CN103031032A - 一种发泡粉末涂料 - Google Patents

一种发泡粉末涂料 Download PDF

Info

Publication number
CN103031032A
CN103031032A CN 201110294919 CN201110294919A CN103031032A CN 103031032 A CN103031032 A CN 103031032A CN 201110294919 CN201110294919 CN 201110294919 CN 201110294919 A CN201110294919 A CN 201110294919A CN 103031032 A CN103031032 A CN 103031032A
Authority
CN
China
Prior art keywords
foaming
urea
powder coating
foaming powder
powder paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201110294919
Other languages
English (en)
Inventor
陆东方
鹿存才
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU ZHENGLING COATING CO Ltd
Original Assignee
JIANGSU ZHENGLING COATING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU ZHENGLING COATING CO Ltd filed Critical JIANGSU ZHENGLING COATING CO Ltd
Priority to CN 201110294919 priority Critical patent/CN103031032A/zh
Publication of CN103031032A publication Critical patent/CN103031032A/zh
Pending legal-status Critical Current

Abstract

本发明公布了一种发泡粉末涂料。该发泡粉末涂料采用了以N，N－二亚硝基五次甲基四胺为发泡剂，以尿素为协效剂，且N，N－二亚硝基五次甲基四胺与尿素的重量比控制在5:1，该发明发泡层表面平整、密度更低，实用性更强，市场前景良好。

Description

一种发泡粉末涂料
技术领域
本发明涉及一种化工涂料、具体的说是一种发泡粉末涂料，属于静电涂装的粉末涂料技术领域。
技术背景
目前发泡技术是利用物理发泡或化学交联发泡使高分子材料发泡达到轻量、缓冲、吸音、吸震、保温、过滤、包装等功能之技术，传统发泡材料有聚苯乙烯、聚氯乙烯、聚氨酯、橡塑材料。发泡产品不只广泛的应用于民生用品上(如鞋材、水上运动器材、缓冲垫等)，在建材(空调保温管、地板、踢脚板等)、汽车及其它工业上(如包装、保温、防震、过滤等)也都有很大需求。
    但上述不少发泡物质存在降解时间长、回收难，尤其对环境造成显著污染，个别发泡物质吸水性强、使用质量难以保证，大多数产品还属于易燃有毒产品，应用隐患明显。
粉末涂料作为环保、节能、经济、高效的产品，逐渐取代液体油漆，成为发展速度和规模最快的涂料新技术，粉末发泡技术受到人们的关注。专利200610161615.8（一种发泡性粉末涂料）披露了发泡性粉末涂料的配方、工艺技术等，但发泡体的密度、孔隙率、表面平整度等不尽理想。
发明内容
本发明的目的在于：为了解决现有发泡物质存在的一些缺陷，本发明提供一种发泡粉末涂料，具有更好的发泡性和涂层质量，可涂装于各类金属建筑材料上，起到隔热、保温、防火等作用。
本发明解决采用问题的技术方案是：一种发泡粉末涂料，该发明的原料及配比为：环氧树脂E-12  45，酚醛环氧固化剂12，二甲基咪唑 0.25，颜填料10~15，N，N－二亚硝基五次甲基四胺5~10，尿素1~2，阻燃剂1～7。
配方中N，N－二亚硝基五次甲基四胺与尿素的重量比为5:1。
所述阻燃剂为四溴双酚A，十溴二苯乙烷、三氧化二锑、水和硼酸锌、磷酸三（2，3－二氯丙）酯等中的一种或两种以上。
制备的发泡粉末涂料在涂装的熔融流平阶段，发泡剂开始分解释放出气体，气体均匀分散于熔融的粉末涂层中，呈细密的泡沫状，涂层均匀膨胀。颜填料起到装饰、增加强度、降低成本的作用。
有益效果：与现有技术比较，本发明采用了以N，N－二亚硝基五次甲基四胺为发泡剂，以尿素为协效剂，且N，N－二亚硝基五次甲基四胺与尿素的重量比控制在5:1。发泡层表面平整、密度更低，实用性更强，市场前景良好。
具体实施方式
下面结合实施例进一步说明本发明的方案和效果。
配方1：（Wt％）
环氧树脂E-12     45
酚醛环氧固化剂   12
二甲基咪唑       0.25
钛白粉           10
硫酸钡            5
N，N－二亚硝基五次甲基四胺   5
尿素            1
十溴二苯乙烷    5
氧化锑         1.5。
将上述原料按熔融挤出混合法制备，可得发泡粉末涂料，经200℃烘烤加热发泡，发泡层密度40 kg/m3，表面平整，发泡层均匀致密，阻燃试验离火自熄。
配方1：（Wt％）
环氧树脂E-12     45
酚醛环氧固化剂   12
二甲基咪唑      0.25
硫酸钡          13
酞菁蓝          0.5
N，N－二亚硝基五次甲基四胺   7.5
尿素     1.5
四溴双酚A      5
氧化锑         1。
将上述原料按熔融挤出混合法制备，可得发泡粉末涂料，经200℃烘烤加热发泡，发泡层密度48 kg/m3，表面平整，发泡层均匀致密。

Claims (1)

1.一种发泡粉末涂料，其特征在于：该发明原料制成的重量比（Wt%）：环氧树脂E-12 45，酚醛环氧固化剂12，二甲基咪唑 0.25，颜填料10~15，N，N－二亚硝基五次甲基四胺5~10，尿素1~2，阻燃剂1～7，所述N，N－二亚硝基五次甲基四胺与尿素的重量比为5:1；该发明的制备工艺为：原料按熔融挤出混合法制备，得发泡粉末涂料，经200℃烘烤加热发泡即可。
CN 201110294919 2011-10-08 2011-10-08 一种发泡粉末涂料 Pending CN103031032A (zh)