CN102993687A - 一种烧结高分子材料及其制备方法 - Google Patents

一种烧结高分子材料及其制备方法 Download PDF

Info

Publication number
CN102993687A
CN102993687A CN2012104236688A CN201210423668A CN102993687A CN 102993687 A CN102993687 A CN 102993687A CN 2012104236688 A CN2012104236688 A CN 2012104236688A CN 201210423668 A CN201210423668 A CN 201210423668A CN 102993687 A CN102993687 A CN 102993687A
Authority
CN
China
Prior art keywords
polymeric materials
parts
sintered
sintered polymeric
lubricant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012104236688A
Other languages
English (en)
Inventor
邵路
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUXI SANXINGGAO MEMBRANE TECHNOLOGY Co Ltd
Original Assignee
WUXI SANXINGGAO MEMBRANE TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUXI SANXINGGAO MEMBRANE TECHNOLOGY Co Ltd filed Critical WUXI SANXINGGAO MEMBRANE TECHNOLOGY Co Ltd
Priority to CN2012104236688A priority Critical patent/CN102993687A/zh
Publication of CN102993687A publication Critical patent/CN102993687A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种烧结高分子材料，所述烧结高分子材料的主料组成按照重量份计为：聚苯乙烯20-35份，聚碳酸酯10-22份，蜡粉8-20份，尼龙35-50份，陶瓷粉10-15份；辅料组成按照重量份计为：无机填充物0.5-2份，润滑剂0.8-1份，抗氧剂0.3-0.5份，并提供了其制备方法。本发明的有益效果为：本发明提供的烧结高分子材料，使用了多种高分子材料，烧结速度快，成型效果好，市场前景较好。

Description

一种烧结高分子材料及其制备方法
技术领域
本发明涉及工业材料成型领域，具体涉及一种烧结高分子材料及其制备方法。
背景技术
快速成型技术（RP&M），是当今世界上发展较快的材料成型技术。目前，比较成熟的工艺有：液态光敏树脂选择性固化（SLA），薄形材料选择性切割（LOM），粉末材料选择性烧结（SLS）等。与其他成型技术相比，粉末材料选择性烧结技术以选材广泛、无需设计和制造复杂支撑并可直接生产功能性零件而受到越来越广泛的重视。
发明内容
本发明的目的就是针对上述现有技术中的缺陷，提供了一种用于SLS的烧结高分子材料。
为了实现上述目的，本发明提供的技术方案为：一种烧结高分子材料，所述烧结高分子材料的主料组成按照重量份计为：
聚苯乙烯    20-35份，
聚碳酸酯    10-22份，
蜡粉        8-20份，
尼龙        35-50份，
陶瓷粉      10-15份；
辅料组成按照重量份计为：
无机填充物  0.5-2份，
润滑剂      0.8-1份，
抗氧剂      0.3-0.5份。
进一步的，上述的一种烧结高分子材料，所述烧结高分子材料的主料组成按照重量份计为：
聚苯乙烯    30份，
聚碳酸酯    18份，
蜡粉        16份，
尼龙        42份，
陶瓷粉      12份；
辅料组成按照重量份计为：
无机填充物  1份，
润滑剂      0.9份，
抗氧剂      0.4份。
进一步的，上述的一种烧结高分子材料，所述无机填充物包含有： 62-80wt%的SiO2，0-10wt%的Al2O3，20-30wt%的B2O3，0-1wt%的Na2O或K2O或二者的组合；所述润滑剂为玻璃酸钠或乙基纤维素；所述抗氧剂为硫代二丙酸双酯或亚磷酸酯。
本发明的第二个目的是提供了上述一种烧结高分子材料的制备方法，包括以下步骤：
1）将烧结高分子材料的主料按照上述的配方量进行混合，得到混合粉末；
2）将步骤1）得到的混合粉末以激光进行烧结，具体条件为，激光能量为20W，扫描速度为2500mm/s，扫描间距为0.05mm，烧结层厚为0.1mm，预热温度为60-80℃；
3）于步骤2）的激光烧结过程中，逐步加入上述配方量的辅料，加入速度为0.1份/分钟，得到烧结高分子材料。
本发明的有益效果为：本发明提供的烧结高分子材料，使用了多种高分子材料，烧结速度快，成型效果好，市场前景较好。
具体实施方式
实施例1：
一种烧结高分子材料，烧结高分子材料的主料组成按照重量份计为：聚苯乙烯20公斤，聚碳酸酯10公斤，蜡粉8公斤，尼龙35公斤，陶瓷粉10公斤；辅料组成按照重量份计为：无机填充物0.5公斤，润滑剂0.8公斤，抗氧剂0.3公斤。
无机填充物包含有：62-80wt%的SiO2，0-10wt%的Al2O3，20-30wt%的B2O3，0-1wt%的Na2O；润滑剂为玻璃酸钠；抗氧剂为硫代二丙酸双酯。
上述一种烧结高分子材料的制备方法，包括以下步骤：
1）将烧结高分子材料的主料按照上述的配方量进行混合，得到混合粉末；
2）将步骤1）得到的混合粉末以激光进行烧结，具体条件为，激光能量为20W，扫描速度为2500mm/s，扫描间距为0.05mm，烧结层厚为0.1mm，预热温度为60-80℃；
3）于步骤2）的激光烧结过程中，逐步加入上述配方量的辅料，加入速度为0.1份/分钟，得到烧结高分子材料。
实施例2：
一种烧结高分子材料，烧结高分子材料的主料组成按照重量份计为：聚苯乙烯35公斤，聚碳酸酯22公斤，蜡粉20公斤，尼龙50公斤，陶瓷粉15公斤；辅料组成按照重量份计为：无机填充物2公斤，润滑剂1公斤，抗氧剂0.5公斤。
无机填充物包含有：62-80wt%的SiO2，0-10wt%的Al2O3，20-30wt%的B2O3，0-1wt%的K2O；润滑剂为乙基纤维素；抗氧剂为亚磷酸酯。
上述一种烧结高分子材料的制备方法，包括以下步骤：
1）将烧结高分子材料的主料按照上述的配方量进行混合，得到混合粉末；
2）将步骤1）得到的混合粉末以激光进行烧结，具体条件为，激光能量为20W，扫描速度为2500mm/s，扫描间距为0.05mm，烧结层厚为0.1mm，预热温度为60-80℃；
3）于步骤2）的激光烧结过程中，逐步加入上述配方量的辅料，加入速度为0.1份/分钟，得到烧结高分子材料。
实施例3：
一种烧结高分子材料，烧结高分子材料的主料组成按照重量份计为：聚苯乙烯30公斤，聚碳酸酯18公斤，蜡粉16公斤，尼龙42公斤，陶瓷粉12公斤；辅料组成按照重量份计为：无机填充物1公斤，润滑剂0.9公斤，抗氧剂0.4公斤。
无机填充物包含有：62-80wt%的SiO2，0-10wt%的Al2O3，20-30wt%的B2O3，0-1wt%的Na2O和K2O；润滑剂为玻璃酸钠；抗氧剂为硫代二丙酸双酯。
上述一种烧结高分子材料的制备方法，包括以下步骤：
1）将烧结高分子材料的主料按照上述的配方量进行混合，得到混合粉末；
2）将步骤1）得到的混合粉末以激光进行烧结，具体条件为，激光能量为20W，扫描速度为2500mm/s，扫描间距为0.05mm，烧结层厚为0.1mm，预热温度为60-80℃；
3）于步骤2）的激光烧结过程中，逐步加入上述配方量的辅料，加入速度为0.1份/分钟，得到烧结高分子材料。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (4)

