CN103102537B - 一种耐油的电容外壳橡胶包裹料 - Google Patents

一种耐油的电容外壳橡胶包裹料 Download PDF

Info

Publication number
CN103102537B
CN103102537B CN201210453910.6A CN201210453910A CN103102537B CN 103102537 B CN103102537 B CN 103102537B CN 201210453910 A CN201210453910 A CN 201210453910A CN 103102537 B CN103102537 B CN 103102537B
Authority
CN
China
Prior art keywords
rubber
oil
carbon black
rubber mass
coal ash
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210453910.6A
Other languages
English (en)
Other versions
CN103102537A (zh
Inventor
杜其信
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongling Xingyi Metal Materials Co., Ltd.
Original Assignee
TONGLING XINGYI METAL MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING XINGYI METAL MATERIALS CO Ltd filed Critical TONGLING XINGYI METAL MATERIALS CO Ltd
Priority to CN201210453910.6A priority Critical patent/CN103102537B/zh
Publication of CN103102537A publication Critical patent/CN103102537A/zh
Application granted granted Critical
Publication of CN103102537B publication Critical patent/CN103102537B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种耐油的电容外壳橡胶包裹料，由下述原料组成：氯丁橡胶CR121、SG-4型PVC树脂、聚-4-甲基-1-戊烯、N，N‘-间苯撑双马来酰亚胺、氢氧化铝粉、硫酸钡粉、防老剂RD、2-硫醇基苯骈咪唑、硬脂酸锌、促进剂CZ1-2、促进剂DM、3-氨丙基三甲氧基硅烷、铝酸酯偶联剂DL-411、抗氧剂、高耐磨炭黑N330、炭黑N220、双巯基乙酸异辛酯二正辛基锡、环氧硬脂酸辛酯、甘油三醋酸酯、碳酸氢钠、改性粉煤灰、二茂铁；合理的原料配方，使得生产出的橡胶料具有良好的综合性能，与金属粘结性强；力学性能、抗疲劳性能、耐油性、耐老化等性能都较高，为电容提供了高强度的保护作用。

Description

一种耐油的电容外壳橡胶包裹料
技术领域
本发明主要涉及一种橡胶包裹料，尤其涉及一种耐油的电容外壳橡胶包裹料。
背景技术
传统的电容外壳为铝制品或塑料制品，在具有腐蚀性酸碱、高温、低温、高压或臭氧等各种恶劣的环境下容易损毁，影响电容的正常工作，不仅造成了资源的浪费，在安全方面也得不到有效的保障，而在电容的外壳采用金属网状内骨架，外面包裹橡胶料的技术目前没有出现过。
发明内容
本发明目的就是提供一种耐油的电容外壳橡胶包裹料。
本发明是通过以下技术方案实现的：
一种耐油的电容外壳橡胶包裹料，电容的外壳采用金属网状内骨架，外面包裹橡胶料，所述的橡胶料由下述重量份的原料组成：
氯丁橡胶CR121 135-145、SG-3型PVC树脂8-12、聚-4-甲基-1-戊烯5-8、N，N‘-间苯撑双马来酰亚胺1-2、纳米白云石40-45、纳米铝矾土30-40、防老剂OD 1-2、防老剂ODA 1-2、硬脂酸5-8、促进剂Na-22 1-2、促进剂CZ 1-2、氨丙基三乙氧基硅烷2-3、铝酸酯偶联剂DL-411 1-2、抗氧剂1035 1-2、炭黑N339 10-20、N660炭黑15-25、硬脂酸锌3-5、环氧油酸丁酯5-8、一缩二乙二醇苯甲酸酯8-12、碳酸氢钠1-2、二茂铁1-2、改性粉煤灰1-3；
所述的改性粉煤灰的制备方法为：粉煤灰用10-15%盐酸浸泡3-4小时，去离子水洗涤，再用10-12%氢氧化钠溶液浸泡3-4小时，再用去离子水洗涤至中性，烘干；将烘干后的粉煤灰放入水中，再加入粉煤灰重量2-3%的月桂醇硫酸钠、1-2%的平平加O、2-3%的柠檬酸三丁酯、3-5%氢氧化铝，高速1200-1500转/分搅拌，得到分散液，分散液烘干粉碎成超细粉末，即得所述改性粉煤灰。
一种耐油的电容外壳橡胶包裹料的制备方法，包括以下步骤：
（1）按照权利要求1所述的各重量份的原料组份准备原料，将各原料放入密炼机，在温度85-90℃下混炼8-15分钟后，开始排料，排料后停放冷却23-25小时；
（2）将冷却后的胶料加入开炼机，在温度为45-55℃下薄通5-7遍即得所述橡胶料。
其特征在于金属网状内骨架与橡胶料采用粘结或硫化结合而成。
本发明的优点是：
本发明通过合理的搭配原料配方，使得生产出的橡胶料具有良好的综合性能，与金属粘结性强；力学性能、抗疲劳性能、耐油、耐老化等性能都较高，为电容提供了高强度的保护作用，加入改性粉煤灰利用工业固体废弃物，不仅节约了成本，还在橡胶料的生产中起到了补强填充的作用，保证了电容在不同的恶劣条件下正常的工作，增加了电容的使用寿命。
具体实施方式
实施例1
一种耐油的电容外壳橡胶包裹料，电容的外壳采用金属网状内骨架，外面包裹橡胶料，所述的橡胶料由下述重量份的原料组成：
氯丁橡胶CR121 145、SG-3型PVC树脂12、聚-4-甲基-1-戊烯8、N，N‘-间苯撑双马来酰亚胺2、纳米白云石45、纳米铝矾土40、防老剂OD 2、防老剂ODA 2、硬脂酸8、促进剂Na-22 2、促进剂CZ 2、氨丙基三乙氧基硅烷3、铝酸酯偶联剂DL-411 1-2、抗氧剂1035 1-2、炭黑N339 20、N660炭黑25、硬脂酸锌5、环氧油酸丁酯8、一缩二乙二醇苯甲酸酯12、碳酸氢钠2、二茂铁2、改性粉煤灰3；
所述的改性粉煤灰的制备方法为：粉煤灰用15%盐酸浸泡4小时，去离子水洗涤，再用12%氢氧化钠溶液浸泡4小时，再用去离子水洗涤至中性，烘干；将烘干后的粉煤灰放入水中，再加入粉煤灰重量2-3%的月桂醇硫酸钠、2%的平平加O、3%的柠檬酸三丁酯、5%氢氧化铝，高速1500转/分搅拌，得到分散液，分散液烘干粉碎成超细粉末，即得所述改性粉煤灰。
（1）按照上述的各重量份的原料组份准备原料，将各原料放入密炼机，混炼8-15分钟后，当温度达到85-90℃时，开始排料，排料后停放冷却23-25小时；
（2）将冷却后的胶料加入开炼机，在温度为45-55℃下薄通5-7遍即得所述橡胶料。
实施例2
橡胶料由下述重量份的原料组成：
氯丁橡胶CR121 141、SG-3型PVC树脂11、聚-4-甲基-1-戊烯6、N，N‘-间苯撑双马来酰亚胺2、纳米白云石45、纳米铝矾土40、防老剂OD 2、防老剂ODA 2、硬脂酸8、促进剂Na-22 2、促进剂CZ 2、氨丙基三乙氧基硅烷3、铝酸酯偶联剂DL-411 1-2、抗氧剂1035 1-2、炭黑N339 20、N660炭黑25、硬脂酸锌5、环氧油酸丁酯8、一缩二乙二醇苯甲酸酯12、碳酸氢钠2、二茂铁2、改性粉煤灰2；
实施例3
橡胶料由下述重量份的原料组成：
氯丁橡胶CR121 139、SG-3型PVC树脂10、聚-4-甲基-1-戊烯8、N，N‘-间苯撑双马来酰亚胺2、纳米白云石42、纳米铝矾土38、防老剂OD 2、防老剂ODA 2、硬脂酸8、促进剂Na-22 2、促进剂CZ 2、氨丙基三乙氧基硅烷3、铝酸酯偶联剂DL-411 1-2、抗氧剂1035 1-2、炭黑N339 20、N660炭黑25、硬脂酸锌5、环氧油酸丁酯8、一缩二乙二醇苯甲酸酯12、碳酸氢钠2、二茂铁2、改性粉煤灰3；(实施例2和3的工艺方法同实施例1)
性能测试：
传统的橡胶料和本发明的橡胶料的性能对比如下表：
由上表可以看出，本发明生产的橡胶料力学性能、耐热性、抗疲劳性等各项性能均优良的前提上，还具有更强的耐油性。

