CN103044893B - 一种高透光率的聚碳酸酯 - Google Patents

一种高透光率的聚碳酸酯 Download PDF

Info

Publication number
CN103044893B
CN103044893B CN201310034705.0A CN201310034705A CN103044893B CN 103044893 B CN103044893 B CN 103044893B CN 201310034705 A CN201310034705 A CN 201310034705A CN 103044893 B CN103044893 B CN 103044893B
Authority
CN
China
Prior art keywords
polycarbonate
parts
light transmittance
kilogram
transmission rate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310034705.0A
Other languages
English (en)
Other versions
CN103044893A (zh
Inventor
陈维君
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHEJIANG SRTPO NEW MATERIAL TECHNOLOGY Co Ltd
Original Assignee
ZHEJIANG SRTPO NEW MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG SRTPO NEW MATERIAL TECHNOLOGY Co Ltd filed Critical ZHEJIANG SRTPO NEW MATERIAL TECHNOLOGY Co Ltd
Priority to CN201310034705.0A priority Critical patent/CN103044893B/zh
Publication of CN103044893A publication Critical patent/CN103044893A/zh
Application granted granted Critical
Publication of CN103044893B publication Critical patent/CN103044893B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种高透光率的聚碳酸酯，以重量份计，所述高透光率的聚碳酸酯包含下列成分：(a)80-95份的聚碳酸酯；(b)0.5-2.0份的光扩散剂；(c)1-3份的阻燃剂；(d)1-5份的润滑剂；(e)0.1-1份的光稳定剂；以及(f)1-3份的增韧剂。本发明所述的高透光率的聚碳酸酯具有高透光性的优点，能满足户外照明用的要求，工艺简单成熟，有利于普遍推广应用。

