CN103008639B - 一种奥氏体不锈钢连铸保护浇注的方法 - Google Patents

一种奥氏体不锈钢连铸保护浇注的方法 Download PDF

Info

Publication number
CN103008639B
CN103008639B CN201110282331.5A CN201110282331A CN103008639B CN 103008639 B CN103008639 B CN 103008639B CN 201110282331 A CN201110282331 A CN 201110282331A CN 103008639 B CN103008639 B CN 103008639B
Authority
CN
China
Prior art keywords
tundish
pouring
nitrogen
continuous casting
molten steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201110282331.5A
Other languages
English (en)
Other versions
CN103008639A (zh
Inventor
范新智
刘承志
邹勇
李俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanxi Taigang Stainless Steel Co Ltd
Original Assignee
Shanxi Taigang Stainless Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanxi Taigang Stainless Steel Co Ltd filed Critical Shanxi Taigang Stainless Steel Co Ltd
Priority to CN201110282331.5A priority Critical patent/CN103008639B/zh
Publication of CN103008639A publication Critical patent/CN103008639A/zh
Application granted granted Critical
Publication of CN103008639B publication Critical patent/CN103008639B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种奥氏体不锈钢连铸保护浇注的方法，它包括下述依次的步骤：<b>Ⅰ</b>烘烤中间包:烘烤后中间包的温度不低于1050℃；<b>Ⅱ</b>开浇前的准备:将装有1510~1530℃钢水的钢包转到浇注位置，用氩气吹中间包4~7min，然后中间包开到固定位置；<b>Ⅲ</b>将钢包钢水导入中间包:在此过程中用氮气保护，从钢包下水口与长水口的接缝处吹入氮气，氮气压强为（1.5~2.0）×105Pa，由中间包液面上方的气体保护管道将氮气吹到中间包液面，氮气压强为（1.0~1.5）×105Pa；<b>Ⅳ</b>浇注:把中间包的钢水浇注成连铸钢坯，钢坯断面为160mm×1238mm，拉速为0.80±0.1m/min。本奥氏体不锈钢连铸保护浇注的方法节省贵重的氩气资源，降低不锈钢的生产成本。

