CN103103792A - 一种抗起毛起球聚氨酯整理剂的制备方法 - Google Patents
一种抗起毛起球聚氨酯整理剂的制备方法 Download PDFInfo
- Publication number
- CN103103792A CN103103792A CN2012105400995A CN201210540099A CN103103792A CN 103103792 A CN103103792 A CN 103103792A CN 2012105400995 A CN2012105400995 A CN 2012105400995A CN 201210540099 A CN201210540099 A CN 201210540099A CN 103103792 A CN103103792 A CN 103103792A
- Authority
- CN
- China
- Prior art keywords
- preparation
- pilling
- product
- reactor
- finishing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗起毛起球聚氨酯整理剂的制备方法,包括如下工艺步骤:1)在充满惰性气体的反应釜中加入4,4’-二苯甲烷二异氰酸酯、N,N-二甲基甲酰胺、六亚甲基二异氰酸酯以及二月桂酸二丁基锡,加热溶解;2)取聚醚多元醇,1,4-丁二醇,混溶后,滴加到反应釜中,得到预聚产物;3)在所获得的预聚产物中加入饱和亚硫酸氢钠溶液,得到封端的聚氨酯乳液;4)向反应釜中加入三乙胺中和剂,调节pH=7.5~8;5)减压脱除溶剂N,N-二甲基甲酰胺,加入去离子水配制成固含量为35~38%的水剂,即可得到产品。本发明具有良好的交联性,耐水性,耐黄变性,储存稳定性,安全无毒等优点,经整理后的织物耐搓洗和抗起毛起球性能优异。
Description
技术领域
本发明涉及织物整理剂领域,具体涉及一种抗起毛起球聚氨酯整理剂的制备方法。
背景技术
羊毛、黏胶,纯棉及其混纺织物.特别是针织物在加工、穿着以及洗涤过程中,由于织物或织物与其它物体之间的摩擦作用,其表面会产生许多绒毛,加之静电作用,织物表面会产生起毛起球,从而造成织物外观和手感变差,与皮肤接触舒适度降低,影响了针织物的服用性能。聚氨酯整理不仅能赋予织物柔软性能,还能使织物具有透湿、防水、防缩、抗静电、抗起球、有弹性及光泽好等多种功能。
聚氨酯是主链上带有氨基甲酸酯基团的一类高分子材料的总称,水性聚氨酯是指以水为分散介质的聚氨酯分散体系,主要原料是多异氰酸酯和多羟基化合物反应生成的高分子链上含有氨酯基和尿基结构单元。合成中所使用的原料直接影响着产物的最终性能,具有高强度、耐摩擦,无毒等优异性能,在轻纺、皮革、涂料、粘合剂、印刷等很多方面得到广泛应用。但普通的抗起毛球聚氨酯助剂获得的织物耐搓洗和抗起毛起球性能还不够,容易失效。
发明内容
本发明的目的在于提供一种抗起毛起球聚氨酯整理剂的制备方法,获得抗起毛起球聚氨酯整理剂,具有良好的交联性,耐水性,耐黄变性,储存稳定性,安全无毒等优点,经整理后的织物耐搓洗和抗起毛起球性能优异。
为实现上述目的,本发明提供一种抗起毛起球聚氨酯整理剂的制备方法,包括如下工艺步骤:
1)在充满惰性气体的反应釜中加入4,4’-二苯甲烷二异氰酸酯、N,N-二甲基甲酰胺、六亚甲基二异氰酸酯以及催化剂量的二月桂酸二丁基锡,加热至65℃溶解;所述4,4’-二苯甲烷二异氰酸酯与六亚甲基二异氰酸酯的质量比为0.8~2.6:1;
2)取聚醚多元醇5~150重量份,1,4-丁二醇2重量份,混溶后,滴加到反应釜中,在75~90℃下反应2~6小时,得到预聚产物;
3)在所获得的预聚产物中加入饱和亚硫酸氢钠溶液,在85~98℃下保温反应2~4小时,得到封端的聚氨酯乳液;