Description

一种高透光率的聚碳酸酯
技术领域
本发明涉及高分子领域，具体的说，本发明涉及一种高透光率的聚碳酸酯。
背景技术
聚碳酸酯材料由于其强度高、透明性、耐高温性及阻燃性，通常被选用为照明灯具外罩材料。未经改性的聚碳酸酯用作灯具外罩时，会裸露刺眼的眩光，需要进行专门的反眩光改性以保持光线的柔和来较少对人眼的刺激，然而在用作LED照明灯具外罩时，聚碳酸酯外罩经过传统的防眩光改性后会导致透光率下降，存在发光效率低下的问题。
发明内容
本发明的目的是提供一种高透光率的聚碳酸酯。
为了实现本发明的目的，本发明提供一种高透光率的聚碳酸酯，以重量份计，所述高透光率的聚碳酸酯包含下列成分：(a)80-95份的聚碳酸酯；(b)0.5-2.0份的光扩散剂；(c)1-3份的阻燃剂；(d)1-5份的润滑剂；(e)0.1-1份的光稳定剂；以及(f)1-3份的增韧剂。
优选地，以重量份计，所述高透光率的聚碳酸酯包含下列成分：(a)90份的聚碳酸酯；(b)1.0份的光扩散剂；(c)2.0份的阻燃剂；(d)1.0份的润滑剂；(e)0.5份的光稳定剂；以及(f)1.5份的增韧剂。
更优选地，所述光扩散剂为三(2，4-二叔丁基苯基)亚磷酸酯、十八烷基-3，5-双((1，1-二甲基乙基)-4-羟基苯丙酸酯、双水杨酸双酚A酯和丙烯酸丁酯中的一种或多种。
更优选地，所述阻燃剂为多聚芳基磷酸酯、氢氧化镁、氢氧化钡和全氟丁基磺酸钾中的一种或多种。
更优选地，所述润滑剂为季戊四醇硬脂酸酯、乙撑双硬脂酰胺、硬脂酸盐和二甲基硅烷中的一种或多种。
更优选地，所述光稳定剂为2-羟基-4-正辛氧基二苯甲酮。
更优选地，所述增韧剂为乙烯-醋酸乙烯酯共聚物(EVA)。
本发明所述的高透光率的聚碳酸酯具有高透光性的优点，能满足户外照明用的要求，工艺简单成熟，有利于普遍推广应用。
具体实施方式
以下通过具体实施方式的描述对本发明作进一步说明，但这并非是对本发明的限制，本领域技术人员根据本发明的基本思想，可以做出各种修改或改进，但是只要不脱离本发明的基本思想，均在本发明的范围之内。
聚碳酸酯(PC)，德国拜耳公司；三(2，4-二叔丁基苯基)亚磷酸酯，淄博齐翔石油化工集团有限公司；十八烷基-3，5-双((1，1-二甲基乙基)-4-羟基苯丙酸酯(CAS号：2082-79-3)，上海江莱生物科技有限公司；多聚芳基磷酸酯，浙江万盛股份有限公司；2-羟基-4-正辛氧基二苯甲酮，武汉远城科技发展有限公司。
实施例1
称取90千克的聚碳酸酯、1.0千克的光扩散剂、2.0千克的多聚芳基磷酸酯、1.0千克的二甲基硅烷、0.5千克的2-羟基-4-正辛氧基二苯甲酮和1.5千克的EVA，其中所述光扩散剂为0.5千克的三(2，4-二叔丁基苯基)亚磷酸酯、0.2千克的十八烷基-3，5-双((1，1-二甲基乙基)-4-羟基苯丙酸酯、0.1千克的双水杨酸双酚A酯和0.2千克的丙烯酸丁酯。
将聚碳酸酯、光扩散剂、多聚芳基磷酸酯、二甲基硅烷、2-羟基-4-正辛氧基二苯甲酮和EVA在高搅锅中高速(950r/min)搅拌5min，初步混合后，从加料口处加入双螺杆挤出机中，双螺杆挤出机中从进料段到机头的各反应段温度分别为250℃、260℃、270℃、265℃、265℃、250℃、245℃、240℃，模头温度为260℃，双螺杆挤出机中螺杆长径比为38∶1，转速350r/min。经双螺杆挤出机挤出后经过水冷、切粒，在鼓风干燥箱中120℃放置4小时后，得到高透光率的聚碳酸酯复合物。
实施例2
按照和实施例1相同的方式制备高透光率的聚碳酸酯复合物，不同之处在于所述光扩散剂为0.5千克的三(2，4-二叔丁基苯基)亚磷酸酯、0.2千克的十八烷基-3，5-双((1，1-二甲基乙基)-4-羟基苯丙酸酯、0.3千克的丙烯酸丁酯。
实施例3
按照和实施例1相同的方式制备高透光率的聚碳酸酯复合物，不同之处在于所述光扩散剂为0.5千克的三(2，4-二叔丁基苯基)亚磷酸酯、0.2千克的十八烷基-3，5-双((1，1-二甲基乙基)-4-羟基苯丙酸酯和0.3千克的双水杨酸双酚A酯。
实施例4
按照和实施例1相同的方式制备高透光率的聚碳酸酯复合物，不同之处在于所述光扩散剂为0.5千克的三(2，4-二叔丁基苯基)亚磷酸酯、0.2千克的十八烷基-3，5-双((1，1-二甲基乙基)-4-羟基苯丙酸酯、0.2千克的双水杨酸双酚A酯和0.1千克的丙烯酸丁酯。
实施例5
按照和实施例1相同的方式制备高透光率的聚碳酸酯复合物，不同之处在于所述光扩散剂为0.5千克的三(2，4-二叔丁基苯基)亚磷酸酯、0.2千克的十八烷基-3，5-双((1，1-二甲基乙基)-4-羟基苯丙酸酯、0.05千克的双水杨酸双酚A酯和0.25千克的丙烯酸丁酯。
根据ASTM D1003，使用Nippon Denshoku的雾度仪NDH2000装置来测量透光率。结果如下：87％(实施例1)、54％(实施例2)、61％(实施例3)、69％(实施例4)和65(实施例5)。

Claims (1)

1.一种高透光率的聚碳酸酯，其特征在于，以重量份计，所述高透光率的聚碳酸酯包含下列成分：
(a)90份的聚碳酸酯；(b)1.0份的光扩散剂；(c)2.0份的阻燃剂；(d)1.0份的润滑剂；(e)0.5份的光稳定剂；以及(f)1.5份的增韧剂；
所述光扩散剂为0.5份三(2,4-二叔丁基苯基)亚磷酸酯、0.2份十八烷基-3,5-双(1,1-二甲基乙基)-4-羟基苯丙酸酯、0.1份双水杨酸双酚A酯和0.2份丙烯酸丁酯的混合；
所述阻燃剂为多聚芳基磷酸酯；
所述润滑剂为二甲基硅烷；
所述光稳定剂为2-羟基-4-正辛氧基二苯甲酮；
所述增韧剂为EVA。
CN201310034705.0A 2013-01-28 2013-01-28 一种高透光率的聚碳酸酯 Expired - Fee Related CN103044893B (zh)