CN103014744B - Method for cleaning industrial metal plate - Google Patents
Method for cleaning industrial metal plate Download PDFInfo
- Publication number
- CN103014744B CN103014744B CN201210393024.9A CN201210393024A CN103014744B CN 103014744 B CN103014744 B CN 103014744B CN 201210393024 A CN201210393024 A CN 201210393024A CN 103014744 B CN103014744 B CN 103014744B
- Authority
- CN
- China
- Prior art keywords
- metal plate
- clean
- cleaning
- industrial metal
- industrial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A method for cleaning an industrial metal plate comprises the following steps of: (1) adopting a cleaning agent which consists of the following components in weight percent: 2.3-5.6% of fatty alcohol-polyoxyethylene ether, 1.2-2.7% of ethanol, 0.5-1.3% of sodium silicate, 0.2-1.6% of citric acid, 1.1-2.0% of sodium benzoate, 2.2-3.4% of sodium dodecyl benzene sulfonate, 0.3-0.9% of sodium molybdate, 0.1-0.5% of oleic acid, 0.2-0.5% of sodium hydrogen phosphate, 1.2-6.6% of ethylene diamine tetraacetic acid, 3.1-3.6% of benzotriazole, 2.5-3.5% of isopropyl alcohol and the balance of deionized water; (2) pouring the cleaning agent into an ultrasonic cleaning tank; (3) putting the industrial metal plate into the ultrasonic cleaning tank to be cleaned for 3-5 minutes under the condition of 35 DEG C-40 DEG C; and then, taking the industrial metal plate out, using clean water to clean the surface of the metal plate cleanly and airing to complete the cleaning. The method for cleaning can be adopted to quickly remove dirt on the surface of the metal plate, moreover, the metal plate cannot be corroded, the surface of the cleaned metal plate can be smooth and bright, the cleaning efficiency is higher than 99%, and the method has an obvious effect.
Description
Technical field
The present invention relates to a kind of purging method, especially a kind of industrial metal plate purging method, belongs to industrial equipments cleaning technique field.
Background technology
According to the applicant understood, in prior art, there is no the special clean-out system for industrial metal plate, be difficult to the greasy dirt on metal sheet thoroughly to clean up.Need a kind of efficient cleaner with strong points badly.
Summary of the invention
Technical problem to be solved by this invention is: overcome the problem that prior art exists, a kind of industrial metal plate purging method is provided, can remove fast the dirt of metal sheet surface, and can corroding metal plate, can make smoothly light of metal sheet surface after cleaning.
The technical scheme that the present invention solves its technical problem is as follows: a kind of industrial metal board cleaning agent, it is characterized in that, and by the component of following weight percent, formed:
Surplus is deionized water.
The preparation method of above-mentioned clean-out system, comprises the following steps:
(1) in stirrer, add by weight percentage successively 2.3-5.6% fatty alcohol-polyoxyethylene ether, 1.2-2.7% ethanol, 0.5-1.3% water glass, 0.2-1.6% citric acid, 1.1-2.0% Sodium Benzoate, 2.2-3.4% Sodium dodecylbenzene sulfonate, 0.3-0.9% Sodium orthomolybdate, 0.1-0.5% oleic acid, 0.2-0.5% Sodium phosphate dibasic, 1.2-6.6% ethylenediamine tetraacetic acid (EDTA), 3.1-3.6% benzotriazole, 2.5-3.5% Virahol; Finally adding deionized water to make total weight percent is 100%;
(2) the clean-out system finished product that stirs to obtain.
The industrial metal plate purging method that adopts above-mentioned clean-out system, comprises the following steps:
(1) adopt the clean-out system being formed by following weight percent component:
Surplus is deionized water;
(2) described clean-out system is poured onto in ultrasonic cleaning tank;
(3) industrial metal plate is put into ultrasonic cleaning tank, under 35 ℃ of-40 ℃ of conditions, clean 3-5 minute; Then take out industrial metal plate, with clear water, metal sheet surface is rinsed well, then dry and complete cleaning.
The present patent application people is through repeatedly, in depth experimental study just draws the clean-out system that adopts above-mentioned formula, this clean-out system can be removed the dirt of metal sheet surface fast, and can corroding metal plate, can make the metal sheet surface after cleaning smoothly bright, cleaning efficiency is greater than 99%, is the crystallization that the present patent application people pays a large amount of painstaking effort.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail.But the invention is not restricted to given example.
Embodiment 1
The industrial metal board cleaning agent of the present embodiment is comprised of the component of following weight percent:
Surplus is deionized water.
The preparation method of the present embodiment clean-out system, comprises the following steps:
(1) in stirrer, add by weight percentage successively 2.3% fatty alcohol-polyoxyethylene ether, 1.2% ethanol, 0.5% water glass, 0.2% citric acid, 1.1% Sodium Benzoate, 2.2% Sodium dodecylbenzene sulfonate, 0.3% Sodium orthomolybdate, 0.1% oleic acid, 0.2% Sodium phosphate dibasic, 1.2% ethylenediamine tetraacetic acid (EDTA), 3.1% benzotriazole, 2.5% Virahol; Finally adding deionized water to make total weight percent is 100%;
(2) the clean-out system finished product that stirs to obtain.
Adopt the purging method of the present embodiment clean-out system to comprise the following steps: (1) is poured onto the present embodiment clean-out system in ultrasonic cleaning tank; (2) industrial metal plate is put into ultrasonic cleaning tank, under 35 ℃ of conditions, clean 5 minutes; Then take out industrial metal plate, with clear water, metal sheet surface is rinsed well, then dry and complete cleaning.Metal sheet surface after cleaning is light smoothly, and cleaning efficiency is greater than 99%, and effect is remarkable.
