CN103101288A - 一种改性水溶性酚醛树脂的蜂窝纸板的制作方法 - Google Patents

一种改性水溶性酚醛树脂的蜂窝纸板的制作方法 Download PDF

Info

Publication number
CN103101288A
CN103101288A CN2012104559928A CN201210455992A CN103101288A CN 103101288 A CN103101288 A CN 103101288A CN 2012104559928 A CN2012104559928 A CN 2012104559928A CN 201210455992 A CN201210455992 A CN 201210455992A CN 103101288 A CN103101288 A CN 103101288A
Authority
CN
China
Prior art keywords
water soluble
honeycomb
modified water
corrugated roll
phenolic resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012104559928A
Other languages
English (en)
Other versions
CN103101288B (zh
Inventor
黄向阳
马应强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEFEI LANGSHENG NEW MATERIAL TECHNOLOGY Co Ltd
Original Assignee
HEFEI LANGSHENG NEW MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEFEI LANGSHENG NEW MATERIAL TECHNOLOGY Co Ltd filed Critical HEFEI LANGSHENG NEW MATERIAL TECHNOLOGY Co Ltd
Priority to CN201210455992.8A priority Critical patent/CN103101288B/zh
Publication of CN103101288A publication Critical patent/CN103101288A/zh
Application granted granted Critical
Publication of CN103101288B publication Critical patent/CN103101288B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种改性水溶性酚醛树脂的蜂窝纸板的制作方法，包括以下步骤：开卷，原材料预处理，烘干，复卷，制作蜂窝纸芯和蜂窝纸板成形；将蜂窝纸板的原材料经过预处理后,再应用到蜂窝纸板的常规生产过程中，本发明的蜂窝纸板性能优良，以瓦楞纸为原纸，易降解，无毒，无害，无污染，具有质轻、防震、隔热、隔音、阻燃、防潮等特点，可广泛应用于建筑业、家具制造业、包装业、运输业。

