CN102745966A - Anti-cracking color retention VOC-free (Volatile Organic Compounds) and zero-alkali-return aqueous dry powder building colored coating - Google Patents
Anti-cracking color retention VOC-free (Volatile Organic Compounds) and zero-alkali-return aqueous dry powder building colored coating Download PDFInfo
- Publication number
- CN102745966A CN102745966A CN2012102663058A CN201210266305A CN102745966A CN 102745966 A CN102745966 A CN 102745966A CN 2012102663058 A CN2012102663058 A CN 2012102663058A CN 201210266305 A CN201210266305 A CN 201210266305A CN 102745966 A CN102745966 A CN 102745966A
- Authority
- CN
- China
- Prior art keywords
- dry powder
- building
- alkali
- sepiolite
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an anti-cracking color retention VOC-free (Volatile Organic Compounds) zero-alkali-return aqueous dry powder building colored coating which comprises the following substances in percentage by weight: 20-40% of low-alkali cementing agent, 50-60% of colored sand, 4-9% of sepiolite powder, 0.01-0.015% of plasticizing agent, 0.05% of high-strength adhesive, 3-9% of redispersible latex powder, 0.01% of water repellent, 0-0.1% of antalkaline, 0.01-0.02% of powdered dispersing agent, 0-0.02% of powdered defoaming agent and 0.8-2% of inorganic pigment. The anti-cracking color retention VOC-free zero-alkali-return aqueous dry powder building colored coating is compounded by utilizing the compatibility principle of various powder raw materials and a scientific formula. The anti-cracking color retention VOC-free zero-alkali-return aqueous dry powder building colored coating has the advantages of strong base wall adhesive force, strong weather resistance, zero alkali return and bright color, no cracks or light pollution is generated, and the service life of the coating is as long as that of a building. The anti-cracking color retention VOC-free zero-alkali-return aqueous dry powder building colored coating is mainly applied to the decorative finish of civil building alternative brick surfaces and the latex coating decorative finish and belongs to a novel environment-friendly and energy-saving material.
Description
Technical field
The present invention relates to a kind of construction industry and use dry powder paint, specifically be that a kind of anticracking is protected look zero VOC zero accumulation of salt in the surface soil water-based dry powder building colo(u)r coating, belong to building material field.
Background technology
Along with Building Trade in China is flourish, various outer (interior) wall facing materials emerge in an endless stream, and early stage brick facial ornament face occupies nearly 90% the market share; In using, existed many deficiencies afterwards, as: come off, high some place is prone to pound when coming off hurts sb.'s feelings; Be prone to be full of cracks; Construction, maintenance cost height, it is extremely difficult especially to change facing, and the city appearance is persevered for several decades as if it were one day.Countries and regions government had taked relative measures according to the practical situation of each department afterwards, and the emulsion coatings that released one after another (stemming from Japan) is though overcome some above-mentioned deficiency; But many problems also occurred in using, paint film is thin, and anti-cracking is not enough; Be prone to stain, especially elastic coating more is prone to stain, and elasticity and anti-pollution characteristic are difficult to balance; Fugitive color, weathering resistance is relatively poor, also has a certain amount of light pollution; Be difficult to satisfy high-grade facing requirement, in construction and the use VOC gas arranged, influence human health.Given this because of, my research staff of company produces a kind of novel inorganic anticracking and protects look zero VOC zero accumulation of salt in the surface soil water-based dry powder building colo(u)r coating through research and development in a lot of years, satisfies the demand of following Green environmental-protection building.
Summary of the invention
To the deficiency that above-mentioned prior art exists, the purpose of this invention is to provide the water-based dry powder building colo(u)r coating of a kind of anticracking, guarantor's look, zero VOC, zero accumulation of salt in the surface soil.
Be above-mentioned technical problem, the technical scheme that the present invention adopts is:
Anticracking is protected look zero VOC zero accumulation of salt in the surface soil water-based dry powder building colo(u)r coating, is made up of the material of following weight percent:
Low alkali agglutinate 20-40%; Color sand 50-60%; Sepiolite powder 4-9%; Fluidizer 0.01-0.015%; High-strength structureal adhesives 0.05%, redispersable latex powder 3-9%; Hydrophober 0.01%; Antalkaline 0-0.1%; Powdery dispersion agent 0.01-0.02%; Powdery skimmer 0-0.02%; Mineral dye 0.8-2%.
In above-mentioned prescription, low alkali agglutinate is the agglutinate of Ph value between 9-10, and the alkalescence of agglutinate can not be too strong, the tetanic excessively accumulation of salt in the surface soil degree that affects coating that connects of alkalescence.
