CN103012889A - 一种氯丁胶布拼接封皮用氯丁橡胶配方及制作方法 - Google Patents

一种氯丁胶布拼接封皮用氯丁橡胶配方及制作方法 Download PDF

Info

Publication number
CN103012889A
CN103012889A CN2012105658032A CN201210565803A CN103012889A CN 103012889 A CN103012889 A CN 103012889A CN 2012105658032 A CN2012105658032 A CN 2012105658032A CN 201210565803 A CN201210565803 A CN 201210565803A CN 103012889 A CN103012889 A CN 103012889A
Authority
CN
China
Prior art keywords
chloroprene rubber
rubber
minutes
antioxidant
detu
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012105658032A
Other languages
English (en)
Other versions
CN103012889B (zh
Inventor
原晓城
马义明
张景亮
李学东
郑玥
商宏超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin Rubber Industry Institute Co ltd
Original Assignee
Tianjin Rubber Industry Institute
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin Rubber Industry Institute filed Critical Tianjin Rubber Industry Institute
Priority to CN201210565803.2A priority Critical patent/CN103012889B/zh
Publication of CN103012889A publication Critical patent/CN103012889A/zh
Application granted granted Critical
Publication of CN103012889B publication Critical patent/CN103012889B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种氯丁胶布拼接封皮用氯丁橡胶配方及制作方法，属于橡胶领域，是将密炼、开炼、下片和硫化胶片工艺。本发明采用DETU，用作氯丁橡胶和丁基橡胶硫化促进剂，保持胶料的基本力学性能的同时，赋予胶料较快的硫化速度；采用DOS极性增塑剂，能够与氯丁橡胶很好的相容；产品各项物理性能指标都符合标准要求，尤其外观有了很大改善。

Description

一种氯丁胶布拼接封皮用氯丁橡胶配方及制作方法
技术领域
本发明涉及橡胶技术领域，特别涉及一种氯丁胶布拼接封皮用氯丁橡胶配方及制作方法。 
背景技术
许多工程胶布（如水坝布、气垫船围裙等）幅宽较大，需要若干块胶布拼接成型。其拼接缝需要覆一层橡胶，进行封皮二次硫化，从而使拼接部位外观平整光滑，起到更好的防护作用。但封皮配方硫化体系若不合理，定型速度较慢，极易导致拼接部位封皮边缘的橡胶呈蜂窝状；封皮配方软化体系若不合理，胶料发粘或者流动性差，极易导致无法下片或者拼接部位封皮边缘凸起。 
发明内容
针对现有技术的不足，本发明目的在于克服上述的缺陷，提供一种氯丁胶布拼接封皮用氯丁橡胶配方及制作方法，通过资料及大量试验实践确定，在氯丁配方硫化体系中采用定型速度较快的DETU，在增塑体系中采用相容性较好的DOS可有效地解决上述问题，保证胶布拼接外观。 
本发明的目的是通过以下技术方案实现的：一种氯丁胶布拼接封皮用氯丁橡胶配方，其特征在于：它包括如下组份：以橡胶为基础量100，其重量份数比为： 
氯丁橡胶CR 232            100.0
ZnO                     3.0～10.0
MgO                   3.0～10.0
橡胶促进剂DM         0.5～5.0
橡胶促进剂DETU       0.5～5.0
炭黑N550             10～40.0
陶土                  5.0～20.0
增塑剂DOS            5.0～15.0
防护蜡             　　1.0～3.0
防老剂A   　　　　　　　　1.0～2.0
防老剂4010NA　　　　　　1.0～2.0。
一种氯丁胶布拼接封皮用氯丁橡胶的制作方法，其特征在于：　　　 
（一）按照以下重量份数比进行各组份配料：
氯丁橡胶CR 232            100.0
ZnO                     3.0～10.0
MgO                   3.0～10.0
橡胶促进剂DM         0.5～5.0
橡胶促进剂DETU       0.5～5.0
炭黑N550             10～40.0
陶土                  5.0～20.0
增塑剂DOS            5.0～15.0
防护蜡             　　1.0～3.0
防老剂A   　　　　　　　　1.0～2.0
防老剂4010NA　　　　　　1.0～2.0；
（二）制作方法依次为：
１、密炼：低于110℃，密炼6分钟；
２、开炼：50至60℃，开炼8分钟；
３、下片：50至60℃，2分钟；
４、硫化胶片：151℃，40分钟；
５、按标准裁取试样；
６、性能检测。
本发明的优点和有益效果是： 
１、DETU化学名为二乙基硫脲，可用作氯丁橡胶和丁基橡胶硫化促进剂，它能保持胶料的基本力学性能的同时，赋予胶料较快的硫化速度。
２、DOS化学名称为癸二酸二辛酯，它是一种极性增塑剂，能够与氯丁橡胶很好的相容。 
３、各项物理性能指标都符合标准要求，尤其外观有了很大改善。 
具体实施方式
一种氯丁胶布拼接封皮用氯丁橡胶，按以下配方实施： 
Figure 1
按所列配方中原材料及用量进行混炼加工：橡胶、原材料称量——低于110℃，密炼6分钟——50至60℃，开炼8分钟——下片：50至60℃，2分钟——151℃，硫化胶片40分钟——按标准裁取试样——性能检测。
下面是对含有DETU和DOS的氯丁胶布拼接封皮用氯丁橡胶配方与传统配方（不含DETU、不含DETU和DOS）的性能对比： 
序号 性能 标准要求 含DETU和DOS 不含DETU 不含DETU和DOS
1 外观 拼接部位封皮胶料无海绵状，无凸起 无海绵、无凸起 拼接边缘胶料呈海绵状 拼接边缘胶料呈海绵状、局部有凸起
1 T10/s ≤90 78 129 80
2 ML1+4 50±5 49 52 61
3 拉伸强度/Mpa ≥18 20.2 19.7 19.2
4 扯断伸长率/% ≥450 600 621 630
5 撕裂/N*mm-1 ≥40 54 60 51
通过含有DETU和DOS的氯丁胶布拼接封皮用氯丁橡胶配方与传统配方的性能对比分析，含有DETU和DOS各项物理性能指标都符合标准要求，尤其外观有了很大改善。

