CN103045070A - LED (Light Emitting Diode) water-based lamp shade paint, manufacturing method thereof and paint film forming method - Google Patents
LED (Light Emitting Diode) water-based lamp shade paint, manufacturing method thereof and paint film forming method Download PDFInfo
- Publication number
- CN103045070A CN103045070A CN2012104946598A CN201210494659A CN103045070A CN 103045070 A CN103045070 A CN 103045070A CN 2012104946598 A CN2012104946598 A CN 2012104946598A CN 201210494659 A CN201210494659 A CN 201210494659A CN 103045070 A CN103045070 A CN 103045070A
- Authority
- CN
- China
- Prior art keywords
- led
- water
- lampshade
- component
- lamp shade
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides an LED (Light Emitting Diode) water-based lamp shade paint which comprises two components, wherein the component A comprises water-based acroleic acid modified PU (Poly Urethane) resin, light-scattering powder, a water-based polyurethane thickening agent, a water-based defoaming agent, a water-based wetting agent and a coloring adjunct; the component B comprises absolute ethyl alcohol and a coupling agent. The manufacturing method of the LED water-based lamp shade paint comprises the following steps of: firstly mixing materials in the component A and grinding by a grinding machine; then mixing with the component B according to the mass ratio of 10:1, and standing for 15-25 minutes; and filtering by using a filter cloth with 200 meshes to obtain the LED water-based lamp shade paint. The LED water-based lamp shade paint is flushed into an LED lamp shade with a downward lamp socket under pressure and naturally flows on the LED lamp shade till no paint flows, and therefore a layer of paint film is formed on the LED lamp shade. The LED water-based lamp shade paint provided by the invention has the advantages of environment protection, no irritation or poison gas, high light transmittance, high drying speed, good adhesive force and high whiteness.
Description
[technical field]
The present invention relates to prescription and the making method of the paint film on a kind of LED water-based lampshade.
[background technology]
The head light in past all is luminescent lamp basically, and is seriously polluted in its production process, and the waste rare earth resources.In recent years, China has put into effect policy, and traditional luminescent lamp will be eliminated in the end, and replacing is the LED lamp of environmental protection and energy saving.But the use of LED lamp needs supporting corresponding lens or plastic lousing just can reach the light source effect of luminescent lamp, so the enterprise of illuminating industry carries out technology shifts one after another, seek supporting lampshade technology, although the existing associated lamp overcoat layer of the first two years is brought into use, but it is the solvent-borne type product of not environmental protection, contaminate environment not only, and have a strong impact on the healthy of operative employee.
[summary of the invention]
The technical problem that the present invention need solve provides a kind of environmental protection, product nonirritant, without poison gas, transmittance is high, rate of drying is fast, sticking power good, whiteness is high LED water-based lampshade lacquer.
According to the above-mentioned technical problem that needs solution, designed a kind of prescription of LED water-based lampshade lacquer, it comprises A component and B component, the mass ratio of A component and B component is 10: 1; Wherein, described A component comprises (wt%):
Described B component comprises (wt%): dehydrated alcohol 80%～90%
Coupling agent 10%～20%.
The present invention also provides the making method of LED water-based lampshade lacquer, comprising: Step1: with each mixing of materials in the A component, then be ground to fineness≤20 micron through skin grinder, viscosity controller is at 8000～50000mpas/25 ℃;
Step2: be to mix at 10: 1 in mass ratio with A component and B component, left standstill 15～25 minutes, with 200 order filter-cloth filterings, namely get LED water-based lampshade and coat with lacquer.
The present invention also provides LED water-based lampshade lacquer is coated to the formation method that forms paint film on the LED lampshade, comprise: Step1: above-mentioned LED water-based lampshade lacquer is poured it in socket LED lampshade down by pressure, allow LED water-based lampshade lacquer on the LED lampshade, naturally trickle to the trickling of nothing lacquer liquid, thereby at LED water-based lampshade formation one deck paint film;
Step2: and then it is mute that LED water-based lampshade is baked to the coating surface change at 40～60 ℃.
Compared with prior art, LED water-based lampshade of the present invention lacquer environmental protection, product nonirritant, without poison gas, transmittance is high, rate of drying is fast, sticking power good, whiteness is high.