In above-mentioned prescription, low alkali agglutinate is preferably low alkali aluminosulfate cement.
In above-mentioned prescription, said color sand be natural colored stone ore deposit through ore dressing, pulverize and the mesh sieve that differs in size after the sand of the different meshes that obtains, wherein the different meshes sand is respectively 20 orders, 40 orders, 60 orders.
In above-mentioned prescription, sepiolite powder is that natural one-level sepiolite or secondary sepiolite worn into 300 orders or 200 purpose meals respectively, and wherein each component is by weight in the one-level sepiolite: sepiolite 70%, quartz 10%, talcum 15%, calcite 5%; Each component is sepiolite 27.38%, quartz 18.62%, talcum 9%, calcite 38%, rhombspar 7% by weight in the secondary sepiolite.
In above-mentioned prescription, said high-strength structureal adhesives are preferably etherificate polyvinylpyrrolidine copper tackiness agent.The use of high-strength structureal adhesives can make that coating anti-shrinks, do not chap, not hollowing, non-scale.
In above-mentioned prescription, said redispersable latex powder is preferably propenoate and the styrene copolymerized propenoate redispersable latex powder that forms.It is the film forming base-material of dry powder paint, and its consumption is directly connected to the performance of dry powder paint, and its consumption is crossed the low intensity and the adhesive property that can influence coating, and too high meeting influence degree of drying and increase cost.
The adding of powdery dispersion agent is in order to disperse those to be difficult to be dissolved in the solid particulate of liquid, also to prevent the sedimentation and the cohesion of solid particulate simultaneously, forming stable suspension-s.Dispersion agent uses in dry powder trade sales coating system, and along with the increase of consumption, the slurry viscosity can descend, so must its consumption of control.
The adding of powdery skimmer mainly is to produce bubble in the construction process in order to prevent.
The adding of mineral dye is in order to increase the ornamental of coating, and consumption is 0.8-2%, can require to add color dye according to different decorations.
At the construction field (site), this inorganic powder building colo(u)r coating is added water, the back spraying that stirs gets final product, wherein coating: water=1: 0.15-0.25.
The present invention has the following advantages than prior art:
1, production technique of the present invention is simple; Raw material is prone to purchase; Cheap; Accumulating is convenient, easy (its flow process: characteristics such as the solid moulding mould → batch mixing of basic unit's levelling → horizontal resiliency lattice → subsides (material: water 1: 0.15-0.25) → manual smear or mechanically spraying → remove mould → manual roller coating and mechanically spraying → inferior optical transparency waterproofing protection film) of quick construction;
2, compare with brick facial ornament face that cost is low, lightweight, alleviate built-loading thing, color variation, Artline, no light pollution, environmental protection, easy construction, design random big, be prone to renovation;
3, compare with the emulsion facing, do not have any volatilization pungent, zero VOC, stain resistance is strong; Deposit non-volatilely, accumulating is convenient, color texture nature, and vision is soft; Stereoscopic sensation is strong, and snappiness is strong, anti-shrinks, do not chap, not hollowing, non-scale, less demanding to Base Smoothness, can economize putty layer; Can eliminate trickle unfairness place of elevation of building, production cost is low, environmental protection, reusable edible.
Embodiment
The following specific embodiment of existing combination is further described the present invention.
Embodiment 1: each component concentration of water-based dry powder building colo(u)r coating of present embodiment is: the Ph value is 9 low alkali aluminosulfate cement 40%; The color sand 25% of color sand 25%, 40 purpose of 20 purposes; 300 purpose one-level sepiolite powders 6%; Fluidizer 0.01%; Etherificate polyvinylpyrrolidine copper high-strength structureal adhesives 0.05%; Propenoate redispersable latex powder 5%; Hydrophober 0.01%; Antalkaline 0.1%; Powdery dispersion agent 0.02%; Powdery skimmer 0.01%; Mineral dye 0.8%.During construction, all components of above-mentioned coating is dropped into stirrer for mixing by weight percentage add water after evenly, restir evenly back spraying gets final product, wherein coating: water=1: 0.15-0.25.The dry powder building colo(u)r coating of present embodiment can be used for the decoration of skin.