Description

一种改性水溶性酚醛树脂的蜂窝纸板的制作方法
技术领域
本发明涉及蜂窝纸板的生产工艺，具体涉及一种改性水溶性酚醛树脂的蜂窝纸板的制作方法。
背景技术
蜂窝纸板是一种全纸型材料，在我国已经有十多年的发展，蜂窝纸板有多种优点，因而在包装、运输、建筑等领域蜂窝纸板也在逐步取代传统的瓦楞纸板、木材、泡沫塑料等材料，蜂窝纸板的应用前景极其广阔，蜂窝纸板的强度的提高对蜂窝纸板更广泛的推广具有非常重要的意义，目前，低碳经济的发展已经成为不可抵挡的潮流，发展低碳经济能有效提高资源利用率，保护和改善生态环境，实现可持续发展，通过提高纸芯与面纸的质量来提高蜂窝纸板的强度会耗费大量的木材，因此，通过结构上的改变来达到提高蜂窝纸板强度的目的更有社会价值及经济价值。
目前，一般的蜂窝纸板由三部分组成，即蜂窝纸芯、蜂窝面纸、胶粘剂，蜂窝纸板的抗压强度主要取决于蜂窝纸芯，用于纸芯的芯纸的定量越高，纸板的强度就越高，但纸芯在生产中就越不好拉开；反之纸芯拉开容易，纸板的强度就随之降低，通常蜂窝纸板的芯纸为定量在120g/m2-180g/m2 之间的单种，纸芯用芯纸的定量超过180g/m2 以后在实际生产时纸芯很难拉伸，且蜂窝的窝型不标准，由于蜂窝芯纸的定量较低，蜂窝纸板的抗压强度很难有高的突破，为解决这一问题也有较多的人进行了尝试，例如在蜂窝纸板中添加镶块以提高其强度，但该方法工艺复杂，生产效率低，为在控制成本的基础上增强蜂窝纸板的强度必须在蜂窝纸芯用芯纸的结构或材料上进行革新。
发明内容
本发明的目的在于提供一种改性水溶性酚醛树脂的蜂窝纸板的制作方法，本发明的蜂窝纸板性能优良，以瓦楞纸为原纸，易降解，无毒，无害，无污染，具有质轻、防震、隔热、隔音、阻燃、防潮等特点，可广泛应用于建筑业、家具制造业、包装业、运输业。
为了实现上述目的本发明采用如下技术方案：
改性水溶性酚醛树脂的蜂窝纸板的制作方法，包括以下内容：
（1）    开卷：将瓦楞纸卷展开，铺整后待用；
（2）    瓦楞纸卷的预处理：在常温下，将开卷后的瓦楞纸卷浸入成膜树脂中浸泡处理，浸泡时间为10-12s，所述的成膜树脂的配方为钛酸酯偶联剂TMC-TTS  2-3、磷酸二氢铵0.2-0.3、改性水溶性酚醛树脂1-2、氯化石蜡2-3、苯乙烯3-5、乙酰柠檬酸三乙酯2-3、树木灰1-2、过硫酸钾0.2-0.3、聚乙烯醇0.1-0.3、苯丙乳液0.3-0.5、三苯乙基酚聚氧乙烯醚  2-3、苯二甲酸二丁酯  1-2，制备方法如下：
a：将钛酸酯偶联剂TMC-TTS、磷酸二氢铵、改性水溶性酚醛树脂、氯化石蜡、苯乙烯、乙酰柠檬酸三乙酯、树木灰、聚乙烯醇、苯丙乳液、三苯乙基酚聚氧乙烯醚和苯二甲酸二丁酯加入不锈钢反应釜，升温至100±5℃，开动搅拌加入过硫酸钾；
b：然后以57-65℃/h速率升温到120-130℃，反应1-2小时停止加热，冷却到65±3℃搅匀得到成膜树脂；
（3）    烘干：将经过步骤（2）预处理后的瓦楞纸卷送入烘道中，在168 -185℃的温度条件下，烘干固化；
（4）    复卷：将经过烘干的瓦楞纸卷复卷，待用；
（5）    制作蜂窝纸芯：用胶黏剂对复卷后的瓦楞纸卷进行涂胶复合，然后再经过分切、连接制成蜂窝纸芯；
（6）    蜂窝纸板成形：将蜂窝纸芯展芯、涂胶后，与面板纸复合，制成蜂窝纸板。
所述的改性水溶性酚醛树脂的制备方法为按重量份纳米碳0.2-0.3、水溶性酚醛树脂3-4、羧甲基纤维素1-2和氧化铁3-4，混合加热至70-80℃，30-40分钟后冷却得到。
本发明的有益效果：
本发明的蜂窝纸板性能优良，以瓦楞纸为原纸，易降解，无毒，无害，无污染，具有质轻、防震、隔热、隔音、阻燃、防潮等特点，可广泛应用于建筑业、家具制造业、包装业、运输业。
具体实施方式
实施例：改性水溶性酚醛树脂的蜂窝纸板的制作方法，包括以下内容：
（1）    开卷：将瓦楞纸卷展开，铺整后待用；
（2）    瓦楞纸卷的预处理：在常温下，将开卷后的瓦楞纸卷浸入成膜树脂中浸泡处理，浸泡时间为10-12s，所述的成膜树脂的配方为钛酸酯偶联剂TMC-TTS  2-3、磷酸二氢铵0.2-0.3、改性水溶性酚醛树脂1-2、氯化石蜡2-3、苯乙烯3-5、乙酰柠檬酸三乙酯2-3、树木灰1-2、过硫酸钾0.2-0.3、聚乙烯醇0.1-0.3、苯丙乳液0.3-0.5、三苯乙基酚聚氧乙烯醚  2-3、苯二甲酸二丁酯  1-2，制备方法如下：
a：将钛酸酯偶联剂TMC-TTS、磷酸二氢铵、改性水溶性酚醛树脂、氯化石蜡、苯乙烯、乙酰柠檬酸三乙酯、树木灰、聚乙烯醇、苯丙乳液、三苯乙基酚聚氧乙烯醚和苯二甲酸二丁酯加入不锈钢反应釜，升温至100±5℃，开动搅拌加入过硫酸钾；
b：然后以57-65℃/h速率升温到120-130℃，反应1-2小时停止加热，冷却到65±3℃搅匀得到成膜树脂；
（3）    烘干：将经过步骤（2）预处理后的瓦楞纸卷送入烘道中，在168 -185℃的温度条件下，烘干固化；
（4）    复卷：将经过烘干的瓦楞纸卷复卷，待用；
（5）    制作蜂窝纸芯：用胶黏剂对复卷后的瓦楞纸卷进行涂胶复合，然后再经过分切、连接制成蜂窝纸芯；
（6）    蜂窝纸板成形：将蜂窝纸芯展芯、涂胶后，与面板纸复合，制成蜂窝纸板。
所述的改性水溶性酚醛树脂的制备方法为按重量份纳米碳0.2-0.3、水溶性酚醛树脂3-4、羧甲基纤维素1-2和氧化铁3-4，混合加热至70-80℃，30-40分钟后冷却得到。
    上述制得的蜂窝纸板的性能数据：
本发明的蜂窝芯纸的含水率：8.5-11%，蜂窝芯纸环压强度：5.85 N·m/g，纸板厚度：13.2mm，每平方重量g/m2：830-900，抗压挠度：初始高17.3mm，加压后高度16.9mm。