[embodiment]
The invention will be further described below in conjunction with embodiment.
LED water-based lampshade lacquer of the present invention is used for being coated in the LED lampshade, form the coast of paint film coating at lampshade, thereby the light that LED water-based lamp is sent reaches the light source effect of luminescent lamp.
LED water-based lampshade enamel-cover of the present invention is drawn together two components, is A component and B component, and the mass ratio of A component and B component is 10: 1.Wherein, described A component comprises that weight percent (wt%) is 40%～62% aqueous acrylic modified PU resin, weight percent is 35.4%～55% scattering of light powder, weight percent is 1.5%～3% aqueous polyurethane thickener, weight percent is 0.5%～1% water-based defoamer, weight percent is 0.5%～1% aqueous wetting agent, and weight percent is 0.10～0.20% toner.Described B component comprises the dehydrated alcohol of weight percent 80%～90%, the coupling agent of weight percent 10%～20%.
Preferred embodiment of the present invention, wherein, the A component comprises that weight percent (wt%) is 62% aqueous acrylic modified PU resin, weight percent is 35.4% scattering of light powder, weight percent is 1.5% aqueous polyurethane thickener, weight percent is 0.5% water-based defoamer, and weight percent is 0.5% aqueous wetting agent, and weight percent is 0.10% toner.
When making present embodiment LED water-based lampshade lacquer, prepare first above each mixing of materials in the A component, then be ground to fineness≤20 micron through skin grinder, viscosity controller is at 8000～50000mpas/25 ℃, with for subsequent use.
Described B component comprises the dehydrated alcohol of weight percent 80%, the coupling agent of weight percent 20%.Be to mix at 10: 1 in mass ratio with good A component for subsequent use and B component, left standstill 15～25 minutes, with 200 order filter-cloth filterings, namely get LED water-based lampshade and coat with lacquer.
For forming paint film at LED water-based lampshade, LED water-based lampshade lacquer pours it in socket LED water-based lampshade down by pressure, allow LED water-based lampshade lacquer on LED water-based lampshade, naturally trickle to the trickling of nothing lacquer liquid, thereby at LED water-based lampshade formation one deck paint film; And then it is mute that LED water-based lampshade is baked to the coating surface change at 40～60 ℃, thereby obtain LED water-based lampshade finished product, the paint film layer that applies on it, and the light that LED water-based lamp is sent reaches the light source effect of luminescent lamp.
The environmental protection of LED water-based lampshade of the present invention lacquer, product nonirritant, without poison gas, transmittance is high, rate of drying is fast, sticking power good, whiteness is high.
Above-described only is embodiments of the present invention, should be pointed out that for the person of ordinary skill of the art at this, under the prerequisite that does not break away from the invention design, can also make improvement, but these all belongs to protection scope of the present invention.
Claims (4)
1. a LED water-based lampshade lacquer is characterized in that, the prescription of described LED water-based lampshade lacquer comprises A component and B component, and the mass ratio of A component and B component is 10: 1,
Described A component comprises (wt%):
Described B component comprises (wt%): dehydrated alcohol 80%～90%
Coupling agent 10%～20%.
2. LED water-based lampshade according to claim 1 coats with lacquer, and it is characterized in that: described A component comprises (wt%):
Described B component comprises (wt%): dehydrated alcohol 80%
Coupling agent 20%.
3. the making method of LED water-based lampshade lacquer as claimed in claim 1 is characterized in that, comprising:
Step1: with each mixing of materials in the A component, then be ground to fineness≤20 micron through skin grinder, viscosity controller is at 8000～50000mpas/25 ℃;
Step2: be to mix at 10: 1 in mass ratio with A component and B component, left standstill 15～25 minutes, with 200 order filter-cloth filterings, namely get LED water-based lampshade and coat with lacquer.
4. the formation method of paint film on the LED water-based lampshade is characterized in that, comprising:
Step1: LED water-based lampshade lacquer pours it in socket LED lampshade down by pressure as claimed in claim 1, allows LED water-based lampshade coat with lacquer and on the LED lampshade, naturally trickles extremely trickle without lacquer liquid, thereby at LED water-based lampshade formation one deck paint film;
Step2: and then it is mute that LED water-based lampshade is baked to the coating surface change at 40～60 ℃.