Claims (2)

1.一种氯丁胶布拼接封皮用氯丁橡胶配方，其特征在于：它包括如下组份：以橡胶为基础量100，其重量份数比为：
氯丁橡胶CR 232            100.0；
ZnO                     3.0～10.0；
MgO                       3.0～10.0；
橡胶促进剂DM             0.5～5.0；
橡胶促进剂DETU           0.5～5.0；
炭黑N550                 10～40.0；
陶土                         5.0～20.0；
增塑剂DOS                5.0～15.0；
防护蜡               　　1.0～3.0；
防老剂A   　　　　　　　　1.0～2.0；
防老剂4010NA　　　　　　1.0～2.0。
2.如权利要求1所述的一种氯丁胶布拼接封皮用氯丁橡胶的制作方法，其特征在于：　　　
（一）按照以下重量份数比进行各组份配料：
氯丁橡胶CR 232            100.0；
ZnO                     3.0～10.0；
MgO                       3.0～10.0；
橡胶促进剂DM             0.5～5.0；
橡胶促进剂DETU           0.5～5.0；
炭黑N550                 10～40.0；
陶土                         5.0～20.0；
增塑剂DOS                5.0～15.0；
防护蜡               　　1.0～3.0；
防老剂A   　　　　　　　　1.0～2.0；
防老剂4010NA　　　　　　1.0～2.0；
（二）制作方法依次为：
１、密炼：低于110℃，密炼6分钟；
２、开炼：50至60℃，开炼8分钟；
３、下片：50至60℃，2分钟；
４、硫化胶片：151℃，40分钟；
５、按标准裁取试样；
６、性能检测。
CN201210565803.2A 2012-12-24 2012-12-24 一种氯丁胶布拼接封皮用氯丁橡胶配方及制作方法 Active CN103012889B (zh)