CN103102536A - 一种用于包裹电容外壳的氯丁橡胶料 - Google Patents

一种用于包裹电容外壳的氯丁橡胶料 Download PDF

Info

Publication number
CN103102536A
CN103102536A CN2012104539074A CN201210453907A CN103102536A CN 103102536 A CN103102536 A CN 103102536A CN 2012104539074 A CN2012104539074 A CN 2012104539074A CN 201210453907 A CN201210453907 A CN 201210453907A CN 103102536 A CN103102536 A CN 103102536A
Authority
CN
China
Prior art keywords
rubber
carbon black
wrapping
chloroprene rubber
antioxidant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012104539074A
Other languages
English (en)
Other versions
CN103102536B (zh
Inventor
杜其信
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongling Xingyi Metal Materials Co., Ltd.
Original Assignee
Tongling Yihengda Electronics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongling Yihengda Electronics Co Ltd filed Critical Tongling Yihengda Electronics Co Ltd
Priority to CN201210453907.4A priority Critical patent/CN103102536B/zh
Publication of CN103102536A publication Critical patent/CN103102536A/zh
Application granted granted Critical
Publication of CN103102536B publication Critical patent/CN103102536B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用于包裹电容外壳的氯丁橡胶料，由下述原料组成：氯丁橡胶（日本电气化学A-90）、顺-1，4-聚异戊二烯橡胶、聚己酸内酯、氧化锌、纳米硅质页岩粉、纳米钾长石、2-硫醇基苯骈咪唑、防老剂MB、聚酰胺蜡微粉、促进剂DM、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷、双(二辛氧基焦磷酸酯基)乙撑钛酸酯、抗氧剂1010、炭黑N339、N660炭黑、二盐基亚磷酸铅、间苯二甲酸酯、顺丁烯二酸二丁酯、苯磺酰肼、二茂铁、改性粉煤灰；合理的原料配方，使得生产出的橡胶料具有良好的综合性能，与金属粘结性强；力学性能、抗疲劳性能、耐老化等性能都较高，为电容提供了高强度的保护作用。

Description

一种用于包裹电容外壳的氯丁橡胶料
技术领域
本发明主要涉及一种橡胶包裹料，尤其涉及一种用于包裹电容外壳的氯丁橡胶料。
背景技术
传统的电容外壳为铝制品或塑料制品，在具有腐蚀性酸碱、高温、低温、高压或臭氧等恶劣的环境下容易损毁，影响电容的正常工作，不仅造成了资源的浪费，在安全方面也得不到有效的保障，而在电容的外壳采用金属网状内骨架，外面包裹橡胶料的技术目前没有出现过。
发明内容
本发明目的就是提供一种用于包裹电容外壳的氯丁橡胶料。
本发明是通过以下技术方案实现的：
一种用于包裹电容外壳的氯丁橡胶料，电容的外壳采用金属网状内骨架，外面包裹橡胶料，所述的橡胶料由下述重量份的原料组成：
氯丁橡胶（日本电气化学A-90）135-145、顺-1，4-聚异戊二烯橡胶5-10、聚己酸内酯5-8、氧化锌2-3、纳米硅质页岩粉30-35、纳米钾长石55-50、2-硫醇基苯骈咪唑1-2、防老剂MB 1-2、聚酰胺蜡微粉5-8、促进剂DM 3-4、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷3-5、双(二辛氧基焦磷酸酯基)乙撑钛酸酯1-2、抗氧剂1010 1-2、炭黑N33915-20、N660炭黑15-25、二盐基亚磷酸铅1-2、间苯二甲酸酯5-10、顺丁烯二酸二丁酯10-15、苯磺酰肼1-2、二茂铁1-2、改性粉煤灰1-3；
所述的改性粉煤灰的制备方法为：粉煤灰用10-15%盐酸浸泡3-4小时，去离子水洗涤，再用10-12%氢氧化钠溶液浸泡3-4小时，再用去离子水洗涤至中性，烘干；将烘干后的粉煤灰放入水中，再加入粉煤灰重量2-3%的月桂醇硫酸钠、1-2%的平平加O、2-3%的柠檬酸三丁酯、3-5%氧化铝，高速1200-1500转/分搅拌，得到分散液，分散液烘干粉碎成超细粉末，即得所述改性粉煤灰。
一种用于包裹电容外壳的氯丁橡胶料的制备方法，包括以下步骤：
（1）按照权利要求1所述的各重量份的原料组份准备原料，将各原料放入密炼机，混炼8-15分钟后，当温度达到85-90℃时，开始排料，排料后停放冷却23-25小时；
（2）将冷却后的胶料加入开炼机，在温度为45-55℃下薄通5-7遍即得所述橡胶料。
其特征在于金属网状内骨架与橡胶料采用粘结或硫化结合而成。
本发明的优点是：
本发明通过合理的搭配原料配方，使得生产出的橡胶料具有良好的综合性能，与金属粘结性强；力学性能、抗疲劳性能、耐热、耐老化等性能都较高，为电容提供了高强度的保护作用，加入改性粉煤灰利用工业固体废弃物，不仅节约了成本，还在橡胶料的生产中起到了补强填充的作用，保证了电容在不同的恶劣条件下正常的工作，增加了电容的使用寿命。
具体实施方式
实施例1
一种用于包裹电容外壳的氯丁橡胶料，电容的外壳采用金属网状内骨架，外面包裹橡胶料，所述的橡胶料由下述重量份的原料组成：
氯丁橡胶（日本电气化学A-90）145、顺-1，4-聚异戊二烯橡胶10、聚己酸内酯8、氧化锌3、纳米硅质页岩粉35、纳米钾长石50、2-硫醇基苯骈咪唑2、防老剂MB2、聚酰胺蜡微粉8、促进剂DM 4、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷5、双(二辛氧基焦磷酸酯基)乙撑钛酸酯1-2、抗氧剂10102、炭黑N339 20、N660炭黑25、二盐基亚磷酸铅2、间苯二甲酸酯10、顺丁烯二酸二丁酯15、苯磺酰肼2、二茂铁2、改性粉煤灰3；
所述的改性粉煤灰的制备方法为：粉煤灰用15%盐酸浸泡4小时，去离子水洗涤，再用12%氢氧化钠溶液浸泡4小时，再用去离子水洗涤至中性，烘干；将烘干后的粉煤灰放入水中，再加入粉煤灰重量2-3%的月桂醇硫酸钠、2%的平平加O、3%的柠檬酸三丁酯、5%氧化铝，高速1500转/分搅拌，得到分散液，分散液烘干粉碎成超细粉末，即得所述改性粉煤灰。
（1）按照权利要求1所述的各重量份的原料组份准备原料，将各原料放入密炼机，在温度为85-90℃下，混炼8-15分钟后开始排料，排料后停放冷却23-25小时；
（2）将冷却后的胶料加入开炼机，在温度为45-55℃下薄通5-7遍即得所述橡胶料。
实施例2
橡胶料由下述重量份的原料组成：
氯丁橡胶（日本电气化学A-90）143、顺-1，4-聚异戊二烯橡胶8、聚己酸内酯7、氧化锌3、纳米硅质页岩粉33、纳米钾长石50、2-硫醇基苯骈咪唑2、防老剂MB2、聚酰胺蜡微粉8、促进剂DM 4、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷5、双(二辛氧基焦磷酸酯基)乙撑钛酸酯2、抗氧剂10102、炭黑N339 20、N660炭黑25、二盐基亚磷酸铅2、间苯二甲酸酯10、顺丁烯二酸二丁酯15、苯磺酰肼2、二茂铁2、改性粉煤灰2；
实施例3
橡胶料由下述重量份的原料组成：
氯丁橡胶（日本电气化学A-90）141、顺-1，4-聚异戊二烯橡胶9、聚己酸内酯5、氧化锌2、纳米硅质页岩粉32、纳米钾长石47、2-硫醇基苯骈咪唑2、防老剂MB2、聚酰胺蜡微粉8、促进剂DM 4、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷5、双(二辛氧基焦磷酸酯基)乙撑钛酸酯2、抗氧剂10102、炭黑N339 20、N660炭黑25、二盐基亚磷酸铅2、间苯二甲酸酯10、顺丁烯二酸二丁酯15、苯磺酰肼2、二茂铁2、改性粉煤灰3；(实施例2和3的工艺方法同实施例1)
性能测试：
传统的橡胶料和本发明的橡胶料的性能对比如下表：
Figure BDA0000239615171
由上表可以看出，本发明生产的橡胶料力学性能、耐油性、耐热性、抗疲劳性等各项性能均优良。

