CN103044766A - 一种阻燃聚丙烯组合物 - Google Patents

一种阻燃聚丙烯组合物 Download PDF

Info

Publication number
CN103044766A
CN103044766A CN2012103777018A CN201210377701A CN103044766A CN 103044766 A CN103044766 A CN 103044766A CN 2012103777018 A CN2012103777018 A CN 2012103777018A CN 201210377701 A CN201210377701 A CN 201210377701A CN 103044766 A CN103044766 A CN 103044766A
Authority
CN
China
Prior art keywords
polypropylene
monomer
content
weight percent
inflaming retarding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103777018A
Other languages
English (en)
Inventor
赵立地
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2012103777018A priority Critical patent/CN103044766A/zh
Publication of CN103044766A publication Critical patent/CN103044766A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种阻燃聚丙烯组合物，由如下重量百分比组份组成：均聚聚丙烯30-50％，共聚聚丙烯20-40％，重质碳酸钙5-20％，十溴二苯乙烷5-10％，硬脂酸0.1-0.5％，四氟乙烯0-0.3％，所述共聚聚丙烯的第二单体为1-丁烯、1-戊烯或者1-己烯，第二单体的含量为共聚聚丙烯含量的5-10％，本发明以均聚聚丙烯和共聚聚丙烯为底料，以重质碳酸钙为填料，以十溴二苯乙烷和四氟乙烯为阻燃剂，以硬脂酸为润滑剂，配合相应的组份含量，既提高了材料的柔韧性，也具有很好的阻燃性，其阻燃性能的提高尤为明显，但是其耐热性和韧性也能很好的满足需求。

Description

一种阻燃聚丙烯组合物
技术领域
本发明涉及一种阻燃聚丙烯组合物。
背景技术
纯的聚丙烯具有密度小、耐腐蚀、加工方便等特性，但是却也由于其本身的物理化学性质的限制，存在在抗冲击差、易老化、收缩率大、使用温度不宜超过75℃等缺点，这些缺点的存在限制了其使用场所，不能最大程度的利用这种材料带来的好处。
因此，如何在保持其性能不降低的基础上，提高聚丙烯的耐热性能是今年来发展的一个方向，通常，研究人员会在聚丙烯材料中加入其他组分以提高其耐热性，但是想要在这么多材料中找到符合要求的添加组分是非常困难的。如CN94107609.3公开了一种溶液丁苯橡胶、无机填料等组分制备高抗冲击聚丙烯组合物，但是制品的拉伸强度最高不过28.3MPa，CN01120444.3公开了一只可替代ABS树脂的改性聚丙烯组合物，其拉伸强度虽然可达到35MPa，但缺口冲击强度只能达到180j/m，这证明想要找到理想的材料是比较困难的。
现有技术中的阻燃聚丙烯组合物存在阻燃性、绝缘性、材料韧性和易腐蚀、耐热性能之间的矛盾，不能达到一种较好的平衡，或者使两者性能都达到优良的效果，因此，市场的聚丙烯材料并不能满足有些场合的需求。
发明内容
本发明要解决的技术问题是提供一种成本低廉的阻燃性好的聚丙烯组合物，其耐热性和韧性都能满足要求。
本发明的内容是，
由如下重量百分比组份组成：
Figure BSA00000786328000021
所述共聚聚丙烯的第二单体为1-丁烯、1-戊烯或者1-己烯，第二单体的含量为共聚聚丙烯含量的5-10％。
优选的，由如下重量百分比组份组成：
Figure BSA00000786328000022
所述共聚聚丙烯的第二单体为1-丁烯、1-戊烯或者1-己烯，第二单体的含量为共聚聚丙烯含量的5-7％。
优选的，所述的均聚聚丙烯，在220℃、2.2kg压力下，熔体流动速率为0.1-0.3g/10min。
优选的，所述重质碳酸钙的颗粒细度为1-5μm。
本发明的制备方法是，(1)将原料按照重量百分比加入高速混合机；(2)充分搅拌，一般在1500-2000rpm速度下，搅拌2-3分钟；(3)、混合充分后的原料加入到挤出机中，挤出造粒，挤出机的速度可设置为50-100转/分，温度为180-200℃。
本发明的有益效果是，本发明以均聚聚丙烯和共聚聚丙烯为底料，以重质碳酸钙为填料，以十溴二苯乙烷和四氟乙烯为阻燃剂，以硬脂酸为润滑剂，配合相应的组份含量，既提高了材料的柔韧性，也具有很好的阻燃性，其阻燃性能的提高尤为明显，但是其耐热性和韧性也能很好的满足需求。
具体实施方式
实施例1
由如下重量百分比组份组成：
Figure BSA00000786328000031
所述共聚聚丙烯的第二单体为1-丁烯，第二单体的含量为共聚聚丙烯含量的5％。
制备方法是，(1)将上述原料按照重量百分比加入高速混合机；(2)充分搅拌，一般在2000rpm速度下，搅拌3分钟；(3)、混合充分后的原料加入到挤出机中，挤出造粒，挤出机的速度设置为100转/分，温度为180℃。
实施例2
由如下重量百分比组份组成：
Figure BSA00000786328000032
所述共聚聚丙烯的第二单体为1-戊烯，第二单体的含量为共聚聚丙烯含量的10％。
制备方法是，(1)将上述原料按照重量百分比加入高速混合机；(2)充分搅拌，一般在1500rpm速度下，搅拌2.5分钟；(3)、混合充分后的原料加入到挤出机中，挤出造粒，挤出机的速度设置为50转/分，温度为200℃。
实施例3
由如下重量百分比组份组成：
所述共聚聚丙烯的第二单体为1-己烯，第二单体的含量为共聚聚丙烯含量的8％。
制备方法是，(1)将上述原料按照重量百分比加入高速混合机；(2)充分搅拌，一般在1800rpm速度下，搅拌2分钟；(3)混合充分后的原料加入到挤出机中，挤出造粒，挤出机的速度设置为80转/分，温度为200℃。
测量性能如下：
实施例1 实施例2 实施例3 检测标准
拉伸强度(MPa) 39 36 38 GB/T6344-2008
熔体流动速率g/min 1.6 1.5 1.55 GB/T3682-2000
冲击强度KJ/m2 80 78 82 GB1943-2007
熔融指数g/10min 0.9 0.8 0.7 GB/T3682-2000

Claims (4)

1.一种阻燃聚丙烯组合物，其特征是，由如下重量百分比组份组成：
所述共聚聚丙烯的第二单体为1-丁烯、1-戊烯或者1-己烯，第二单体的含量为共聚聚丙烯含量的5-10％。
2.根据权利要求1所述的一种阻燃聚丙烯组合物，其特征是，由如下重量百分比组份组成：
Figure FSA00000786327900012
所述共聚聚丙烯的第二单体为1-丁烯、1-戊烯或者1-己烯，第二单体的含量为共聚聚丙烯含量的5-7％。
3.根据权利要求1或2所述的阻燃聚丙烯组合物，其特征是，所述的均聚聚丙烯，在220℃、2.2kg压力下，熔体流动速率为0.1-0.3g/10min。
4.根据权利要求1或2所述的阻燃聚丙烯组合物，其特征是，所述重质碳酸钙的颗粒细度为1-5μm。
CN2012103777018A 2012-09-07 2012-09-07 一种阻燃聚丙烯组合物 Pending CN103044766A (zh)