Embodiment 2: each component concentration of water-based dry powder building colo(u)r coating of present embodiment is: the Ph value is 9 low alkali aluminosulfate cement 22%; The color sand 20% of color sand 15%, 60 order of color sand 25%, 40 order of 20 orders; 200 order secondary sepiolite powders 9%; Fluidizer 0.01%; Etherificate polyvinylpyrrolidine copper high-strength structureal adhesives 0.05%; Propenoate redispersable latex powder 8%; Hydrophober 0.01%; Antalkaline 0.05%; Powdery dispersion agent 0.01%; Powdery skimmer 0.02%; Mineral dye 0.85%.During construction, all components of above-mentioned coating is dropped into stirrer for mixing by weight percentage add water after evenly, restir evenly back spraying gets final product, wherein coating: water=1:0.15-0.25.The dry powder building colo(u)r coating of present embodiment can be used for the decoration of inner wall of building.
Embodiment 3: each component concentration of water-based dry powder building colo(u)r coating of present embodiment is: the Ph value is 10 the color sand 15% of color sand 20%, 60 purpose of color sand 25%, 40 purpose of low alkali agglutinate 30%20 purposes; 300 purpose one-level sepiolite powders 6%; Fluidizer 0.01%; Dry type compound polyurethane high-strength structureal adhesives 0.05%; The redispersable latex powder 3% that vinyl acetate and the copolymerization of higher fatty acid vinyl acetate form; Hydrophober 0.01%; Antalkaline 0.1%; Powdery dispersion agent 0.02%; Powdery skimmer 0.01%; Mineral dye 0.8%.During construction, all components of above-mentioned coating is dropped into stirrer for mixing by weight percentage add water after evenly, restir evenly back spraying gets final product, wherein coating: water=1: 0.15-0.25.The dry powder building colo(u)r coating of present embodiment can be used for the decoration of skin.
Embodiment 4: each component concentration of water-based dry powder building colo(u)r coating of present embodiment is that the Ph value is 10 low alkali agglutinates 25%; The color sand 25% of color sand 35%, 60 order of 40 orders; 200 order secondary sepiolite powders 5%; Fluidizer 0.01%; Dry type compound polyurethane high-strength structureal adhesives 0.05%; The redispersable latex powder 9% that vinyl acetate and ethylene copolymer form; Hydrophober 0.01%; Antalkaline 0.05%; Powdery dispersion agent 0.01%; Powdery skimmer 0.02%; Mineral dye 0.85%.During construction, all components of above-mentioned coating is dropped into stirrer for mixing by weight percentage add water after evenly, restir evenly back spraying gets final product, wherein coating: water=1: 0.15-0.25.The dry powder building colo(u)r coating of present embodiment can be used for the decoration of inner wall of building.
Claims (7)
1. anticracking is protected look zero VOC zero accumulation of salt in the surface soil water-based dry powder building colo(u)r coating, and it is characterized in that: it is made up of the material of following weight percent:
Low alkali agglutinate 20-40%; Color sand 50-60%; Sepiolite powder 4-9%; Fluidizer 0.01-0.015%; High-strength structureal adhesives 0.05%, redispersable latex powder 2-10%; Hydrophober 0.01%; Antalkaline 0-0.1%; Powdery dispersion agent 0.01-0.02%; Powdery skimmer 0-0.02%: mineral dye 0.8-2%.
2. water-based dry powder building colo(u)r coating according to claim 1, it is characterized in that: low alkali agglutinate is the agglutinate of Ph value between 9-10.
3. water-based dry powder building colo(u)r coating according to claim 1 and 2, it is characterized in that: low alkali agglutinate is preferably low alkali aluminosulfate cement.
4. water-based dry powder building colo(u)r coating according to claim 1; It is characterized in that: said color sand be natural colored stone ore deposit through ore dressing, pulverize and the mesh sieve that differs in size after the sand of the different meshes that obtains, wherein the particle size of different meshes sand is respectively 20 orders, 40 orders, 60 orders.
5. water-based dry powder building colo(u)r coating according to claim 1; It is characterized in that: sepiolite powder is that natural one-level sepiolite or secondary sepiolite worn into 300 orders or 200 purpose meals respectively, and wherein each component is by weight in the one-level sepiolite: sepiolite 70%, quartz 10%, talcum 15%, calcite 5%; Each component is sepiolite 27.38%, quartz 18.62%, talcum 9%, calcite 38%, rhombspar 7% by weight in the secondary sepiolite.
6. water-based dry powder building colo(u)r coating according to claim 1, it is characterized in that: said high-strength structureal adhesives are preferably etherificate polyvinylpyrrolidine copper tackiness agent.
7. water-based dry powder building colo(u)r coating according to claim 1, it is characterized in that: said redispersable latex powder is preferably propenoate and the styrene copolymerized propenoate redispersable latex powder that forms.