CN102978340A - 一种炼钢脱氧剂及其制备方法 - Google Patents

一种炼钢脱氧剂及其制备方法 Download PDF

Info

Publication number
CN102978340A
CN102978340A CN2012105074892A CN201210507489A CN102978340A CN 102978340 A CN102978340 A CN 102978340A CN 2012105074892 A CN2012105074892 A CN 2012105074892A CN 201210507489 A CN201210507489 A CN 201210507489A CN 102978340 A CN102978340 A CN 102978340A
Authority
CN
China
Prior art keywords
magnesium
preparation
steel making
aluminium
vacuum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012105074892A
Other languages
English (en)
Inventor
张桂芬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2012105074892A priority Critical patent/CN102978340A/zh
Publication of CN102978340A publication Critical patent/CN102978340A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种炼钢脱氧剂及制备方法，其组成按重量百分比为，25-35％的镁、35-45％的铝，余量为铁。通过粉末冶金技术，克服了镁相对于铁溶解度低的问题，并减少了镁的浇损量，提高了合金中镁的含量，减少脱氧剂的添加量，减少生产成本。

Description

一种炼钢脱氧剂及其制备方法
技术领域
本发明属于金属材料领域，特别是指一种炼钢脱氧剂及其制备方法。
背景技术
现在炼钢过程中，一般使用的是纯铝脱氧剂，这是利用纯铝和氧亲合力强、脱氧效率高而得到广泛应用，但是纯铝脱氧也有一些缺陷，就是铝的熔点低、密度小，在钢液中上浮，而且脱氧产生的三氧化二铝可塑性差且熔点高，存在于钢中会引起钢的热蠕变脆性，降低钢的高温强度。
现脱氧剂中也使用镁做脱氧剂，因为镁的性质活泼，更利于氧的结合，是最理想的脱氧剂，但镁的密度小，并且镁的沸点低、溶解度低，很难溶解到钢液中。
现技术已经使用由铝和镁配合并制成铝镁铁合金来做为脱氧剂，但是采用普通的炼制方法，因镁相对于铁的低溶解度，因此在炼制时导致镁的烧损过多，制得的镁铝合金的收率低而导致成本高。
发明内容
本发明的目的是提供一种炼钢脱氧剂及其制备方法，通过本技术方案，能够克服现技术生产炼钢脱氧剂的镁损耗大、成本高的问题。
一种炼钢脱氧剂及其制备方法，其组成按重量百分比为，25-35％的镁、35-45％的铝，余量为铁。
所述制备方法为：
配料，按重量百分比为，25-35％的镁、35-45％的铝，余量为铁进行计算配料；
混料，将上述各组成分别通过磨制机械成粉末，各粉末的平均粒径为20-60微米；将上述粉末在混料机内进行混料30-60分钟；
压制，在模具内通过350-500MPa压力压制10-60秒成坯体；
烧制，将制得的坯体在炉内在650-700℃下烧结1-3小时，然后冷却至室温得到合金。
所述在烧制过程中，炉内保持真空条件或真空氮气氛围下进行烧制。
所述真空真空氮气氛围的真空度为500-3000Pa。
本发明同现有技术相比的有益效果是：
通过粉末冶金技术，克服了镁相对于铁溶解度低的问题，并减少了镁的浇损量，提高了合金中镁的含量，减少脱氧剂的添加量，减少生产成本。
具体实施方式
以下通过实施例来详细说明本发明的技术方案，应当理解的是，以下的实施例仅能用来解释本发明而不能解释为是对本发明的限制。
一种炼钢脱氧剂及其制备方法，其组成按重量百分比为，25-35％的镁、35-45％的铝，余量为铁。
所述制备方法为：
配料，按重量百分比为，25-35％的镁、35-45％的铝，余量为铁进行计算配料；
混料，将上述各组成分别通过磨制机械成粉末，各粉末的平均粒径为20-60微米；将上述粉末在混料机内进行混料30-60分钟；
压制，在模具内通过350-500MPa压力压制10-60秒成坯体；
烧制，将制得的坯体在炉内在保持真空条件或真空氮气氛围为500-3000Pa炉温为650-700℃下烧结1-3小时，然后冷却至室温得到合金。
实施例1
所述制备方法为：
配料，按重量百分比为，25％的镁、35％的铝，余量为铁进行计算配料；
混料，将上述各组成分别通过磨制机械成粉末，各粉末的平均粒径为20-60微米；将上述粉末在混料机内进行混料30分钟；
压制，在模具内通过350MPa压力压制30秒成坯体；
烧制，将制得的坯体在炉内在保持真空条件或真空氮气氛围为500Pa炉温为650-700℃下烧结1小时，然后冷却至室温得到合金。
实施例2
所述制备方法为：
配料，按重量百分比为，35％的镁、45％的铝，余量为铁进行计算配料；
混料，将上述各组成分别通过磨制机械成粉末，各粉末的平均粒径为20-60微米；将上述粉末在混料机内进行混料60分钟；
压制，在模具内通过350-500MPa压力压制60秒成坯体；
烧制，将制得的坯体在炉内在保持真空条件或真空氮气氛围为3000Pa炉温为650-700℃下烧结3小时，然后冷却至室温得到合金。
实施例3
所述制备方法为：
配料，按重量百分比为，30％的镁、40％的铝，余量为铁进行计算配料；
混料，将上述各组成分别通过磨制机械成粉末，各粉末的平均粒径为20-60微米；将上述粉末在混料机内进行混料45分钟；
压制，在模具内通过400MPa压力压制45秒成坯体；
烧制，将制得的坯体在炉内在保持真空条件或真空氮气氛围为1500Pa炉温为650-700℃下烧结2小时，然后冷却至室温得到合金。

Claims (4)

1.一种炼钢脱氧剂，其特征在于：其组成按重量百分比为，25-35％的镁、35-45％的铝，余量为铁。
2.一种炼钢脱氧剂制备方法，其特征在于：
配料，按重量百分比为，25-35％的镁、35-45％的铝，余量为铁进行计算配料；
混料，将上述各组成分别通过磨制机械成粉末，各粉末的平均粒径为20-60微米；将上述粉末在混料机内进行混料30-60分钟；
压制，在模具内通过350-500MPa压力压制10-60秒成坯体；
烧制，将制得的坯体在炉内在650-700℃下烧结1-3小时，然后冷却至室温得到合金。
3.根据权利要求2所述的炼钢脱氧剂制备方法，其特征在于：所述在烧制过程中，炉内保持真空条件或真空氮气氛围下进行烧制。
4.根据权利要求3所述的炼钢脱氧剂制备方法，其特征在于：所述真空真空氮气氛围的真空度为500-3000Pa。
CN2012105074892A 2012-11-26 2012-11-26 一种炼钢脱氧剂及其制备方法 Pending CN102978340A (zh)