CN102994284A - Wax removal cleaning agent - Google Patents
Wax removal cleaning agent Download PDFInfo
- Publication number
- CN102994284A CN102994284A CN2012103965407A CN201210396540A CN102994284A CN 102994284 A CN102994284 A CN 102994284A CN 2012103965407 A CN2012103965407 A CN 2012103965407A CN 201210396540 A CN201210396540 A CN 201210396540A CN 102994284 A CN102994284 A CN 102994284A
- Authority
- CN
- China
- Prior art keywords
- clean
- out system
- weight percent
- cleaning agent
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a wax removal cleaning agent, which is composed of the following constituents in percentage by weight: 7.6-10.3% of octaphenyl polyoxyethyiene, 3.5-6.7% of salicylic acid, 1.5-5.2% of acetamide, 2.6-7.8% of 2-hydroxyphosphonoacetic acid, 4.1-8.3% of sodium silicate, 3.7-5.8% of sodium gluconate, 5.1-9.2% of alcohol, 1.3-4.0% of isopropanol, 5.5-9.8% of trichloro ethylene, and the balance of deionized water. The cleaning agent can be used for rapidly removing waxy dirt on the surface of an object without corrosion on the surface of the object, and making the cleaned object clean as new.
Description
Technical field
The present invention relates to a kind of paraffin removal clean-out system, belong to industrial cleaning technique field.
Background technology
Understand according to the applicant, there is no targetedly paraffin removal clean-out system in the prior art, be difficult to the wax dirt of body surface is thoroughly cleaned up.Need a kind of efficient cleaner with strong points badly.
Summary of the invention
Technical problem to be solved by this invention is: overcome the problem that prior art exists, a kind of paraffin removal clean-out system is provided, can remove fast the wax dirt of body surface, and can the erosion surface, can make the object after the cleaning clean as new.
The technical scheme that the present invention solves its technical problem is as follows:
A kind of paraffin removal clean-out system is characterized in that, is comprised of the component of following weight percent:
The preparation method of above-mentioned clean-out system may further comprise the steps:
(1) in stirrer, adds by weight percentage successively 7.6-10.3% polyoxyethylene octylphenol ether, 3.5-6.7% Whitfield's ointment, 1.5-5.2% ethanamide, 2.6-7.8%2-HPAA, 4.1-8.3% water glass, 3.7-5.8% Sunmorl N 60S, 5.1-9.2% ethanol, 1.3-4.0% Virahol, 5.5-9.8% trieline; Adding at last deionized water, to make total weight percent be 100%;
(2) the clean-out system finished product that stirs to get.
Adopt the purging method of above-mentioned clean-out system, may further comprise the steps:
(1) adopt the clean-out system that is comprised of following weight percent component: 7.6-10.3% polyoxyethylene octylphenol ether, 3.5-6.7% Whitfield's ointment, 1.5-5.2% ethanamide, 2.6-7.8%2-HPAA, 4.1-8.3% water glass, 3.7-5.8% Sunmorl N 60S, 5.1-9.2% ethanol, 1.3-4.0% Virahol, 5.5-9.8% trieline, surplus are deionized water;
(2) will clean first in the cloth immersion clean-out system of usefulness, use again this cloth cleaning piece surface, until the body surface wax is removed totally.
The present patent application people is through repeatedly, in depth experimental study just draws the clean-out system that adopts above-mentioned prescription, this clean-out system can be removed the wax dirt of body surface fast, and can not corrode object, can make the object after the cleaning clean as new, cleaning efficiency is the crystallization that the present patent application people pays a large amount of painstaking effort greater than 99%.
Embodiment
Below in conjunction with embodiment the present invention is described in further detail.But the invention is not restricted to given example.
Embodiment 1
Present embodiment paraffin removal clean-out system is comprised of the component of following weight percent:
The present embodiment clean-out system is the preparation method may further comprise the steps:
(1) in stirrer, adds by weight percentage successively 7.6% polyoxyethylene octylphenol ether, 3.5% Whitfield's ointment, 1.5% ethanamide, 2.6%2-HPAA, 4.1% water glass, 3.7% Sunmorl N 60S, 5.1% ethanol, 1.3% Virahol, 5.5% trieline; Adding at last deionized water, to make total weight percent be 100%;
(2) the clean-out system finished product that stirs to get.