Claims (3)

1.一种用于包裹电容外壳的氯丁橡胶料，其特征在于电容的外壳采用金属网状内骨架，外面包裹橡胶料，所述的橡胶料由下述重量份的原料组成：
氯丁橡胶（日本电气化学A-90）135-145、顺-1，4-聚异戊二烯橡胶5-10、聚己酸内酯5-8、氧化锌2-3、纳米硅质页岩粉30-35、纳米钾长石55-50、2-硫醇基苯骈咪唑1-2、防老剂MB 1-2、聚酰胺蜡微粉5-8、促进剂DM 3-4、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷3-5、双(二辛氧基焦磷酸酯基)乙撑钛酸酯1-2、抗氧剂1010 1-2、炭黑N339 15-20、N660炭黑15-25、二盐基亚磷酸铅1-2、间苯二甲酸酯5-10、顺丁烯二酸二丁酯10-15、苯磺酰肼1-2、二茂铁1-2、改性粉煤灰1-3；
所述的改性粉煤灰的制备方法为：粉煤灰用10-15%盐酸浸泡3-4小时，去离子水洗涤，再用10-12%氢氧化钠溶液浸泡3-4小时，再用去离子水洗涤至中性，烘干；将烘干后的粉煤灰放入水中，再加入粉煤灰重量2-3%的月桂醇硫酸钠、1-2%的平平加O、2-3%的柠檬酸三丁酯、3-5%氧化铝，高速1200-1500转/分搅拌，得到分散液，分散液烘干粉碎成超细粉末，即得所述改性粉煤灰。
2.一种如权利要求1所述的用于包裹电容外壳的氯丁橡胶料的制备方法，其特征在于包括以下步骤：
（1）按照权利要求1所述的各重量份的原料组份准备原料，将各原料放入密炼机，在温度为85-90℃下，混炼8-15分钟后开始排料，排料后停放冷却23-25小时；
（2）将冷却后的胶料加入开炼机，在温度为45-55℃下薄通5-7遍即得所述橡胶料。
3.根据权利要求1所述的一种用于包裹电容外壳的氯丁橡胶料，其特征在于金属网状内骨架与橡胶料采用粘结或硫化结合而成。
CN201210453907.4A 2012-11-13 2012-11-13 一种用于包裹电容外壳的氯丁橡胶料 Expired - Fee Related CN103102536B (zh)