Claims (1)

1.一种耐油的电容外壳橡胶包裹料，其特征在于电容的外壳采用金属网状内骨架，外面包裹橡胶料，金属网状内骨架与橡胶料采用粘结或硫化结合而成，所述的橡胶料由下述重量份的原料组成：
氯丁橡胶CR121 135-145、SG-3型PVC树脂8-12、聚-4-甲基-1-戊烯5-8、N，N’-间苯撑双马来酰亚胺1-2、纳米白云石40-45、纳米铝矾土30-40、防老剂OD 1-2、防老剂ODA 1-2、硬脂酸5-8、促进剂Na-22 1-2、促进剂CZ 1-2、氨丙基三乙氧基硅烷2-3、铝酸酯偶联剂DL-411 1-2、抗氧剂1035 1-2、炭黑N339 10-20、N660炭黑15-25、硬脂酸锌3-5、环氧油酸丁酯5-8、一缩二乙二醇苯甲酸酯8-12、碳酸氢钠1-2、二茂铁1-2、改性粉煤灰1-3；
所述的改性粉煤灰的制备方法为：粉煤灰用10-15%盐酸浸泡3-4小时，去离子水洗涤，再用10-12%氢氧化钠溶液浸泡3-4小时，再用去离子水洗涤至中性，烘干；将烘干后的粉煤灰放入水中，再加入粉煤灰重量2-3%的月桂醇硫酸钠、1-2%的平平加O、2-3%的柠檬酸三丁酯、3-5%氢氧化铝，高速1200-1500转/分搅拌，得到分散液，分散液烘干粉碎成超细粉末，即得所述改性粉煤灰；
所述的耐油的电容外壳橡胶包裹料的制备方法包括以下步骤：
（1）按照权利要求1所述的各重量份的原料组份准备原料，将各原料放入密炼机，在温度85-90℃下混炼8-15分钟后，开始排料，排料后停放冷却23-25小时；
（2）将冷却后的胶料加入开炼机，在温度为45-55℃下薄通5-7遍即得所述橡胶料。
CN201210453910.6A 2012-11-13 2012-11-13 一种耐油的电容外壳橡胶包裹料 Expired - Fee Related CN103102537B (zh)