Claims (2)

1.一种改性水溶性酚醛树脂的蜂窝纸板的制作方法，其特征在于包括以下内容：
（1）开卷：将瓦楞纸卷展开，铺整后待用；
（2）瓦楞纸卷的预处理：在常温下，将开卷后的瓦楞纸卷浸入成膜树脂中浸泡处理，浸泡时间为10-12s，所述的成膜树脂的配方为钛酸酯偶联剂TMC-TTS  2-3、磷酸二氢铵0.2-0.3、改性水溶性酚醛树脂1-2、氯化石蜡2-3、苯乙烯3-5、乙酰柠檬酸三乙酯2-3、树木灰1-2、过硫酸钾0.2-0.3、聚乙烯醇0.1-0.3、苯丙乳液0.3-0.5、三苯乙基酚聚氧乙烯醚  2-3、苯二甲酸二丁酯  1-2，制备方法如下：
a：将钛酸酯偶联剂TMC-TTS、磷酸二氢铵、改性水溶性酚醛树脂、氯化石蜡、苯乙烯、乙酰柠檬酸三乙酯、树木灰、聚乙烯醇、苯丙乳液、三苯乙基酚聚氧乙烯醚和苯二甲酸二丁酯加入不锈钢反应釜，升温至100±5℃，开动搅拌加入过硫酸钾；
b：然后以57-65℃/h速率升温到120-130℃，反应1-2小时停止加热，冷却到65±3℃搅匀得到成膜树脂；
（3）烘干：将经过步骤（2）预处理后的瓦楞纸卷送入烘道中，在168 -185℃的温度条件下，烘干固化；
（4）复卷：将经过烘干的瓦楞纸卷复卷，待用；
（5）制作蜂窝纸芯：用胶黏剂对复卷后的瓦楞纸卷进行涂胶复合，然后再经过分切、连接制成蜂窝纸芯；
（6）蜂窝纸板成形：将蜂窝纸芯展芯、涂胶后，与面板纸复合，制成蜂窝纸板。
2.根据权利要求书1所述的改性水溶性酚醛树脂的蜂窝纸板的制作方法，其特征在于：所述的改性水溶性酚醛树脂的制备方法为按重量份纳米碳0.2-0.3、水溶性酚醛树脂3-4、羧甲基纤维素1-2和氧化铁3-4，混合加热至70-80℃，30-40分钟后冷却得到。
CN201210455992.8A 2012-11-14 2012-11-14 一种改性水溶性酚醛树脂的蜂窝纸板的制作方法 Active CN103101288B (zh)