CN102978953A - 一种防水棉织物的制造方法 - Google Patents
一种防水棉织物的制造方法 Download PDFInfo
- Publication number
- CN102978953A CN102978953A CN2012104984068A CN201210498406A CN102978953A CN 102978953 A CN102978953 A CN 102978953A CN 2012104984068 A CN2012104984068 A CN 2012104984068A CN 201210498406 A CN201210498406 A CN 201210498406A CN 102978953 A CN102978953 A CN 102978953A
- Authority
- CN
- China
- Prior art keywords
- cotton fabric
- fabric
- preparation
- mixed emulsion
- manufacture method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防水棉织物的制造方法，包括步骤为：将氨基硅油和活性聚醚加入到溶剂中并搅拌加热反应，至溶液透明再保温3-4小时，反应结束后再加入醋酸调节pH值得到混合乳液；将混合乳液用水和助剂进行稀释得到浸轧液，采用一浸一轧方式整理棉织物，再进行烘焙并烘干得到具有防水功能的棉织物。通过上述方式，本发明提供的一种防水棉织物的制造方法，制得的棉织物具有很好的防水性能，在整理和后续工序中高温加热棉织物的颜色不会发生变化，制成衣服后人穿着清爽且舒适，清洗也不会破坏织物的防水性能，该制造方法操作简单，能有效提高织物的品质。
Description
技术领域
本发明涉及纺织面料领域，特别是涉及一种防水棉织物的制造方法。
背景技术
随着人们生活水平的不断提高和纺织工业技术的向前发展，只具有单一功能的纺织织物已经不能满足市场的需求，多功能复合后进行整理的织物已越来越受到人们的欢迎。二甲基聚硅氧烷结构与织物的纤维结合能赋予织物优良的爽滑、柔软和弹性，同时氨基能够增加二甲基聚硅氧烷在织物上的有序排列，使织物的功能性进一步提高。
虽然传统的氨基硅油相对于普通的硅油具有一定的优异性，并逐渐取代普通硅油广泛应用于织物上，但应用氨基硅油的织物穿着后感到闷热，清洗也会破坏织物的防水性能，特别是在制造过程中整理和后续工序中高温加热会使织物的颜色发生变化，不能保证织物的品质。
发明内容
本发明主要解决的技术问题是提供一种防水棉织物的制造方法，该棉织物具有防水、穿着舒适的效果。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种防水棉织物的制造方法，包括步骤为：
（1）将氨基硅油和活性聚醚加入到溶剂中并搅拌加热反应，至溶液透明再保温3-4小时，反应结束后再加入醋酸调节pH值得到混合乳液；
（2）将混合乳液用水和助剂进行稀释得到浸轧液，采用一浸一轧方式整理棉织物，再进行烘焙并烘干得到具有防水功能的棉织物。
在本发明一个较佳实施例中，步骤（1）中所述溶剂包括乙醇、丙醇或异丙醇。
在本发明一个较佳实施例中，步骤（1）中所述加热温度为80-90℃。
在本发明一个较佳实施例中，步骤（1）中所述混合乳液的pH值为5.5-6。
本发明的有益效果是：本发明的防水棉织物的制造方法，制得的棉织物具有很好的防水性能，在整理和后续工序中高温加热棉织物的颜色不会发生变化，制成衣服后人穿着清爽且舒适，清洗也不会破坏织物的防水性能，该制造方法操作简单，能有效提高织物的品质。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
实施例一：
（1）将氨基硅油和活性聚醚加入到乙醇溶剂中并搅拌加热反应，反应温度设定为80℃，至溶液透明再保温3小时，反应结束后再加入醋酸调节pH值为6，得到混合乳液；
（2）将混合乳液用水和助剂进行稀释得到浸轧液，采用一浸一轧方式整理棉织物，再进行烘焙并烘干得到具有防水功能的棉织物。
实施例二：
（1）将氨基硅油和活性聚醚加入到丙醇溶剂中并搅拌加热反应，反应温度设定为90℃，至溶液透明再保温3小时，反应结束后再加入醋酸调节pH值为5.5，得到混合乳液；
（2）将混合乳液用水和助剂进行稀释得到浸轧液，采用一浸一轧方式整理棉织物，再进行烘焙并烘干得到具有防水功能的棉织物。
实施例三：
（1）将氨基硅油和活性聚醚加入到异丙醇溶剂中并搅拌加热反应，反应温度设定为90℃，至溶液透明再保温4小时，反应结束后再加入醋酸调节pH值为6，得到混合乳液；
（2）将混合乳液用水和助剂进行稀释得到浸轧液，采用一浸一轧方式整理棉织物，再进行烘焙并烘干得到具有防水功能的棉织物。
本发明揭示的防水棉织物的制造方法，制得的棉织物具有很好的防水性能，在整理和后续工序中高温加热棉织物的颜色不会发生变化，制成衣服后人穿着清爽且舒适，清洗也不会破坏织物的防水性能，该制造方法操作简单，能有效提高织物的品质。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (4)
1.一种防水棉织物的制造方法，其特征在于，包括步骤为：
（1）将氨基硅油和活性聚醚加入到溶剂中并搅拌加热反应，至溶液透明再保温3-4小时，反应结束后再加入醋酸调节pH值得到混合乳液；
（2）将混合乳液用水和助剂进行稀释得到浸轧液，采用一浸一轧方式整理棉织物，再进行烘焙并烘干得到具有防水功能的棉织物。
2.根据权利要求1所述的防水棉织物的制造方法，其特征在于，步骤（1）中所述溶剂包括乙醇、丙醇或异丙醇。
3.根据权利要求1所述的防水棉织物的制造方法，其特征在于，步骤（1）中所述加热温度为80-90℃。
4.根据权利要求1所述的防水棉织物的制造方法，其特征在于，步骤（1）中所述混合乳液的pH值为5.5-6。