CN103059458A - 一种含有改性纳米级二氧化钛的pvc管材及其制备方法 - Google Patents

一种含有改性纳米级二氧化钛的pvc管材及其制备方法 Download PDF

Info

Publication number
CN103059458A
CN103059458A CN2012105345521A CN201210534552A CN103059458A CN 103059458 A CN103059458 A CN 103059458A CN 2012105345521 A CN2012105345521 A CN 2012105345521A CN 201210534552 A CN201210534552 A CN 201210534552A CN 103059458 A CN103059458 A CN 103059458A
Authority
CN
China
Prior art keywords
titanium dioxide
parts
modified nano
grade titanium
nano grade
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012105345521A
Other languages
English (en)
Other versions
CN103059458B (zh
Inventor
强健娜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Taixie Intelligent Technology Co ltd
Original Assignee
An Huihai Na Chuan Su Ye Science And Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by An Huihai Na Chuan Su Ye Science And Technology Ltd filed Critical An Huihai Na Chuan Su Ye Science And Technology Ltd
Priority to CN201210534552.1A priority Critical patent/CN103059458B/zh
Publication of CN103059458A publication Critical patent/CN103059458A/zh
Application granted granted Critical
Publication of CN103059458B publication Critical patent/CN103059458B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种含有改性纳米级二氧化钛的pvc管材及其制备方法，其组成原料的重量份为：SG-7型PVC树脂48-52、ASA树脂37-39、聚-4-甲基-1-戊烯0.9-1.1、乙烯-醋酸乙烯酯共聚物1-3、硬酯酸单甘油酯1.5-2.5、复合铅盐稳定剂3-5、改性纳米级二氧化钛2-4、抗氧剂DLTP 0.7-0.9、柠檬酸三丁酯1-2和异丙基二硬脂酰氧基铝酸酯1.1-1.3；本发明通过对配方进一步优化，在配方中添加了改性纳米级二氧化钛成分，使得在pvc管材的加工过程中能促进无机填料的分散，提高pvc熔体的流动性，还能提升拉伸强度与断裂伸长率，韧性好，硬度低的缺点；而且制备方法简单，可以有效的应用于各行各业中。

Description

一种含有改性纳米级二氧化钛的pvc管材及其制备方法
技术领域
本发明涉及pvc管材生产领域，尤其涉及一种含有改性纳米级二氧化钛的pvc管材及其制备方法。
背景技术
pvc管材的主要成份为聚氯乙烯，另外加入增塑剂、抗老化剂等辅料来增加其耐热性、韧性、延展性等，pvc是当今世界上深受喜爱、颇为流行并且也被广泛应用的一种合成材料，PVC管材是一种成熟的管材，主要应用于给排水工程，pvc管材具有耐酸、耐碱、耐腐蚀性、强度高等优点，但是，目前大步分生产厂家生产出来的pvc管材抗冲击性能并不好，尤其在PVC制品的加工中的塑化过程，无机物的分散和pvc熔体的加工流动性一直是个难题。
发明内容
    本发明的目的是针对现有技术的不足，提供一种含有改性纳米级二氧化钛的pvc管材及其制备方法。
为实现上述目的，本发明采用如下技术方案：
含有改性纳米级二氧化钛的pvc管材，其组成原料的重量份为：SG-7型PVC树脂48-52、ASA树脂37-39、聚-4-甲基-1-戊烯 0.9-1.1、乙烯-醋酸乙烯酯共聚物1-3、硬酯酸单甘油酯1.5-2.5、复合铅盐稳定剂3-5、改性纳米级二氧化钛2-4、抗氧剂DLTP  0.7-0.9、柠檬酸三丁酯1-2和异丙基二硬脂酰氧基铝酸酯1.1-1.3。
含有改性纳米级二氧化钛的pvc管材，其组成原料的重量份为：SG-7型PVC树脂50、ASA树脂38、聚-4-甲基-1-戊烯 1、乙烯-醋酸乙烯酯共聚物2、硬酯酸单甘油酯2、复合铅盐稳定剂4、改性纳米级二氧化钛3、抗氧剂DLTP  0.8、柠檬酸三丁酯1.5和异丙基二硬脂酰氧基铝酸酯1.2。
含有改性纳米级二氧化钛的pvc管材的制备方法，包括以下步骤：
（1）按组成原料的重量份称取各原料，在热混锅内加入SG-7型PVC树脂和ASA树脂，加热2-3分钟，然后依次加入聚-4-甲基-1-戊烯、乙烯-醋酸乙烯酯共聚物、硬酯酸单甘油酯、复合铅盐稳定剂、改性纳米级二氧化钛、抗氧剂DLTP  、柠檬酸三丁酯和异丙基二硬脂酰氧基铝酸酯，混料5-7分钟；
（2）然后加入到平行双螺杆挤出机中进行熔融共混并造粒即得混合粒子，挤出机机筒温度为168-178℃，模头温度为180-185℃，螺杆转速为530-580rpm；
（3）采用锥形双螺杆挤出机将所得的混合粒子挤出成型，即得含有改性纳米级二氧化钛的pvc管材，挤出机机筒温度为193-208℃，模头温度为208-215℃。
所述的含有改性纳米级二氧化钛的pvc管材，其特征在于：所述的改性纳米级二氧化钛的制备方法为：在纳米级二氧化钛中加入1-2%纳米碳、10-20%氢氧化铝、1-2%的三聚磷酸钠、3-4%的铁矿尾渣，改性，混合，烘干，粉碎成粉末。
本发明的优点：
本发明通过对配方进一步优化，在配方中添加了改性纳米级二氧化钛成分，使得在pvc管材的加工过程中能促进无机填料的分散，提高pvc熔体的流动性，还能提升拉伸强度与断裂伸长率，韧性好，硬度低的缺点；而且制备方法简单，可以有效的应用于各行各业中。
具体实施方式
下面结合实施例对本发明做进一步详细说明。
实施例1：含有改性纳米级二氧化钛的pvc管材，其组成原料的重量份（公斤）为：SG-7型PVC树脂50、ASA树脂38、聚-4-甲基-1-戊烯 1、乙烯-醋酸乙烯酯共聚物2、硬酯酸单甘油酯2、复合铅盐稳定剂4、改性纳米级二氧化钛3、抗氧剂DLTP  0.8、柠檬酸三丁酯1.5和异丙基二硬脂酰氧基铝酸酯1.2。
含有改性纳米级二氧化钛的pvc管材的制备方法，包括以下步骤：
（1）按组成原料的重量份称取各原料，在热混锅内加入SG-7型PVC树脂和ASA树脂，加热2-3分钟，然后依次加入聚-4-甲基-1-戊烯、乙烯-醋酸乙烯酯共聚物、硬酯酸单甘油酯、复合铅盐稳定剂、改性纳米级二氧化钛、抗氧剂DLTP  、柠檬酸三丁酯和异丙基二硬脂酰氧基铝酸酯，混料5-7分钟；
（2）然后加入到平行双螺杆挤出机中进行熔融共混并造粒即得混合粒子，挤出机机筒温度为168-178℃，模头温度为180-185℃，螺杆转速为530-580rpm；
（3）采用锥形双螺杆挤出机将所得的混合粒子挤出成型，即得含有改性纳米级二氧化钛的pvc管材，挤出机机筒温度为193-208℃，模头温度为208-215℃。
改性纳米级二氧化钛的制备方法为：在纳米级二氧化钛中加入相当于其重量2%纳米碳、20%氢氧化铝、1%的三聚磷酸钠、3%的铁矿尾渣，改性，混合，烘干，粉碎成粉末。
上述实施例制得的pvc管材的对比验证测试结果如下表：
序号 检测项目及单位 QB/T2480指标 普通pvc管材 本实施中的试样
1 外观 内外壁应光滑平整，无凹陷及分解变色线等表面缺陷 内外壁光滑平整，无凹陷及分解变色线等表面缺陷 内外壁光滑平整，无凹陷及分解变色线等表面缺陷
2 拉伸强度，Mpa ≥43 43 58
3 断裂伸长率，% ≥80 105 116
4 纵向回缩率，% ≤3.5 3.1 1.9
5 维卡软化温度，℃ ≥75 83 98
6 落锤冲击试验（20℃,2kg，2m），TIR ≤10% 5.5 1.55

