CN102978329B - 一种转炉用复合造渣剂 - Google Patents

一种转炉用复合造渣剂 Download PDF

Info

Publication number
CN102978329B
CN102978329B CN201210426467.3A CN201210426467A CN102978329B CN 102978329 B CN102978329 B CN 102978329B CN 201210426467 A CN201210426467 A CN 201210426467A CN 102978329 B CN102978329 B CN 102978329B
Authority
CN
China
Prior art keywords
parts
slag
chromium slag
calcium
converter
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210426467.3A
Other languages
English (en)
Other versions
CN102978329A (zh
Inventor
王海军
王存邦
吴雪健
高金菊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201210426467.3A priority Critical patent/CN102978329B/zh
Publication of CN102978329A publication Critical patent/CN102978329A/zh
Application granted granted Critical
Publication of CN102978329B publication Critical patent/CN102978329B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种转炉用复合造渣剂，属于转炉炼钢工艺中的造渣剂技术领域。本发明的一种转炉用复合造渣剂，其各组分按质量份组成如下：无钙铬渣68～73份、白刚玉12～15份和石灰石20～23份。本发明的一种转炉用复合造渣剂，不含CaF2，避免了含氟气体与氟离子对大气与水资源的污染，且综合利用了难以回收利用的无钙铬渣这一废弃物作为主要原料，大大降低了造渣剂的生产成本，无钙铬渣中的Cr、Fe等元素得以综合利用；本发明的一种转炉用复合造渣剂，成渣时间短，成渣时间减少30%左右，生产效率高，钢铁料消耗降低3Kg/t以上，造渣料消耗降低，经济效益明显。

