CN103045070B - The formation method of LED water-based lampshade paint and preparation method thereof and paint film - Google Patents
The formation method of LED water-based lampshade paint and preparation method thereof and paint film Download PDFInfo
- Publication number
- CN103045070B CN103045070B CN201210494659.8A CN201210494659A CN103045070B CN 103045070 B CN103045070 B CN 103045070B CN 201210494659 A CN201210494659 A CN 201210494659A CN 103045070 B CN103045070 B CN 103045070B
- Authority
- CN
- China
- Prior art keywords
- paint
- lampshade
- component
- led water
- led
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a kind of LED water-based lampshade paint, it comprises two components, and wherein, described component A comprises aqueous acrylic modified PU resin, scattering of light powder, aqueous polyurethane thickener, water-based defoamer, aqueous wetting agent, toner.Described B component comprises dehydrated alcohol and coupling agent.First each for component A mixing of materials is ground through skin grinder, then be 10: 1 mixing in mass ratio with B component, leave standstill 15 ~ 25 minutes, with 200 order filter-cloth filterings, obtain LED water-based lampshade paint.LED water-based lampshade paint is poured in socket LED lamp cover down by pressure, allows LED water-based lampshade paint naturally trickle in LED lamp cover to without paint liquid and trickles, thus in LED lamp cover, form one deck paint film.LED water-based lampshade paint of the present invention environmental protection, product nonirritant, without poison gas, transmittance is high, rate of drying is fast, sticking power is good, whiteness is high.
Description
[technical field]
The present invention relates to formula and the making method of the paint film on a kind of LED water-based lampshade.
[background technology]
The head light in past is all luminescent lamp substantially, seriously polluted in its production process, and waste rare earth resources.In recent years, China puts into effect policy, and end is eliminated traditional luminescent lamp, and replacing is the LED of environmental protection and energy saving.But the use of LED needs supporting corresponding lens or plastic lousing just can reach the light source effect of luminescent lamp, so the enterprise of illuminating industry carries out technology shifts one after another, seek supporting lampshade technology, although the existing associated lamp overcoat layer of the first two years is brought into use, but it is solvent based product not environmentally, not only contaminate environment, and have a strong impact on the healthy of operative employee.
[summary of the invention]
The technical problem that the present invention need solve be to provide a kind of environmental protection, product nonirritant, without poison gas, transmittance is high, rate of drying is fast, sticking power is good, whiteness is high LED water-based lampshade paint.
According to the above-mentioned technical problem that need solve, devise a kind of formula of LED water-based lampshade paint, it comprises component A and B component, and the mass ratio of component A and B component is 10: 1; Wherein, described component A comprises the component of following weight percent:
Described B component comprises the component of following weight percent:
Dehydrated alcohol 80%
Coupling agent 20%.
The present invention also provides the making method of LED water-based lampshade paint, comprising: Step1: by each mixing of materials in component A, be then ground to fineness≤20 micron through skin grinder, viscosity controller is at 8000 ~ 50000mPas/25 DEG C;
Step2: be 10: 1 mixing in mass ratio by component A and B component, leave standstill 15 ~ 25 minutes, with 200 order filter-cloth filterings, obtain LED water-based lampshade paint.
The present invention also provides and LED water-based lampshade paint is coated to formation method LED lamp cover being formed paint film, comprise: Step1: above-mentioned LED water-based lampshade paint is poured in socket LED lamp cover down by pressure, allow LED water-based lampshade paint naturally trickle in LED lamp cover to without paint liquid trickle, thus form one deck paint film on LED water-based lampshade;
Step2: and then it is mute that LED water-based lampshade is baked to coating surface change at 40 ~ 60 DEG C.
Compared with prior art, LED water-based lampshade paint of the present invention environmental protection, product nonirritant, without poison gas, transmittance is high, rate of drying is fast, sticking power is good, whiteness is high.
[embodiment]
Below in conjunction with embodiment, the invention will be further described.