The present embodiment purging method may further comprise the steps:
(1) adopt the clean-out system that is comprised of following weight percent component: 7.6% polyoxyethylene octylphenol ether, 3.5% Whitfield's ointment, 1.5% ethanamide, 2.6%2-HPAA, 4.1% water glass, 3.7% Sunmorl N 60S, 5.1% ethanol, 1.3% Virahol, 5.5% trieline, surplus are deionized water;
(2) will clean first in the cloth immersion clean-out system of usefulness, use again this cloth cleaning piece surface, until the body surface wax is removed totally.
Object after the cleaning is clean as new, and cleaning efficiency is greater than 99%.
Embodiment 2
Present embodiment paraffin removal clean-out system is comprised of the component of following weight percent:
The present embodiment clean-out system is the preparation method may further comprise the steps:
(1) in stirrer, adds by weight percentage successively 10.3% polyoxyethylene octylphenol ether, 6.7% Whitfield's ointment, 5.2% ethanamide, 7.8%2-HPAA, 8.3% water glass, 5.8% Sunmorl N 60S, 9.2% ethanol, 4.0% Virahol, 9.8% trieline; Adding at last deionized water, to make total weight percent be 100%;
(2) the clean-out system finished product that stirs to get.
The present embodiment purging method may further comprise the steps:
(1) adopt the clean-out system that is comprised of following weight percent component: 10.3% polyoxyethylene octylphenol ether, 6.7% Whitfield's ointment, 5.2% ethanamide, 7.8%2-HPAA, 8.3% water glass, 5.8% Sunmorl N 60S, 9.2% ethanol, 4.0% Virahol, 9.8% trieline, surplus are deionized water;
(2) will clean first in the cloth immersion clean-out system of usefulness, use again this cloth cleaning piece surface, until the body surface wax is removed totally.
Object after the cleaning is clean as new, and cleaning efficiency is greater than 99%.
Embodiment 3
Present embodiment paraffin removal clean-out system is comprised of the component of following weight percent:
The present embodiment clean-out system is the preparation method may further comprise the steps:
(1) in stirrer, adds by weight percentage successively 8.4% polyoxyethylene octylphenol ether, 5.1% Whitfield's ointment, 2.7% ethanamide, 4.3%2-HPAA, 5.8% water glass, 4.3% Sunmorl N 60S, 6.7% ethanol, 2.7% Virahol, 8.4% trieline; Adding at last deionized water, to make total weight percent be 100%;
(2) the clean-out system finished product that stirs to get.
The present embodiment purging method may further comprise the steps:
(1) adopt the clean-out system that is comprised of following weight percent component: 8.4% polyoxyethylene octylphenol ether, 5.1% Whitfield's ointment, 2.7% ethanamide, 4.3%2-HPAA, 5.8% water glass, 4.3% Sunmorl N 60S, 6.7% ethanol, 2.7% Virahol, 8.4% trieline, surplus are deionized water;
(2) will clean first in the cloth immersion clean-out system of usefulness, use again this cloth cleaning piece surface, until the body surface wax is removed totally.
Object after the cleaning is clean as new, and cleaning efficiency is greater than 99%.
Embodiment 4
Present embodiment paraffin removal clean-out system is comprised of the component of following weight percent:
The present embodiment clean-out system is the preparation method may further comprise the steps:
(1) in stirrer, adds by weight percentage successively 9.8% polyoxyethylene octylphenol ether, 4.2% Whitfield's ointment, 3.9% ethanamide, 6.2%2-HPAA, 7.1% water glass, 5.4% Sunmorl N 60S, 8.4% ethanol, 3.6% Virahol, 6.9% trieline; Adding at last deionized water, to make total weight percent be 100%;
(2) the clean-out system finished product that stirs to get.
The present embodiment purging method may further comprise the steps:
(1) adopt the clean-out system that is comprised of following weight percent component: 9.8% polyoxyethylene octylphenol ether, 4.2% Whitfield's ointment, 3.9% ethanamide, 6.2%2-HPAA, 7.1% water glass, 5.4% Sunmorl N 60S, 8.4% ethanol, 3.6% Virahol, 6.9% trieline, surplus are deionized water;
(2) will clean first in the cloth immersion clean-out system of usefulness, use again this cloth cleaning piece surface, until the body surface wax is removed totally.
Object after the cleaning is clean as new, and cleaning efficiency is greater than 99%.
Claims (3)