Description

一种转炉用复合造渣剂
技术领域
本发明涉及转炉炼钢工艺中的造渣剂技术领域，更具体地说，涉及一种转炉用复合造渣剂。
背景技术
造渣是炼钢炼铁工艺中必不可少的一环。炼钢和炼铁要使得钢中的杂质降低，这些杂质被分离出来后进入熔渣，因为熔渣比重轻，飘浮在钢水上面，就比较容易除去。另外熔渣还可以保护钢水不和大气直接接触。造渣就是在炼钢过程中加入称为造渣剂的炼钢物质，比如氟化钙或氧化钙等，以便形成炉渣。
由此可见，转炉造渣是转炉冶炼的关键操作，而快速化渣是转炉造渣的核心内容。采用造渣剂是促进转炉快速化渣的重要措施。早年使用的造渣剂中含有CaF2，其缺陷是CaF2与炉渣中SiO2反应生成SiF4，随炉气进入大气中，污染了空气，氟离子溶于水中，污染水源。
现有技术中的造渣剂，对现有冶金领域的废弃物利用不充分。中国专利申请号 201010266582X，申请日 2010年8月25日，发明创造名称为：转炉炼钢无氟复合造渣剂，该申请案涉及一种转炉炼钢无氟复合造渣剂，按重量百分比（%）由下列组分组成：A12O3 25~45，Fe2O3 15~35，B2O3 3~l0，MgO 5~15，CaO 3~15，其余为杂质和粘结剂。该申请案由工业原料 ：铁矾土粉、铁精矿粉、含硼矿粉、白云石粉按上述规定的组分（重量百分比）配制，加入粘结剂，经混匀-制粒-烘干-冷却-装袋，呈颗粒状球团，粒径直径为30~60mm。该申请案中的造渣剂虽然是无氟，但是其化渣速度有待改善，且其制造成本大，没有将冶金废弃物资源化利用。
无钙铬渣是利用当前最先进的无钙焙烧工艺技术生产铬盐过程中排放的一种工业废渣，无钙铬渣既是有害废渣，又是可利用的二次资源，其无害化处理和综合利用技术的开发已迫在眉睫。
发明内容
1.发明要解决的技术问题
本发明的目的在于克服现有技术中的不足，提供一种转炉用复合造渣剂，采用本发明的造渣剂，能够综合利用无钙铬渣，生产成本低，且造渣剂的化渣速度较快。
2.技术方案
为达到上述目的，本发明提供的技术方案为：
本发明的一种转炉用复合造渣剂，其各组分按质量份组成如下：
无钙铬渣         68~73份
白刚玉           12~15份
石灰石           20~23份。
优选地，其各组分按质量份组成如下：
无钙铬渣         71份
白刚玉           13份
石灰石           21份。
3.有益效果
采用本发明提供的技术方案，与已有的公知技术相比，具有如下显著效果：
（1）本发明的一种转炉用复合造渣剂，不含CaF2，避免了含氟气体与氟离子对大气与水资源的污染，且综合利用了难以回收利用的无钙铬渣这一废弃物作为主要原料，大大降低了造渣剂的生产成本，无钙铬渣中的Cr、Fe等元素得以综合利用；
（2）本发明的一种转炉用复合造渣剂，成渣时间短，成渣时间减少30%左右，生产效率高，钢铁料消耗降低 3Kg/t 以上，造渣料消耗降低，经济效益明显。
具体实施方式
为进一步了解本发明的内容，下面结合实施例对本发明作进一步的描述。
实施例1
本实施例的一种转炉用复合造渣剂，其各组分按质量份组成如下：无钙铬渣68份，白刚玉15份，石灰石20份。
本实施例的一种转炉用复合造渣剂的制备方法，其具体步骤为：
（1）按质量比称取无钙铬渣68份、白刚玉15份、石灰石20份，并将上述的无钙铬渣、白刚玉和石灰石在150℃的温度下进行分别烘烤，烘烤时间均为1.0小时；
（2）将步骤（1）烘烤后的无钙铬渣、白刚玉、石灰石进行搅拌混合；
（3）在1500℃温度下对步骤（2）的混合料进行预熔，预熔2小时；
（4）将步骤（3）预熔后的混合料冷却后，破碎成粒度为1~5cm的颗粒，即得转炉用复合造渣剂。
本实施例的转炉用复合造渣剂，加入量为8kg/t，成渣时间为13分钟，生产成本为造渣剂的60%左右。
实施例2
本实施例的一种转炉用复合造渣剂，其各组分按质量份组成如下：无钙铬渣73份，白刚玉12份，石灰石23份。
本实施例的一种转炉用复合造渣剂的制备方法，其具体步骤为：
（1）按质量比称取无钙铬渣73份、白刚玉12份、石灰石23份，并将上述的无钙铬渣、白刚玉和石灰石在110℃的温度下进行分别烘烤，烘烤时间均为1.0小时；
（2）将步骤（1）烘烤后的无钙铬渣、白刚玉、石灰石进行搅拌混合；
（3）在1700℃温度下对步骤（2）的混合料进行预熔，预熔1小时；
（4）将步骤（3）预熔后的混合料冷却后，破碎成粒度为1~5cm的颗粒，即得转炉用复合造渣剂。
本实施例的转炉用复合造渣剂，加入量为9kg/t，成渣时间为12分钟，生产成本为造渣剂的60%左右。
实施例3
本实施例的一种转炉用复合造渣剂，其各组分按质量份组成如下：无钙铬渣71份，白刚玉13份，石灰石21份。
本实施例的一种转炉用复合造渣剂的制备方法，其具体步骤为：
（1）按质量比称取无钙铬渣71份、白刚玉13份、石灰石21份，并将上述的无钙铬渣、白刚玉和石灰石在140℃的温度下进行分别烘烤，烘烤时间均为1.0小时；
（2）将步骤（1）烘烤后的无钙铬渣、白刚玉、石灰石进行搅拌混合；
（3）在1600℃温度下对步骤（2）的混合料进行预熔，预熔1.5小时；
（4）将步骤（3）预熔后的混合料冷却后，破碎成粒度为1~5cm的颗粒，即得转炉用复合造渣剂。
本实施例的转炉用复合造渣剂，加入量为12kg/t，成渣时间为14分钟，生产成本为造渣剂的60%左右。

Claims (2)

1.一种转炉用复合造渣剂，其特征在于，其各组分按质量份组成如下：
无钙铬渣  68～73份
白刚玉    12～15份
石灰石    20～23份；其制备方法为：在1500℃、1600℃或1700℃温度下对无钙铬渣68～73份、白刚玉12～15份、石灰石20～23份的混合料进行预熔，预熔2小时、1.5小时或1小时。
2.根据权利要求1所述的一种转炉用复合造渣剂，其特征在于，其各组分按质量份组成如下：
无钙铬渣  71份
白刚玉    13份
石灰石    21份。
CN201210426467.3A 2012-10-31 2012-10-31 一种转炉用复合造渣剂 Expired - Fee Related CN102978329B (zh)