CN103044884A - 一种聚碳酸酯组合物 - Google Patents
一种聚碳酸酯组合物 Download PDFInfo
- Publication number
- CN103044884A CN103044884A CN201210554044XA CN201210554044A CN103044884A CN 103044884 A CN103044884 A CN 103044884A CN 201210554044X A CN201210554044X A CN 201210554044XA CN 201210554044 A CN201210554044 A CN 201210554044A CN 103044884 A CN103044884 A CN 103044884A
- Authority
- CN
- China
- Prior art keywords
- parts
- phenyl
- sulfonic acid
- polycarbonate
- triethoxysilane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种聚碳酸酯组合物，由以下重量份的组分组成，双酚A型芳香族聚碳酸酯树脂30-45份、八苯基环四硅氧烷5-10份、乙烯基三烷氧基硅烷10-15份、甲基三烷氧基硅烷10-20份、苯基三烷氧基硅烷15-20份、硼酸三甲酯2-5份、硼酸三丁酯10-30份、甲基丙烯酸甲酯12-25份、顺丁烯二酸酐3-8份、苯基N-取代马来酰亚胺4-12份、全氟链烷磺酸的碱金属盐3-8份、全氟链烷磺酸的碱土金属盐1-5份、亚磷酸苯酯2-9份。该材料具有良好的耐候和阻燃性能。
Description
技术领域
本发明涉及高分子复合材料领域，尤其涉及一种聚碳酸酯组合物。
背景技术
随着以塑代钢和以塑代木步伐加快和可回收循环使用的环保观念日益加深，很多国家特别是欧美国家都出台了相应的法律法规，来鼓励使用环保材料，减少非环保材料的使用，因此很多行业如电信、IT和汽车等行业迫切需要可在户外长期使用具有高耐候性能的塑料材料来替代现有的许多不可回收循环利用的非环保材料。
聚碳酸酯以其优良的各项性能而被广泛应用于各行各业，而其无卤化阻燃改性和循环回收利用方面均领先于其他材料，是一种符合可持续发展的环保型材料。目前，仍主要采用添加阻燃剂的方法来提高聚碳酸酯的阻燃性，溴系阻燃剂由于含有卤素已逐渐被淘汰；磷酸酯阻燃剂是目前使用较广泛的一类无卤阻燃剂，但是以损失聚碳酸酯的力学性能和耐热性能为代价的；而磺酸盐类阻燃剂对聚碳酸酯的原有物性基本无影响，是聚碳酸酯的理想阻燃剂，但该阻燃聚碳酸酯材料仍不能满足户外使用对材料的耐候和耐高低温要求。
因此，有必要开发一种环保型户外用聚碳酸酯材料。
发明内容
本发明的目的在于克服现有技术存在的不足而提供一种户外用的、能耐聚碳酸酯组合物。
为了实现上述目的，本发明采用如下技术方案：
一种聚碳酸酯组合物，由以下重量份的组分组成，双酚A型芳香族聚碳酸酯树脂30-45份、八苯基环四硅氧烷5-10份、乙烯基三烷氧基硅烷10-15份、甲基三烷氧基硅烷10-20份、苯基三烷氧基硅烷15-20份、硼酸三甲酯2-5份、硼酸三丁酯10-30份、甲基丙烯酸甲酯12-25份、顺丁烯二酸酐3-8份、苯基N-取代马来酰亚胺4-12份、全氟链烷磺酸的碱金属盐3-8份、全氟链烷磺酸的碱土金属盐1-5份、亚磷酸苯酯2-9份。
与现有技术相比，本发明的阻燃聚碳酸酯组合物的优点在于采用了具有双重功能的有机硅增韧阻燃剂和协效的耐候体系，保持了聚碳酸酯原有的优良性能，并同时赋予了该材料良好的耐候和阻燃性能，可保持120摄氏度高温烘烤不变形和零下40摄氏度冲击韧性，能保证不同气候和温度条件下的使用性。该材料满足现行各国的环保法律法规，是一款高性能环保材料，适用于注塑成型各种电子电器设备、汽车和家电产品。
具体实施方式
下面结合实施例和比较例对本发明做进一步详细说明。该实施例只是为了详细说明，而不能解释为限制本发明的范围。
实施例1
一种聚碳酸酯组合物，由以下重量份的组分组成，双酚A型芳香族聚碳酸酯树脂30份、八苯基环四硅氧烷5份、乙烯基三烷氧基硅烷10份、甲基三烷氧基硅烷10份、苯基三烷氧基硅烷15份、硼酸三甲酯2份、硼酸三丁酯10份、甲基丙烯酸甲酯12份、顺丁烯二酸酐3份、苯基N-取代马来酰亚胺4份、全氟链烷磺酸的碱金属盐3份、全氟链烷磺酸的碱土金属盐1份、亚磷酸苯酯2份。
实施例2
一种聚碳酸酯组合物，由以下重量份的组分组成，双酚A型芳香族聚碳酸酯树脂45份、八苯基环四硅氧烷10份、乙烯基三烷氧基硅烷15份、甲基三烷氧基硅烷20份、苯基三烷氧基硅烷20份、硼酸三甲酯5份、硼酸三丁酯30份、甲基丙烯酸甲酯25份、顺丁烯二酸酐8份、苯基N-取代马来酰亚胺12份、全氟链烷磺酸的碱金属盐8份、全氟链烷磺酸的碱土金属盐5份、亚磷酸苯酯9份。
实施例3
一种聚碳酸酯组合物，由以下重量份的组分组成，双酚A型芳香族聚碳酸酯树脂35份、八苯基环四硅氧烷8份、乙烯基三烷氧基硅烷14份、甲基三烷氧基硅烷15份、苯基三烷氧基硅烷16份、硼酸三甲酯4份、硼酸三丁酯20份、甲基丙烯酸甲酯20份、顺丁烯二酸酐5份、苯基N-取代马来酰亚胺5份、全氟链烷磺酸的碱金属盐5份、全氟链烷磺酸的碱土金属盐4份、亚磷酸苯酯8份。
Claims (1)
1.一种聚碳酸酯组合物，其特征在于：由以下重量份的组分组成，双酚A型芳香族聚碳酸酯树脂30-45份、八苯基环四硅氧烷5-10份、乙烯基三烷氧基硅烷10-15份、甲基三烷氧基硅烷10-20份、苯基三烷氧基硅烷15-20份、硼酸三甲酯2-5份、硼酸三丁酯10-30份、甲基丙烯酸甲酯12-25份、顺丁烯二酸酐3-8份、苯基N-取代马来酰亚胺4-12份、全氟链烷磺酸的碱金属盐3-8份、全氟链烷磺酸的碱土金属盐1-5份、亚磷酸苯酯2-9份。