaments in the market are fair-faced concrete products, the surface of the ornament is plain, people have a very low-adjustment feeling, and part of the color concrete handicraft products are plain surfaces, or the ornament is directly painted with paint during post-treatment of the handicraft, so that the natural color of the concrete is covered.
The invention is realized in this way, a preparation method of a colorful high-brightness concrete handicraft furnishing piece, the raw material formula of the colorful high-brightness concrete comprises the following components in parts by weight: white cement (700 kg/m)3~ 1300kg/m3) Sand (1000 kg/m)3~1500kg/m3) Pigment (20 kg/m)3~50kg/m3) Brightener (30 kg/m)3~50kg/m3) Water reducing agent (6 kg/m)3~10kg/m3) Water (170 kg/m)3~240kg/m3);
The preparation process of the colored high-brightness concrete comprises the following specific steps:
putting raw materials of white cement, sand, pigment, brightening agent, water reducing agent and water of the colorful high-brightness concrete into a mixing and stirring device according to the proportion of the raw material formula, mixing and stirring the raw materials by the mixing and stirring device, and carrying out the next procedure after uniformly stirring and mixing;
injecting the fully mixed and stirred raw materials into a mould, vibrating the mould to enable the internal structure of the raw materials in the mould to be more compact, and then using the mould to smooth the top surface of the raw materials;
thirdly, covering a film on the mould, curing the raw materials in the mould for 3-5 days, and dismantling the mould after the hardness of the raw materials reaches a standard to obtain a formed concrete product;
and (IV) coating the outer surface of the formed concrete product with a transparent protective agent.
The white cement is white silicate mud water, and the whiteness value in the white silicate mud water is more than 78%.
The sand is quartz sand or transparent glass sand, and the particle size of the sand body is medium-grained sand.
The pigment is selected from iron oxide pigment and color paste.
The brightener is an additive for brightening concrete.
The water reducing agent is a polycarboxylic acid high-performance water reducing agent, and the reduction rate of the water reducing agent in use is more than 25%.
The mould chooses silica gel mould, ABS mould for use, the shape of mould is for formulating according to actual conditions.
The transparent protective agent is selected from a concrete protective agent and a hydrophobic agent.
Compared with the prior art, the invention has the beneficial effects that: the novel raw material formula and the manufacturing process of the concrete process ornament can enable the manufactured concrete process ornament to become lively and bright in color and have jade-like texture, greatly improve the ornamental value of the concrete process ornament, enable the concrete process ornament to be used as a gift for gifting, improve the connotation and value of concrete, and help people change the traditional thinking of rough and rough concrete industry.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention more apparent, the present invention is further described in detail with reference to the following embodiments. It should be understood that the specific embodiments described herein are merely illustrative of the invention and are not intended to limit the invention.
Example 1
The invention provides a technical scheme that: a preparation method of a colorful high-brightness concrete handicraft furnishing part comprises the following raw material formulas in parts by weight: white cement (700 kg/m)3~1300kg/m3) Sand (1000 kg/m)3~1500kg/m3) Pigment (20 kg/m)3~50kg/m3) Brightener (30 kg/m)3~50kg/m3) Water reducing agent (6 kg/m)3~10kg/m3) Water (170 kg/m)3~240kg/m3);
The preparation process of the color high-brightness concrete comprises the following specific steps:
firstly, putting white cement, sand, pigment, brightening agent, water reducing agent and water which are raw materials of the colorful high-brightness concrete into a mixing and stirring device according to the proportion of a raw material formula, mixing and stirring the raw materials by the mixing and stirring device, and carrying out the next procedure after uniformly stirring and mixing;
injecting the fully mixed and stirred raw materials into a mould, vibrating the mould to enable the internal structure of the raw materials in the mould to be more compact, and then using the mould to smooth the top surface of the raw materials;
thirdly, covering a film on the mould, curing the raw materials in the mould for 3-5 days, and dismantling the mould after the hardness of the raw materials reaches the standard to obtain a formed concrete product;
and (IV) coating the outer surface of the formed concrete product with a transparent protective agent.
Example 2
The white cement is white silicate mud water, the whiteness value in the white silicate mud water is more than 78 percent, and the chromaticity of the manufactured concrete can be ensured;
the sand is quartz sand and transparent glass sand, the particle size of the sand body is medium-grained sand, and the medium-grained sand is crumbles with the particle size of 0.5-0.25 mm, so that the sand is convenient to mix, and the manufactured concrete has smooth touch, so that the texture of the concrete ornament is improved;
the pigment is iron oxide pigment and color paste, so that the color degree of the concrete ornament can be increased, and the manufactured concrete ornament has multi-color;
the brightener is an additive for brightening the concrete, and the brightness of the concrete ornament is increased;
the water reducing agent is a polycarboxylic acid high-performance water reducing agent, the reduction rate of the water reducing agent in use is more than 25%, and the dehydration rate of raw materials is ensured;
the mold is a silica gel mold and an ABS mold, so that the cost is low, the mold is convenient to disassemble, the shape of the mold is set according to the actual situation, the mold can be adjusted and customized according to the customer requirements, and the manufactured concrete ornament has individuation;
concrete protective agent, hydrophobe are chooseed for use to transparent protective agent, can protect the concrete goods of furniture for display rather than for use, prevent that it from suffering external environment's influence.
