CN103073947A - 一种附着力高的工业喷码墨水 - Google Patents
一种附着力高的工业喷码墨水 Download PDFInfo
- Publication number
- CN103073947A CN103073947A CN2012105653734A CN201210565373A CN103073947A CN 103073947 A CN103073947 A CN 103073947A CN 2012105653734 A CN2012105653734 A CN 2012105653734A CN 201210565373 A CN201210565373 A CN 201210565373A CN 103073947 A CN103073947 A CN 103073947A
- Authority
- CN
- China
- Prior art keywords
- spraying ink
- industrial code
- code spraying
- sticking power
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种附着力高的工业喷码墨水，由下列重量比组成：染料3-13；溶剂80-90；树脂10-20；该喷码墨水具有不变质，不沉淀，在紫外光照射下不易褪色的特点；该喷码墨水拥有极强的化学稳定性，从而保证了墨水的有效期在18个月；适用于食品袋喷码，安全无毒、无臭符合食品包装卫生标准；该喷码墨水拥有高度兼容性，可以广泛适用于多少种打印介质；该喷码墨水具有不会伤害打印头，渗透能力强，保证打印完毕用水冲不掉，会得到广泛使用，并不断替代现有材料。
Description
技术领域
本发明涉及食品包装用工业喷码墨水，尤其涉及一种附着力高的工业喷码墨水。
背景技术
随着社会城市化、科技化、人性化的发展，食品包装业得到了蓬勃的发展，越来越多的食品为了保质保鲜会在包装上喷上使用日期等，随之而来的是喷码机使用量的增加和喷码墨水不防水、在紫外线照射下很快分解、光泽度低和附着力低等问题的彰显，喷码机是用来在产品表面喷印字符（如生产日期，保质期，批号等）图标、规格、条码及防伪标识等内容的机器，其优点在于不接触产品，喷印内容灵活可变，字符大小可以调节，以及可以和计算机连接进行复杂数据库喷印。
而随着人性化理念的普及，及新型和谐社会的构成，食品塑料包装袋一般使用的是opp材料或pe材料附着困难，不断提高工业喷码墨水的附着力，设计一种附着力高的工业喷码墨水是非常必要的。
现有的工业喷码墨水，主要采用在三辊研磨机制得，中国专利CN 1073698A公开了一种塑料包装用防伪油墨，但是考虑到上述方法工艺复杂，成本高昂，相容性差，墨水透明性降低，附着力低和节能环保等角度，现有技术就显得略有不足。
发明内容
本发明提供一种附着力高的工业喷码墨水，解决现有工业喷码墨水中的透明度低，工艺复杂，成本高昂，相容性差，易分解和附着力低等技术问题。
本发明采用以下技术方案：
附着力高的工业喷码墨水，由下列原料组成，以重量份数表示法为：
染料 3-13；
溶剂 80-90；
树脂 10-20；
作为本发明的一种优选技术方案：所述染料为金属络合染料，溶解性优，与各种树脂有良好的相容性 ，不含游离重金属，无污染。
作为本发明的一种优选技术方案：所述溶剂为丁酮或醋酸乙酯中的一种或多种混合物，所述丁酮的相对密度为1.131 g/cm3，折光率为1.5584，所述醋酸乙酯的相对密度为0.9006（20℃），沸点：77.1℃。
作为本发明的一种优选技术方案：所述树脂采用氯化聚丙烯的改性树脂。
作为本发明的一种优选技术方案：所述氯化聚丙烯的改性树脂是通过丙烯酸酯单体对氯化聚丙烯树脂的改性得到一种氯化聚丙烯的改性树脂。
作为本发明的一种优选技术方案：所述丙烯酸酯单体为甲基丙烯酸甲酯、甲基丙烯酸乙酯或甲基丙烯酸丁酯中的一种或多种混合物，所述甲基丙烯酸甲酯的熔点为-48℃，沸点为100~101℃，相对密度为0.9440 g/cm3，折光率为1.4142；所述甲基丙烯酸乙酯的密度为0.912g/cm3，熔点为-75℃，沸点为118～119℃；所述甲基丙烯酸丁酯的沸点为160~163℃，相对密度为0.894 g/cm3，折光率为1.4229，闪点为50℃。