LED water-based lampshade paint of the present invention, for being coated in LED lamp cover, lampshade forms coast of paint film coating, thus the light that LED water-based lamp is sent reaches the light source effect of luminescent lamp.
Two components drawn together by LED water-based lampshade enamel-cover of the present invention, are component A and B component, and the mass ratio of component A and B component is 10: 1.Wherein, described component A comprises the aqueous acrylic modified PU resin that weight percent (wt%) is 40% ~ 62%, weight percent is the scattering of light powder of 35.4% ~ 55%, weight percent is the aqueous polyurethane thickener of 1.5% ~ 3%, weight percent is the water-based defoamer of 0.5% ~ 1%, weight percent is the aqueous wetting agent of 0.5% ~ 1%, and weight percent is the toner of 0.10 ~ 0.20%.Described B component comprises the dehydrated alcohol of weight percent 80% ~ 90%, the coupling agent of weight percent 10% ~ 20%.
Preferred embodiment of the present invention, wherein, component A comprises the aqueous acrylic modified PU resin that weight percent (wt%) is 62%, weight percent is the scattering of light powder of 35.4%, weight percent is the aqueous polyurethane thickener of 1.5%, weight percent is the water-based defoamer of 0.5%, and weight percent is the aqueous wetting agent of 0.5%, and weight percent is 0.10% toner.
Make the present embodiment LED water-based lampshade paint time, first prepare, by the above each mixing of materials in component A, to be then ground to fineness≤20 micron through skin grinder, viscosity controller at 8000 ~ 50000mPas/25 DEG C, with for subsequent use.
Described B component comprises the dehydrated alcohol of weight percent 80%, the coupling agent of weight percent 20%.Be 10: 1 mixing in mass ratio by good component A for subsequent use and B component, leave standstill 15 ~ 25 minutes, with 200 order filter-cloth filterings, obtain LED water-based lampshade paint.
For forming paint film on LED water-based lampshade, LED water-based lampshade paint is poured in socket LED water-based lampshade down by pressure, allow LED water-based lampshade paint naturally trickle on LED water-based lampshade to without paint liquid trickle, thus form one deck paint film on LED water-based lampshade; And then it is mute that LED water-based lampshade is baked to coating surface change at 40 ~ 60 DEG C, thus obtain LED water-based lampshade finished product, the paint film layer of coating on it, the light that LED water-based lamp is sent reaches the light source effect of luminescent lamp.
LED water-based lampshade paint of the present invention environmental protection, product nonirritant, without poison gas, transmittance is high, rate of drying is fast, sticking power is good, whiteness is high.
Above-described is only embodiments of the present invention, it should be pointed out that for the person of ordinary skill of the art at this, without departing from the concept of the premise of the invention, can also make improvement, but these all belongs to protection scope of the present invention.
Claims (3)
1. a LED water-based lampshade paint, is characterized in that, the formula of described LED water-based lampshade paint comprises component A and B component, and the mass ratio of component A and B component is 10: 1,
Described component A comprises the component of following weight percent:
Described B component comprises the component of following weight percent:
Dehydrated alcohol 80%
Coupling agent 20%.
2. a making method for LED water-based lampshade paint as claimed in claim 1, is characterized in that, comprising:
Step1: by each mixing of materials in component A, be then ground to fineness≤20 micron through skin grinder, viscosity controller is at 8000 ~ 50000mPas/25 DEG C;
Step2: be 10: 1 mixing in mass ratio by component A and B component, leave standstill 15 ~ 25 minutes, with 200 order filter-cloth filterings, obtain LED water-based lampshade paint.
3. the formation method of paint film on LED water-based lampshade, is characterized in that, comprising:
Step1: LED water-based lampshade paint is as claimed in claim 1 poured in socket LED lamp cover down by pressure, allow LED water-based lampshade paint in LED lamp cover naturally trickling to without the trickling of paint liquid, thus form one deck paint film on LED water-based lampshade;
Step2: and then it is mute that LED water-based lampshade is baked to coating surface change at 40 ~ 60 DEG C.