Example 3
The preparation process flow of the invention is that white cement, sand, pigment and brightener are added into a mixing and stirring device in sequence to be stirred for 1 to 3 minutes, then water and water reducing agent are added into the mixing and stirring device to be stirred for 3 to 5 minutes, then the mixture is injected into a mould, the mould is carefully cleaned before use, mould oil is coated on the mould, the mould is vibrated after the mixture is injected into the mould to ensure that the internal structure of the raw material in the mould is more compact, then the top surface of the raw material is smoothed by using the mould, a film is covered after the top surface is smoothed, the raw material in the mould is maintained for 3 to 5 days, the mould is removed after the hardness of the raw material reaches the standard, a formed concrete product can be obtained, and then a transparent protective agent is coated on the surface of the formed concrete product.
Example 4
The invention has the beneficial effects that: the novel raw material formula and the manufacturing process of the concrete process ornament can enable the manufactured concrete process ornament to become lively and bright in color and have jade-like texture, greatly improve the ornamental value of the concrete process ornament, enable the concrete process ornament to be used as a gift for gifting, improve the connotation and value of concrete, and help people change the traditional thinking of rough and rough concrete industry.
Example 5
The raw material formula of the invention comprises the following standard dosage in parts by weight: white cement 1000kg/m31000kg/m of sand330kg/m of pigment3Brightener 40kg/m36kg/m of water reducing agent3240kg/m of water3。
The present invention is not limited to the above preferred embodiments, and any modifications, equivalent substitutions and improvements made within the spirit and principle of the present invention should be included in the protection scope of the present invention.
Claims (8)
1. A preparation method of a colorful high-brightness concrete handicraft furnishing piece is characterized in that: the raw material formula of the color high-brightness concrete comprises the following components in parts by weight: thin cement (700 kg/m-1300 kg/m), sand (1000 kg/m-1500 kg/m), pigment (20 kg/m-50 kg/m), brightener (30 kg/m-50 kg/m), water-reducing agent (6 kg/m-10 kg/m), water (170 kg/m-240 kg/m);
the preparation process of the colored high-brightness concrete comprises the following specific steps:
putting raw materials of the colored high-brightness concrete, namely white cement, sand, pigment, a brightening agent, a water reducing agent and water into mixing and stirring equipment according to the proportion of the raw material formula, mixing and stirring the raw materials by the mixing and stirring equipment, and performing the next procedure after uniformly stirring and mixing the raw materials;
injecting the fully mixed and stirred raw materials into a mould, vibrating the mould to enable the internal structure of the raw materials in the mould to be more compact, and then using a mould to smooth the top surface of the raw materials;
covering a film on the mould, maintaining the raw materials in the mould for 3-5 days, and removing the mould after the hardness of the raw materials reaches a standard to obtain a formed concrete product;
and coating the outer surface of the formed concrete product with a transparent protective agent.
2. The method for preparing a colorful high-brightness concrete handicraft furnishing piece according to claim 1, wherein: the white cement is white silicate mud water, and the whiteness value in the white silicate mud water is more than 78%.
3. The method for preparing a colorful high-brightness concrete handicraft furnishing piece according to claim 1, wherein: the sand is quartz sand or transparent glass sand, and the particle size of the sand body is medium-grained sand.
4. The method for preparing a colorful high-brightness concrete handicraft furnishing piece according to claim 1, wherein: the pigment is selected from iron oxide pigment and color paste.
5. The method for preparing a colorful high-brightness concrete handicraft furnishing piece according to claim 1, wherein: the brightener is an additive for brightening concrete.
6. The method for preparing a colorful high-brightness concrete handicraft furnishing piece according to claim 1, wherein: the water reducing agent is a polycarboxylic acid high-performance water reducing agent, and the reduction rate of the water reducing agent in use is more than 25%.
7. The method for preparing a colorful high-brightness concrete handicraft furnishing piece according to claim 1, wherein: the mould chooses silica gel mould, ABS mould for use, the shape of mould is for formulating according to actual conditions.
8. The method for preparing a colorful high-brightness concrete handicraft furnishing piece according to claim 1, wherein: the transparent protective agent is selected from a concrete protective agent and a hydrophobic agent.