Claims (4)

1.一种含有改性纳米级二氧化钛的pvc管材，其特征在于其组成原料的重量份为：SG-7型PVC树脂48-52、ASA树脂37-39、聚-4-甲基-1-戊烯 0.9-1.1、乙烯-醋酸乙烯酯共聚物1-3、硬酯酸单甘油酯1.5-2.5、复合铅盐稳定剂3-5、改性纳米级二氧化钛2-4、抗氧剂DLTP  0.7-0.9、柠檬酸三丁酯1-2和异丙基二硬脂酰氧基铝酸酯1.1-1.3。
2.根据权利要求1所述的含有改性纳米级二氧化钛的pvc管材，其特征在于其组成原料的重量份为：SG-7型PVC树脂50、ASA树脂38、聚-4-甲基-1-戊烯 1、乙烯-醋酸乙烯酯共聚物2、硬酯酸单甘油酯2、复合铅盐稳定剂4、改性纳米级二氧化钛3、抗氧剂DLTP  0.8、柠檬酸三丁酯1.5和异丙基二硬脂酰氧基铝酸酯1.2。
3.一种如权利要求1所述的含有改性纳米级二氧化钛的pvc管材的制备方法，其特征在于包括以下步骤：
（1）按组成原料的重量份称取各原料，在热混锅内加入SG-7型PVC树脂和ASA树脂，加热2-3分钟，然后依次加入聚-4-甲基-1-戊烯、乙烯-醋酸乙烯酯共聚物、硬酯酸单甘油酯、复合铅盐稳定剂、改性纳米级二氧化钛、抗氧剂DLTP  、柠檬酸三丁酯和异丙基二硬脂酰氧基铝酸酯，混料5-7分钟；
（2）然后加入到平行双螺杆挤出机中进行熔融共混并造粒即得混合粒子，挤出机机筒温度为168-178℃，模头温度为180-185℃，螺杆转速为530-580rpm；
（3）采用锥形双螺杆挤出机将所得的混合粒子挤出成型，即得含有改性纳米级二氧化钛的pvc管材，挤出机机筒温度为193-208℃，模头温度为208-215℃。
4.根据权利要求1所述的含有改性纳米级二氧化钛的pvc管材，其特征在于：所述的改性纳米级二氧化钛的制备方法为：在纳米级二氧化钛中加入1-2%纳米碳、10-20%氢氧化铝、1-2%的三聚磷酸钠、3-4%的铁矿尾渣，改性，混合，烘干，粉碎成粉末。
CN201210534552.1A 2012-12-12 2012-12-12 一种含有改性纳米级二氧化钛的pvc管材及其制备方法 Expired - Fee Related CN103059458B (zh)