本发明使用的所有原料均为共知的已有。
本发明所述一种附着力高的工业喷码墨水采用以上技术方案与现有技术相比，具有以下技术效果：1、该喷码墨水具有不变质，不沉淀，在紫外光照射下不易褪色的特点；2、该喷码墨水拥有极强的化学稳定性，从而保证了墨水的有效期在18个月；3、适用于食品袋喷码，安全无毒、无臭符合食品包装卫生标准；4、该喷码墨水拥有高度兼容性，可以广泛适用于多少种打印介质；5、该喷码墨水具有不会伤害打印头，渗透能力强，保证打印完毕用水冲不掉，会得到广泛使用，并不断替代现有材料。
具体实施方式
以下通过实施例更加详细地阐述本发明的内容。
实施例1:
第一步：按照下文所述重量分数比称取各种原料
金属络合染料 8 南通丽鑫化工设备有限公司
丁酮 85 日照力德士化工有限公司
改性氯化聚丙烯 15 东莞市成泰化工有限公司
第二步：将上述原料放入混合，使各种成分分散均匀。
第三步：将第二步混合后的原料经过1um，0.5um，0.2um的三级严格过滤。
第四步：分装成500ml、1000ml包装，25瓶一箱。
实施例2:
第一步：按照下文所述重量分数比称取各种原料
金属络合染料 8 南通丽鑫化工设备有限公司
醋酸乙酯 85 上海吕氏化工有限公司
改性氯化聚丙烯 15 东莞市成泰化工有限公司
第二步：将上述原料放入混合，使各种成分分散均匀。
第三步：将第二步混合后的原料经过1um，0.5um，0.2um的三级严格过滤。
第四步：分装成500ml、1000ml包装，25瓶一箱。
实施例3:
第一步：按照下文所述重量分数比称取各种原料
金属络合染料 13 南通丽鑫化工设备有限公司
丁酮 90 日照力德士化工有限公司
改性氯化聚丙烯 20 东莞市成泰化工有限公司
第二步：将上述原料放入混合，使各种成分分散均匀。
第三步：将第二步混合后的原料经过1um，0.5um，0.2um的三级严格过滤。
第四步：分装成500ml、1000ml包装，25瓶一箱。
实施例4:
第一步：按照下文所述重量分数比称取各种原料
金属络合染料 13 南通丽鑫化工设备有限公司
醋酸乙酯 90 上海吕氏化工有限公司
改性氯化聚丙烯 20 东莞市成泰化工有限公司
第二步：将上述原料放入混合，使各种成分分散均匀。
第三步：将第二步混合后的原料经过1um，0.5um，0.2um的三级严格过滤。
第四步：分装成500ml、1000ml包装，25瓶一箱。
以上实施例和对比例中的组合物所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述，而不是限制，因此在与本发明的权利要求书相当的含义和范围内的任何改变，都应该认为是包括在权利要求书的范围内。
Claims (6)
1.一种附着力高的工业喷码墨水，其特征在于：其组成成份以重量份数表示法为：
染料 3-13；
溶剂 80-90；
树脂 10-20。
2.根据权利要求1所述的一种附着力高的工业喷码墨水，其特征在于：所述染料为金属络合染料，溶解性优，与各种树脂有良好的相容性，不含游离重金属，无污染。
3.根据权利要求1所述的一种附着力高的工业喷码墨水，其特征在于：所述溶剂为丁酮或醋酸乙酯中的一种或多种混合物，所述丁酮的相对密度为1.131 g/cm3，折光率为1.5584，所述醋酸乙酯的相对密度为0.9006 g/cm3（20℃），沸点：77.1℃。
4.根据权利要求1所述的一种附着力高的工业喷码墨水，其特征在于：所述树脂采用氯化聚丙烯的改性树脂。
5.根据权利要求4所述的一种附着力高的工业喷码墨水，其特征在于：所述氯化聚丙烯的改性树脂是通过丙烯酸酯单体对氯化聚丙烯树脂的改性得到一种氯化聚丙烯的改性树脂。
6.根据权利要求5所述的一种附着力高的工业喷码墨水，其特征在于：所述丙烯酸酯单体为甲基丙烯酸甲酯、甲基丙烯酸乙酯或甲基丙烯酸丁酯中的一种或多种混合物，所述甲基丙烯酸甲酯的熔点为-48℃，沸点为100~101℃，相对密度为0.9440 g/cm3，折光率为1.4142；所述甲基丙烯酸乙酯的密度为0.912g/cm3，熔点为-75℃，沸点为118～119℃；所述甲基丙烯酸丁酯的沸点为160~163℃，相对密度为0.894 g/cm3，折光率为1.4229，闪点为50℃。