CN103103546B - 工业酒精反应器锈垢层清洗剂及制备方法 - Google Patents
工业酒精反应器锈垢层清洗剂及制备方法 Download PDFInfo
- Publication number
- CN103103546B CN103103546B CN201310035118.3A CN201310035118A CN103103546B CN 103103546 B CN103103546 B CN 103103546B CN 201310035118 A CN201310035118 A CN 201310035118A CN 103103546 B CN103103546 B CN 103103546B
- Authority
- CN
- China
- Prior art keywords
- reactor
- preparation
- tartrate
- edta
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种操作简单、节省能耗、除垢效果好的工业酒精反应器锈垢层清洗剂及制备方法,所用原料及质量百分比如下:氢氧化钾1~8%,氢氧化钠1~15%,三聚磷酸钠1~6%,乙二胺四乙酸1~3%,酒石酸1~2%,拉开粉0.1~0.6%,脂肪醇聚氧乙烯醚磷酸酯0.1~0.5%及水余量。制备方法按照如下步骤进行:先将计算称量的水加入到反应釜中,启动搅拌器,控制转速为60转/分钟,然后依次将计算称量的氢氧化钾、氢氧化钠、三聚磷酸钠、乙二胺四乙酸、酒石酸、拉开粉、脂肪醇聚氧乙烯醚磷酸酯徐徐加入到反应釜中,每加入一种原料均需搅拌至彻底溶解;当全部原料加入后,再继续搅拌至溶液呈浅透明状。
Description
技术领域
本发明涉及一种清洗剂及制备方法,尤其是一种操作简单、节省能耗、除垢效果好的工业酒精反应器锈垢层清洗剂及制备方法。
背景技术
工业酒精反应器在长时间的生产运行后,其不锈钢内壁就会累积一层2~5mm厚的垢锈层,由于此锈垢层非常坚固地粘覆在内壁上,使用现有的清洗技术(超声波清洗、蒸气清洗、高压清洗、臭氧—紫外线清洗,离子束清洗和等离子体清洗等)均难以将其清除。因此,生产企业只能采取人工除垢,既操作工人钻进反应器中,用铁铲清除锈垢层。人工除垢费时费力,不仅增加了工人的劳动强度,而且每清除一个反应器中的锈垢层就需要10天左右,企业的生产效率因停产(除垢)时间过长而受到影响。
发明内容
本发明是为了解决现有技术所存在的上述技术问题,提供一种操作简单、节省能耗、除垢效果好的工业酒精反应器锈垢层清洗剂及制备方法。
本发明的技术解决方案是:一种工业酒精反应器锈垢层清洗剂,其特征在于所用原料及质量百分比如下:氢氧化钾1~8%,氢氧化钠1~15%,三聚磷酸钠1~6%,乙二胺四乙酸1~3%,酒石酸1~2%,拉开粉0.1~0.6%,脂肪醇聚氧乙烯醚磷酸酯0.1~0.5%及水余量。
一种上述工业酒精反应器锈垢层清洗剂的制备方法,其特征在于按照如下步骤进行:先将计算称量的水加入到反应釜中,启动搅拌器,控制转速为60转/分钟,然后依次将计算称量的氢氧化钾、氢氧化钠、三聚磷酸钠、乙二胺四乙酸、酒石酸、拉开粉、脂肪醇聚氧乙烯醚磷酸酯徐徐加入到反应釜中,每加入一种原料均需搅拌至彻底溶解;当全部原料加入后,再继续搅拌至溶液呈浅透明状。
本发明无需加热,只需常温浸泡24~48小时,即可除去反应器内壁的锈垢层且不会对不锈钢造成腐蚀,具有操作简单、节省能耗、除垢效果好等优点,无需人工除垢,降低了工人的劳动强度,缩短了清洗工期,提高了企业的生产效率。
具体实施方式
实施例1:
所用原料及质量百分比如下:氢氧化钾1%,氢氧化钠15%,三聚磷酸钠1%,乙二胺四乙酸3%,酒石酸1%,拉开粉0.6%,脂肪醇聚氧乙烯醚磷酸酯0.1%及自来水余量。
制备方法按照如下步骤进行:先将计算称量的自来水加入到反应釜中,启动搅拌器,控制转速为60转/分钟,然后依次将计算称量的氢氧化钾、氢氧化钠、三聚磷酸钠、乙二胺四乙酸、酒石酸、拉开粉、脂肪醇聚氧乙烯醚磷酸酯徐徐加入到反应釜中,每加入一种原料均需搅拌至彻底溶解;当全部原料加入后,再继续搅拌30分钟,溶液呈浅透明状。
所用原料均为市售商品。
实施例2:
所用原料及质量百分比如下:氢氧化钾8%,氢氧化钠1%,三聚磷酸钠6%,乙二胺四乙酸1%,酒石酸2%,拉开粉0.1%,脂肪醇聚氧乙烯醚磷酸酯0.5%及自来水余量。
制备方法及原料来源同实施例1。
实施例3:
所用原料及质量百分比如下:氢氧化钾5%,氢氧化钠10%,三聚磷酸钠3%,乙二胺四乙酸2%,酒石酸1.5%,拉开粉0.3%,脂肪醇聚氧乙烯醚磷酸酯0.2%及自来水余量。
制备方法及原料来源同实施例1。
使用时,在第一个反应器内按容积计算称量将本发明实施例1、2或3的清洗剂加入到反应器中,常温浸泡24~48小时,即可彻底清除锈垢。然后再把工作液用泵导入第二个反应器中,并补充新的除垢剂至所需量,常温浸泡24~48小时,即可清除第二个反应器中的锈垢层,并由此类推。操作简单、节省能耗、除垢效果好。
Claims (1)
1.一种工业酒精反应器锈垢层清洗剂的制备方法,所用原料及质量百分比如下:氢氧化钾1~8%,氢氧化钠1~15%,三聚磷酸钠1~6%,乙二胺四乙酸1~3%,酒石酸1~2%,拉开粉0.1~0.6%,脂肪醇聚氧乙烯醚磷酸酯0.1~0.5%及水余量,其特征在于按照如下步骤进行:先将计算称量的水加入到反应釜中,启动搅拌器,控制转速为60转/分钟,然后依次将计算称量的氢氧化钾、氢氧化钠、三聚磷酸钠、乙二胺四乙酸、酒石酸、拉开粉、脂肪醇聚氧乙烯醚磷酸酯加入到反应釜中,每加入一种原料均需搅拌至彻底溶解;当全部原料加入后,再继续搅拌至溶液呈浅透明状。