CN103012916B - 一种含有尼龙pa12的包装用薄膜 - Google Patents
一种含有尼龙pa12的包装用薄膜 Download PDFInfo
- Publication number
- CN103012916B CN103012916B CN201210482127.2A CN201210482127A CN103012916B CN 103012916 B CN103012916 B CN 103012916B CN 201210482127 A CN201210482127 A CN 201210482127A CN 103012916 B CN103012916 B CN 103012916B
- Authority
- CN
- China
- Prior art keywords
- powder
- film containing
- packaging film
- nylon
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种含有尼龙PA12的包装用薄膜，其是由下述重量份的原料制得：尼龙PA12 18-20、LDPE低密度聚乙烯23-26、SG-1型聚氯乙烯12-16、环氧大豆油3-5、聚乙烯蜡粉2-3、异丙基二硬脂酰氧基铝酸酯1-2、硅藻土8-12、聚异丁烯1.4-2.5、聚-4-甲基-1-戊烯0.8-1.5、氧化锌1-2、滑石粉5-8、树木灰烬0.8-1.2、间苯二甲酸酯1.2-2.5、硬脂酸0.8-1.6、甲基三乙氧基硅烷1.5-3、二茂铁0.9-1.8、改性海泡石粉4-6。本发明阻隔性和气密性好，耐压性和耐冲击性优秀，同时又具有热封强度高、热封性能好的特点。
Description
技术领域
本发明涉及包装材料领域，确切地说是一种含有尼龙PA12的包装用薄膜。
背景技术
我国是世界包装制造和消费大国，塑料包装在包装产业总产值中的比例已超过30%，成为包装产业中的生力军，在食品、饮料、日用品及工农业生产各个领域发挥着不可替代的作用。近年来，塑料包装行业的包装产品、包装材料平稳增长，包装新材料、新工艺、新技术、新产品不断涌现。食品包装塑料基材膜通常用聚乙烯原料生产，当前市场上有多种性能优越的可用于制作食品包装塑料基材膜的聚乙烯原料。从主要塑料品种来看，在塑料包装领域，高密度聚乙烯薄膜的消耗量将继续稳定增长。单层的聚乙烯薄膜对氧等气体的阻隔性差，包装油炸类等食品时，易造成封口处污染，一般的液体包装聚乙烯薄膜对此类包装的封口性能差，不能满足其包装工艺和包装物品存放期的要求，因此必须采用阻隔性能和夹杂封口性能都好的多层聚乙烯改性薄膜或复合薄膜。
发明内容
本发明的目的一种热封强度高的含有尼龙PA12的包装用薄膜。
上述目的通过以下方案实现：
一种含有尼龙PA12的包装用薄膜，其特征在于：其是由下述重量份的原料制得：尼龙PA1218-20、LDPE低密度聚乙烯23-26、SG-1型聚氯乙烯12-16、环氧大豆油3-5、聚乙烯蜡粉2-3、异丙基二硬脂酰氧基铝酸酯1-2、硅藻土8-12、聚异丁烯1.4-2.5、聚-4-甲基-1-戊烯0.8-1.5、氧化锌1-2、滑石粉5-8、树木灰烬0.8-1.2、间苯二甲酸酯1.2-2.5、硬脂酸0.8-1.6、甲基三乙氧基硅烷1.5-3、二茂铁0.9-1.8、改性海泡石粉4-6；
所述的改性海泡石粉的制备方法为：将海泡石用浓度为8-12%的氢氧化钠溶液浸泡5-7小时，再于600-700℃下煅烧4-6小时，研成粉末，过200-400目筛，再与相当于粉末重量3-5%的平平加混合，搅拌均匀后，即得。
所述的一种含有尼龙PA12的包装用薄膜，其特征在于：制备方法包括以下步骤：