1.一种烧结高分子材料，其特征在于，所述烧结高分子材料的主料组成按照重量份计为：
聚苯乙烯    20-35份，
聚碳酸酯    10-22份，
蜡粉        8-20份，
尼龙        35-50份，
陶瓷粉      10-15份；
辅料组成按照重量份计为：
无机填充物  0.5-2份，
润滑剂      0.8-1份，
抗氧剂      0.3-0.5份。
2.根据权利要求1所述的一种烧结高分子材料，其特征在于，所述烧结高分子材料的主料组成按照重量份计为：
聚苯乙烯    30份，
聚碳酸酯    18份，
蜡粉        16份，
尼龙        42份，
陶瓷粉      12份；
辅料组成按照重量份计为：
无机填充物  1份，
润滑剂      0.9份，
抗氧剂      0.4份。
3.根据权利要求1或2所述的一种烧结高分子材料，其特征在于，所述无机填充物包含有： 62-80wt%的SiO2，0-10wt%的Al2O3，20-30wt%的B2O3，0-1wt%的Na2O或K2O或二者的组合；所述润滑剂为玻璃酸钠或乙基纤维素；所述抗氧剂为硫代二丙酸双酯或亚磷酸酯。
4.一种烧结高分子材料的制备方法，其特征在于，包括以下步骤：
1）将烧结高分子材料的主料按照权利要求1-3任一所述的配方量进行混合，得到混合粉末；
2）将步骤1）得到的混合粉末以激光进行烧结，具体条件为，激光能量为20W，扫描速度为2500mm/s，扫描间距为0.05mm，烧结层厚为0.1mm，预热温度为60-80℃；
3）于步骤2）的激光烧结过程中，逐步加入权利要求1-3任一所述配方量的辅料，加入速度为0.1份/分钟，得到烧结高分子材料。
CN2012104236688A 2012-10-30 2012-10-30 一种烧结高分子材料及其制备方法 Pending CN102993687A (zh)