Embodiment 2
The industrial metal board cleaning agent of the present embodiment is comprised of the component of following weight percent:
Surplus is deionized water.
The preparation method of the present embodiment clean-out system, comprises the following steps:
(1) in stirrer, add by weight percentage successively 5.6% fatty alcohol-polyoxyethylene ether, 2.7% ethanol, 1.3% water glass, 1.6% citric acid, 2.0% Sodium Benzoate, 3.4% Sodium dodecylbenzene sulfonate, 0.9% Sodium orthomolybdate, 0.5% oleic acid, 0.5% Sodium phosphate dibasic, 6.6% ethylenediamine tetraacetic acid (EDTA), 3.6% benzotriazole, 3.5% Virahol; Finally adding deionized water to make total weight percent is 100%
(2) the clean-out system finished product that stirs to obtain.
Adopt the purging method of the present embodiment clean-out system to comprise the following steps: (1) is poured onto the present embodiment clean-out system in ultrasonic cleaning tank; (2) industrial metal plate is put into ultrasonic cleaning tank, under 40 ℃ of conditions, clean 3 minutes; Then take out industrial metal plate, with clear water, metal sheet surface is rinsed well, then dry and complete cleaning.Metal sheet surface after cleaning is light smoothly, and cleaning efficiency is greater than 99%, and effect is remarkable.
Embodiment 3
The industrial metal board cleaning agent of the present embodiment is comprised of the component of following weight percent:
Surplus is deionized water.
The preparation method of the present embodiment clean-out system, comprises the following steps:
(1) in stirrer, add by weight percentage successively 3.2% fatty alcohol-polyoxyethylene ether, 1.5% ethanol, 0.7% water glass, 0.8% citric acid, 1.6% Sodium Benzoate, 3.0% Sodium dodecylbenzene sulfonate, 0.4% Sodium orthomolybdate, 0.3% oleic acid, 0.3% Sodium phosphate dibasic, 4.6% ethylenediamine tetraacetic acid (EDTA), 3.3% benzotriazole, 2.8% Virahol; Finally adding deionized water to make total weight percent is 100%;
(2) the clean-out system finished product that stirs to obtain.
Adopt the purging method of the present embodiment clean-out system to comprise the following steps: (1) is poured onto the present embodiment clean-out system in ultrasonic cleaning tank; (2) industrial metal plate is put into ultrasonic cleaning tank, under 37 ℃ of conditions, clean 4 minutes; Then take out industrial metal plate, with clear water, metal sheet surface is rinsed well, then dry and complete cleaning.Metal sheet surface after cleaning is light smoothly, and cleaning efficiency is greater than 99%, and effect is remarkable.
Embodiment 4
The industrial metal board cleaning agent of the present embodiment is comprised of the component of following weight percent:
Surplus is deionized water.
The preparation method of the present embodiment clean-out system, comprises the following steps:
(1) in stirrer, add by weight percentage successively 4.5% fatty alcohol-polyoxyethylene ether, 2.2% ethanol, 1.1% water glass, 1.2% citric acid, 1.8% Sodium Benzoate, 3.2% Sodium dodecylbenzene sulfonate, 0.7% Sodium orthomolybdate, 0.4% oleic acid, 0.4% Sodium phosphate dibasic, 5.2% ethylenediamine tetraacetic acid (EDTA), 3.5% benzotriazole, 3.1% Virahol; Finally adding deionized water to make total weight percent is 100%;
(2) the clean-out system finished product that stirs to obtain.
Adopt the purging method of the present embodiment clean-out system to comprise the following steps: (1) is poured onto the present embodiment clean-out system in ultrasonic cleaning tank; (2) industrial metal plate is put into ultrasonic cleaning tank, under 38 ℃ of conditions, clean 4 minutes; Then take out industrial metal plate, with clear water, metal sheet surface is rinsed well, then dry and complete cleaning.Metal sheet surface after cleaning is light smoothly, and cleaning efficiency is greater than 99%, and effect is remarkable.
Claims (5)
1. an industrial metal plate purging method, is characterized in that, comprises the following steps:
(1) adopt the clean-out system being formed by following weight percent component:
Surplus is deionized water;
(2) described clean-out system is poured onto in ultrasonic cleaning tank;
(3) industrial metal plate is put into ultrasonic cleaning tank, under 35 ℃ of-40 ℃ of conditions, clean 3-5 minute; Then take out industrial metal plate, with clear water, metal sheet surface is rinsed well, then dry and complete cleaning.
2. industrial metal plate purging method according to claim 1, is characterized in that, in step (1), adopts the clean-out system being comprised of following weight percent component:
Surplus is deionized water.
3. industrial metal plate purging method according to claim 1, is characterized in that, in step (1), adopts the clean-out system being comprised of following weight percent component:
Surplus is deionized water.
4. industrial metal plate purging method according to claim 1, is characterized in that, in step (3), industrial metal plate is put into ultrasonic cleaning tank, under 37 ℃ of conditions, cleans 4 minutes; Then take out industrial metal plate, with clear water, metal sheet surface is rinsed well, then dry and complete cleaning.
5. industrial metal plate purging method according to claim 1, is characterized in that, in step (3), industrial metal plate is put into ultrasonic cleaning tank, under 38 ℃ of conditions, cleans 4 minutes; Then take out industrial metal plate, with clear water, metal sheet surface is rinsed well, then dry and complete cleaning.