（1）将环氧大豆油、聚乙烯蜡粉加入到混料机中，升温至80-85℃，加入SG-1型聚氯乙烯搅拌4-8分钟后，加入异丙基二硬脂酰氧基铝酸酯搅拌12-16分钟后，再加入改性海泡石粉，加热至100-110℃，搅拌25-35分钟；
（2）、再加入其它原料搅拌均匀后送入挤出机熔体挤出，熔融温度为180-190℃；进行模头吹膜定型，模头温度是由下向上逐渐升高，其范围控制在185-200℃；然后牵引切割；最后收卷，即得。
所述的一种含有尼龙PA12的包装用薄膜，其特征在于：所述挤出机的转速控制在90-110r/min。
本发明的有益效果为：本发明阻隔性和气密性好，耐压性和耐冲击性优秀，同时又具有热封强度高、热封性能好的特点。
具体实施方式
一种含有尼龙PA12的包装用薄膜，其是由下述重量份（kg)的原料制得：尼龙PA1220、LDPE低密度聚乙烯25、SG-1型聚氯乙烯15、环氧大豆油5、聚乙烯蜡粉2.5、异丙基二硬脂酰氧基铝酸酯1、硅藻土9.5、聚异丁烯2.5、聚-4-甲基-1-戊烯0.8、氧化锌2、滑石粉8、树木灰烬1.2、间苯二甲酸酯2.2、硬脂酸1.6、甲基三乙氧基硅烷3、二茂铁1.8、改性海泡石粉6；
所述的改性海泡石粉的制备方法为：将海泡石用浓度为12%的氢氧化钠溶液浸泡7小时，再于700℃下煅烧6小时，研成粉末，过400目筛，再与相当于粉末重量5%的平平加混合，搅拌均匀后，即得。
所述的一种含有尼龙PA12的包装用薄膜，制备方法包括以下步骤：
（1）将环氧大豆油、聚乙烯蜡粉加入到混料机中，升温至85℃，加入SG-1型聚氯乙烯搅拌8分钟后，加入异丙基二硬脂酰氧基铝酸酯搅拌16分钟后，再加入改性海泡石粉，加热至110℃，搅拌35分钟；
（2）、再加入其它原料搅拌均匀后送入挤出机熔体挤出，挤出机的转速控制在90r/min，熔融温度为180℃；进行模头吹膜定型，模头温度是由下向上逐渐升高，其范围控制在200℃；然后牵引切割；最后收卷，即得。
本实施例生产出的产品的性能参数为：拉伸强度：46Mpa；断裂伸长率：1019%；热封强度：10.9；摩擦系数：0.205。
Claims (3)
1.一种含有尼龙PA12的包装用薄膜，其特征在于：其是由下述重量份的原料制得：尼龙PA1218-20、LDPE低密度聚乙烯23-26、SG-1型聚氯乙烯12-16、环氧大豆油3-5、聚乙烯蜡粉2-3、异丙基二硬脂酰氧基铝酸酯1-2、硅藻土8-12、聚异丁烯1.4-2.5、聚-4-甲基-1-戊烯0.8-1.5、氧化锌1-2、滑石粉5-8、树木灰烬0.8-1.2、间苯二甲酸酯1.2-2.5、硬脂酸0.8-1.6、甲基三乙氧基硅烷1.5-3、二茂铁0.9-1.8、改性海泡石粉4-6；
所述的改性海泡石粉的制备方法为：将海泡石用浓度为8-12%的氢氧化钠溶液浸泡5-7小时，再于600-700℃下煅烧4-6小时，研成粉末，过200-400目筛，再与相当于粉末重量3-5%的平平加混合，搅拌均匀后，即得。
2.根据权利要求1所述的一种含有尼龙PA12的包装用薄膜，其特征在于：制备方法包括以下步骤：
（1）将环氧大豆油、聚乙烯蜡粉加入到混料机中，升温至80-85℃，加入SG-1型聚氯乙烯搅拌4-8分钟后，加入异丙基二硬脂酰氧基铝酸酯搅拌12-16分钟后，再加入改性海泡石粉，加热至100-110℃，搅拌25-35分钟；
（2）、再加入其它原料搅拌均匀后送入挤出机熔体挤出，熔融温度为180-190℃；进行模头吹膜定型，模头温度是由下向上逐渐升高，其范围控制在185-200℃；然后牵引切割；最后收卷，即得。
3.根据权利要求2所述的一种含有尼龙PA12的包装用薄膜，其特征在于：所述挤出机的转速控制在90-110r/min。