Description

一种奥氏体不锈钢连铸保护浇注的方法
技术领域
本发明涉及一种奥氏体不锈钢连铸保护浇注的方法，具体讲是奥氏体不锈钢0Cr18Ni9连铸保护浇注的方法。
背景技术：
不锈钢产品对表面质量要求严格，因此在连铸生产过程中需要采取许多特殊的工艺保护措施，防止钢水氧化。从钢包长水口到中间包，钢水如果和大气接触，极易发生二次氧化恶化钢质洁净度。众所周知，连铸时从钢包下水口流出的钢流在长水口内侧形成限制射流，产生负压引起接缝吸气，吸入的空气又在长水口内与钢流形成起气─液乳化相，造成钢液的连铸过程的再氧化。另外中间包钢液面也容易和空气接触产生钢液再氧化。
为了防止再氧化，普遍采取氩气无氧化保护浇注措施，来提高钢质洁净度。由于氩气价格高（约为氮气价格的十倍），生产成本较高。生产0Cr18Ni9不锈钢，采用氩气保护浇注常有报道，但采用氮气进行保护浇注的工艺技术还未有报道。
发明内容
为了克服现有奥氏体不锈钢连铸保护浇注的方法的上述不足，本发明提供一种成本低的奥氏体不锈钢连铸保护浇注的方法。
本发明奥氏体不锈钢0Cr18Ni9的钢种特点，在连铸0Cr18Ni9不锈钢时，长水口和中间包装均采用氮气进行保护浇注。在不影响钢种质量的前
提下，节约了0Cr18Ni9不锈钢生产成本。
本奥氏体不锈钢连铸保护浇注方法所涉及的0Cr18Ni9不锈钢的化学成分的重量百分比为：
0.04%≤C≤0.08%0.20%≤Si≤1.00%1.00%≤Mn≤2.00%0≤P≤0.045%0≤S≤0.030%18.00%≤Cr≤20.00%8.00%≤Ni≤11.00%0.030%≤N≤0.080%，
其余为铁和不可避免的杂质。
本奥氏体不锈钢连铸保护浇注的方法包括下述依次的步骤：
Ⅰ烘烤中间包
烘烤后中间包的温度不低于1050℃；
Ⅱ开浇前的准备
将装有1510~1530℃钢水的钢包转到浇注位置。用氩气吹烘烤好的中间包排净中间包的空气，吹氩气时间4~7min，氩气流量20~40L/min，吹氩后中间包开到浇注位置并固定。
Ⅲ将钢水导入中间包
将钢包的钢水通过长水口导入中间包，过程中用氮气保护，具体为：在钢包下水口与长水口接缝处吹入保护气体氮气，使气体在接缝处形成气幕，以防止钢水与空气的接触。吹入氮气流量为50~80L/min，压强为（1.5~2.0）×105Pa；由中间包液面上方的气体保护的管道将氮气吹到中间包液面，氮气管道出口离液面50~100mm，氮气流量为30~60L/min，压强为（1.0~1.5）×105Pa。
Ⅳ浇注
把中间包的1490~1500℃的钢水浇注成连铸钢坯，拉速为0.80±
0.1m/min。
上述的奥氏体不锈钢连铸保护浇注方法，其特征是：钢包钢水43~45吨，中间包容量为18~20吨。
本奥氏体不锈钢连铸保护浇注方法开浇前中间包进行吹氩气，可以有效地排净中间包空气，防止中间包空气中的氧气和钢水发生发应，造成钢中夹杂物增多。开浇前中间包吹氩气比氮气有效，因为氩气密度大，可以到达中间包底部并停留，而氮气和空气密度相当，效果略差。
本发明连铸0Cr18Ni9不锈钢时，长水口到中间包装均采用氮气进行保护浇注。氮在奥氏体不锈钢中的作用除代替部分镍以节约贵重的镍元素外，主要是作为固溶强化元素提高奥氏体不锈钢的强度，但不显著损害钢的塑性和韧性；同时氮提高钢的耐腐蚀性能，特别是耐局部腐蚀，比如耐晶间腐蚀，点腐蚀和缝隙腐蚀。0Cr18Ni9不锈钢钢中氮含量为0.030%~0.080%，对0Cr18Ni9奥氏体型不锈钢来说，氮是有益元素，采用氮气保护浇注，其氮含量在控制范围之内。由于氮气比氩气密度小，因此适当增加氮气的压力与流量，能达到与氩气相同保护浇注效果。在连铸生产奥氏体不锈钢0Cr18Ni9时，中间包和长水口采用氮气保护技术，节省贵重的氩气资源，降低0Cr18Ni9不锈钢的生产成本。
具体实施方式：
下面结合实施例详细说明本奥氏体不锈钢连铸保护浇注的方法的具体实施方式，但本奥氏体不锈钢连铸保护浇注的方法的具体实施方式不局限于下述的实施例。
实施例
本奥氏体不锈钢连铸保护浇注的方法实施例为下述依次的步骤：
Ⅰ烘烤中间包
烘烤后中间包的温度为1120℃；
Ⅱ开浇前的准备
将装有下述成分与温度的钢水的钢包转到浇注位置；
C：0.06%Si：0.54%Mn：1.21%P：0.035%S：0.011%
Cr：18.34%Ni：8.22%N：0.055%，其余为铁和不可避免的杂质。
钢水温度1526℃，钢水44.5吨。
用氩气吹烘烤好的中间包排净中间包的空气，吹氩气时间5min，氩气流量30L/min，吹氩后钢包开到固定位置。
Ⅲ将钢包钢水导入中间包
将钢包里44.5吨钢水通过钢包长水口导入中间包，过程中用氮气保护，具体为：在钢包下水口与长水口接缝处吹入保护气体氮气，氮气流量为65L/min，压强为1.7×105Pa，由中间包装液面上方的气体保护的管道将氮气吹到中间包液面，氮气流量为45L/min，压强为1.2×105Pa。
Ⅳ浇注
把中间包的1492℃的20吨钢水浇注成连铸钢坯，拉速为0.85m/min，连铸成规格为160×1238mm的铸坯。

Claims (2)

1.一种奥氏体不锈钢连铸保护浇注的方法，它是0Cr18Ni9不锈钢连铸保护浇注的方法，它包括下述依次的步骤：
Ⅰ烘烤中间包
烘烤后中间包的温度不低于1050℃；
Ⅱ开浇前的准备
将装有1510~1530℃钢水的钢包转到浇注位置，用氩气吹烘烤好的中间包排净中间包的空气，吹氩气时间4~7min，氩气流量20~40L/min，吹氩后中间包开到浇注位置并固定；
Ⅲ将钢水导入中间包
将钢包的钢水通过长水口导入中间包，过程中用氮气保护，具体操作为在钢包下水口与长水口接缝处吹入保护气体氮气，使气体在接缝处形成气幕，以防止钢水与空气的接触；吹入氮气流量为50~80L/min，压强为（1.5~2.0）×105Pa；由中间包液面上方的气体保护的管道将氮气吹到中间包液面，氮气管道出口离液面50~100mm，氮气流量为30~60L/min，压强为（1.0~1.5）×105Pa；
Ⅳ浇注
把中间包的1490~1500℃的钢水浇注成连铸钢坯，拉速为0.80±0.1m/min。
2.根据权利要求1所述的奥氏体不锈钢连铸保护浇注的方法，其特征是：钢包钢水43~45吨，中间包容量为18~20吨。
CN201110282331.5A 2011-09-21 2011-09-21 一种奥氏体不锈钢连铸保护浇注的方法 Active CN103008639B (zh)