4)向反应釜中加入三乙胺中和剂,调节pH=7.5~8;
5)减压脱除溶剂N,N-二甲基甲酰胺,加入去离子水配制成固含量为35~38%的水剂,即可得到产品。
本发明的优点和有益效果在于:提供一种抗起毛起球聚氨酯整理剂的制备方法,获得抗起毛起球聚氨酯整理剂,具有良好的交联性,耐水性,耐黄变性,储存稳定性,安全无毒等优点,经整理后的织物耐搓洗和抗起毛起球性能优异。
具体实施方式
下面结合具体实施例,对本发明作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
实施例1
一种抗起毛起球聚氨酯整理剂的制备方法,包括如下工艺步骤:
1)在充满惰性气体的反应釜中加入4,4’-二苯甲烷二异氰酸酯、N,N-二甲基甲酰胺、六亚甲基二异氰酸酯以及催化剂量的二月桂酸二丁基锡,加热至65℃溶解;所述4,4’-二苯甲烷二异氰酸酯与六亚甲基二异氰酸酯的质量比为1.6:1;
2)取聚醚多元醇80重量份,1,4-丁二醇2重量份,混溶后,滴加到反应釜中,在75~90℃下反应4小时,得到预聚产物;
3)在所获得的预聚产物中加入饱和亚硫酸氢钠溶液,在90℃下保温反应3小时,得到封端的聚氨酯乳液;
4)向反应釜中加入三乙胺中和剂,调节pH=7.8;
5)减压脱除溶剂N,N-二甲基甲酰胺,加入去离子水配制成固含量为37%的水剂,即可得到产品。
实施例2
一种抗起毛起球聚氨酯整理剂的制备方法,包括如下工艺步骤:
1)在充满惰性气体的反应釜中加入4,4’-二苯甲烷二异氰酸酯、N,N-二甲基甲酰胺、六亚甲基二异氰酸酯以及催化剂量的二月桂酸二丁基锡,加热至65℃溶解;所述4,4’-二苯甲烷二异氰酸酯与六亚甲基二异氰酸酯的质量比为0.8:1;
2)取聚醚多元醇5重量份,1,4-丁二醇2重量份,混溶后,滴加到反应釜中,在75℃下反应2小时,得到预聚产物;
3)在所获得的预聚产物中加入饱和亚硫酸氢钠溶液,在85℃下保温反应2小时,得到封端的聚氨酯乳液;
4)向反应釜中加入三乙胺中和剂,调节pH=7.5;
5)减压脱除溶剂N,N-二甲基甲酰胺,加入去离子水配制成固含量为35%的水剂,即可得到产品。
实施例3
一种抗起毛起球聚氨酯整理剂的制备方法,包括如下工艺步骤:
1)在充满惰性气体的反应釜中加入4,4’-二苯甲烷二异氰酸酯、N,N-二甲基甲酰胺、六亚甲基二异氰酸酯以及催化剂量的二月桂酸二丁基锡,加热至65℃溶解;所述4,4’-二苯甲烷二异氰酸酯与六亚甲基二异氰酸酯的质量比为2.6:1;
2)取聚醚多元醇5~150重量份,1,4-丁二醇2重量份,混溶后,滴加到反应釜中,在90℃下反应6小时,得到预聚产物;
3)在所获得的预聚产物中加入饱和亚硫酸氢钠溶液,在98℃下保温反应4小时,得到封端的聚氨酯乳液;
4)向反应釜中加入三乙胺中和剂,调节pH=8;
5)减压脱除溶剂N,N-二甲基甲酰胺,加入去离子水配制成固含量为38%的水剂,即可得到产品。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.一种抗起毛起球聚氨酯整理剂的制备方法,其特征在于,包括如下工艺步骤:
1)在充满惰性气体的反应釜中加入4,4’-二苯甲烷二异氰酸酯、N,N-二甲基甲酰胺、六亚甲基二异氰酸酯以及催化剂量的二月桂酸二丁基锡,加热至65℃溶解;所述4,4’-二苯甲烷二异氰酸酯与六亚甲基二异氰酸酯的质量比为0.8~2.6:1;
2)取聚醚多元醇5~150重量份,1,4-丁二醇2重量份,混溶后,滴加到反应釜中,在75~90℃下反应2~6小时,得到预聚产物;
3)在所获得的预聚产物中加入饱和亚硫酸氢钠溶液,在85~98℃下保温反应2~4小时,得到封端的聚氨酯乳液;
4)向反应釜中加入三乙胺中和剂,调节pH=7.5~8;
5)减压脱除溶剂N,N-二甲基甲酰胺,加入去离子水配制成固含量为35~38%的水剂,即可得到产品。