CN102990745A - 一种木材防腐剂的制备方法 - Google Patents
一种木材防腐剂的制备方法 Download PDFInfo
- Publication number
- CN102990745A CN102990745A CN201210392702XA CN201210392702A CN102990745A CN 102990745 A CN102990745 A CN 102990745A CN 201210392702X A CN201210392702X A CN 201210392702XA CN 201210392702 A CN201210392702 A CN 201210392702A CN 102990745 A CN102990745 A CN 102990745A
- Authority
- CN
- China
- Prior art keywords
- weight percent
- deionized water
- preparation
- timber
- preservative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种木材防腐剂的制备方法，包括以下步骤：（1）将4-16％双十烷基二甲基氯化铵、3.6-5.8％八硼酸二钠、1-3％丙环唑、和适量去离子水混合，将该混合物加热至100-110℃，不断搅拌直至固体完全溶解；（2）冷却至室温后加入20-30％氧化铜和1-3％氨水，最后加入去离子水使总重量百分比为100％；（3）搅拌直到所有组分完全溶解。本发明制得防腐剂不含砷、铬等物质、毒性低、具有良好的防腐、防虫效果。
Description
技术领域
本发明涉及一种木材防腐剂的制备方法。
背景技术
木材是国家建设和人们日常生活用品的重要原料之一，例如用于建筑材料、工业材料等。随着人们生活水平的提高，对木材的需求量也日益增加。木材是一种天然有机材料，具有明显的生物特性，易被菌、虫、海生钻孔虫等生物侵袭。所以木材的长期使用特别是长期户外使用受到很大的限制。腐败生物会引起木材的腐烂，使其受到破坏。在使用前，根据不同的应用环境，选用合适的防腐剂，进行恰当的处理，则可以有效地延缓木材腐朽。我国可采伐使用的森林资源十分有限，寄希望于使用大量外汇进口木材是不现实的。对木材进行防腐处理，延长木制品的使用年限，是节约木材、保护森林资源的重要途径之一。目前世界各国使用的木材防腐剂主要是CCA防腐剂，该类防腐剂由于含有砷、铬等物质而具有毒性，不利于环境保护，在一些国家已严格限制使用。
发明内容
本发明的目的是提供一种低毒、防腐效果好的木材防腐剂的制备方法。
本发明的木材防腐剂由以下重量百分比的组分组成：
余量为去离子水。
其中氧化铜对真菌具有较好的抑制作用，价格适中，对环境友好，并且对人、畜无害。丙环唑具有防霉作用。氨水可增加氧化铜的溶解性。双十烷基二甲基氯化铵具有杀菌效果，还可提高制剂的稳定性，防止丙环唑的沉淀。八硼酸二钠是优良的防腐剂，渗透性好并且具有防虫功能。本发明的木材防腐剂不会对环境造成污染，使用安全，并且具有明显的防腐和防虫效果。
上述防腐剂的制备方法，包括以下步骤：
（1）将4-16％双十烷基二甲基氯化铵、3.6-5.8％八硼酸二钠、1-3％丙环唑、和适量去离子水混合，将该混合物加热至100-110℃，不断搅拌直至固体完全溶解；
（2）冷却至室温后加入20-30％氧化铜和1-3％氨水，最后加入去离子水使总重量百分比为100％；
（3）搅拌直到所有组分完全溶解。
具体实施方式
下面结合实施例对本发明作进一步详细描述。但是本发明不限于所给出的例子。
实施例1
本实施例的木材防腐剂由以下重量百分比的组分组成：
余量为去离子水。
本实施例木材防腐剂的制备方法，包括以下步骤：
（1）将4％双十烷基二甲基氯化铵、3.6％八硼酸二钠、1％丙环唑和适量去离子水混合，将该混合物加热至100-110℃，不断搅拌直至固体完全溶解；
（2）冷却至室温后加入20％氧化铜和1氨水，最后加入去离子水使总重量百分比为100％；
（3）搅拌直到所有组分完全溶解。
实施例2
本实施例的木材防腐剂由以下重量百分比的组分组成：
余量为去离子水。
本实施例木材防腐剂的制备方法，包括以下步骤：
（1）将8％双十烷基二甲基氯化铵、4.4％八硼酸二钠、1.3％丙环唑和适量去离子水混合，将该混合物加热至100-110℃，不断搅拌直至固体完全溶解；
（2）冷却至室温后加入24％氧化铜和1.3％氨水，最后加入去离子水使总重量百分比为100％；
（3）搅拌直到所有组分完全溶解。
实施例3
本实施例的木材防腐剂由以下重量百分比的组分组成
余量为去离子水。
本实施例木材防腐剂的制备方法，包括以下步骤：
（1）将11.5％双十烷基二甲基氯化铵、5.1％八硼酸二钠、2.3％丙环唑和适量去离子水混合，将该混合物加热至100-110℃，不断搅拌直至固体完全溶解；
（2）冷却至室温后加入26％氧化铜和2.4％氨水，最后加入去离子水使总重量百分比为100％；
（3）搅拌直到所有组分完全溶解。
实施例4
本实施例的木材防腐剂由以下重量百分比的组分组成
余量为去离子水。
本实施例木材防腐剂的制备方法，包括以下步骤：
（1）将16％双十烷基二甲基氯化铵、5.8％八硼酸二钠、3％丙环唑和适量去离子水混合，将该混合物加热至100-110℃，不断搅拌直至固体完全溶解；
（2）冷却至室温后加入30％氧化铜和3氨水，最后加入.去离子水使总重量百分比为100％；
（3）搅拌直到所有组分完全溶解。
使用本发明的木材防腐剂处理木材及木制品的方法包括以下步骤：
（1）将木材置于密闭的压力浸注罐中，加入本发明的木材防腐剂至满罐；
（2）加压至0.8Mpa±0.05Mpa，保持约1-10小时；
（3）泄压并排空防腐剂；
（4）从罐中取出木材。
用本发明防腐剂处理的防腐木材，经检测其顺纹抗压强度大于41Mpa，抗弯强度大于61Mpa，使用寿命在25年以上。
Claims (1)
1.一种木材防腐剂的制备方法，包括以下步骤：
（1）将4-16％双十烷基二甲基氯化铵、3.6-5.8％八硼酸二钠、1-3％丙环唑、和适量去离子水混合，将该混合物加热至100-110℃，不断搅拌直至固体完全溶解；
（2）冷却至室温后加入20-30％氧化铜和1-3％氨水，最后加入去离子水使总重量百分比为100％；
（3）搅拌直到所有组分完全溶解。