CN102977800A - Insulating glue of textile machine and preparation method thereof - Google Patents
Insulating glue of textile machine and preparation method thereof Download PDFInfo
- Publication number
- CN102977800A CN102977800A CN 201210473709 CN201210473709A CN102977800A CN 102977800 A CN102977800 A CN 102977800A CN 201210473709 CN201210473709 CN 201210473709 CN 201210473709 A CN201210473709 A CN 201210473709A CN 102977800 A CN102977800 A CN 102977800A
- Authority
- CN
- China
- Prior art keywords
- parts
- acetone
- barium sulfate
- textile machinery
- resins
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses insulating glue of a textile machine and a preparation method thereof. The insulating glue is formed by the following components in parts by weight: 10-20 parts of vinyl chloride resin, 6-8 parts of epoxy resin, 3-5 parts of polysulfone, 1-3 parts of zinc sulfide, 2-6 parts of barium sulfate, 3-5 parts of dimethyl formamide, 40-60 parts of acetone, 3-6 parts of maleic anhydride and 5-8 parts of vinylidene chloride. Compared with the prior art, the insulating glue has the following beneficial effects: (1) the insulating glue is acid-proof and alkali-proof and can be cured at a room temperature; the curing time is short and a coating is thick; the insulating strippable property is good; the utilization is convenient; and (2) the preparation process is simple and the cost is low.
Description
Technical field
The invention belongs to the adhesive technology field, more specifically relate to a kind of textile machinery insulation paste and preparation method thereof.
Background technology
Textile manufacturing machine commonly used is normally switched on and is driven at present; because machinery equipment is made of metal; the good conductor that belongs to electricity; and machine itself may be connected with many electric wires; therefore, if textile machinery is not carried out insulation processing, can bring larger potential safety hazard; therefore, usually at textile machinery surface-coated one deck insulation paste to carry out insulation protection.
Polycomponent composite gum with good electrical insulating property.Take natural resin or synthetic resins as material of main part, have very high viscosity under the normal temperature, heat to improve flowability during use, make it to be convenient to perfusion, dipping, apply.Can solidify after the cooling, also can not solidify.Be characterized in not containing volatile solvent, can be used as the machine surface protection.
Summary of the invention
The object of the invention is to overcome the deficiency that prior art exists, a kind of textile machinery insulation paste is provided.
Another object of the present invention provides the preparation method of this textile machinery insulation paste.
For achieving the above object, the present invention has taked following technical scheme:
A kind of textile machinery insulation paste, in weight part, composed of the following components:
Supervinyi chloride resin: 10～20, Resins, epoxy: 6～8, polysulfones: 3～5,
Zinc sulphide: 1～3, barium sulfate: 2～6, dimethyl formamide: 3～5,
Acetone: 40～60, MALEIC ANHYDRIDE: 3～6, chlorinated polyvinyl chloride: 5～8.
The preparation method of described a kind of textile machinery insulation paste comprises the steps:
(1) by proportioning, supervinyi chloride resin and Resins, epoxy are placed container, add acetone and make its dissolving;
(2) zinc sulphide and barium sulfate are ground to form finely powdered, add in the product of step (1), mix;
(3) product with step (2) adds in the product of step (1), stirs;
(4) add all the other components, get final product to get finished product after the mixing and stirring.
Compared with prior art, the present invention has following beneficial effect:
(1) have acid and alkali-resistance, self-vulcanizing, set time is short, thick coating, the insulation strippability is good; The characteristics such as easy to use.
(2) preparation technology is easy, and is with low cost.
Embodiment
The invention will be further described below in conjunction with specific embodiment.
Embodiment 1
A kind of textile machinery insulation paste, in weight part, composed of the following components:
Supervinyi chloride resin: 10, Resins, epoxy: 6, polysulfones: 3,
Zinc sulphide: 1, barium sulfate: 2, dimethyl formamide: 3,
Acetone: 40, MALEIC ANHYDRIDE: 3, chlorinated polyvinyl chloride: 5.
Embodiment 2
A kind of textile machinery insulation paste, in weight part, composed of the following components:
Supervinyi chloride resin: 20, Resins, epoxy: 8, polysulfones: 5,
Zinc sulphide: 3, barium sulfate: 6, dimethyl formamide: 5,
Acetone: 60, MALEIC ANHYDRIDE: 6, chlorinated polyvinyl chloride: 8.
Embodiment 3
A kind of textile machinery insulation paste, in weight part, composed of the following components:
Supervinyi chloride resin: 16, Resins, epoxy: 7, polysulfones: 4,
Zinc sulphide: 2, barium sulfate: 4, dimethyl formamide: 4,
Acetone: 50, MALEIC ANHYDRIDE: 5, chlorinated polyvinyl chloride: 6.
The preparation method of described a kind of textile machinery insulation paste comprises the steps:
(1) by proportioning, supervinyi chloride resin and Resins, epoxy are placed container, add acetone and make its dissolving;
(2) zinc sulphide and barium sulfate are ground to form finely powdered, add in the product of step (1), mix;
(3) product with step (2) adds in the product of step (1), stirs;
(4) add all the other components, get final product to get finished product after the mixing and stirring.
Claims (5)
1. a textile machinery insulation paste is characterized in that, and is in weight part, composed of the following components:
Supervinyi chloride resin: 10～20, Resins, epoxy: 6～8, polysulfones: 3～5,
Zinc sulphide: 1～3, barium sulfate: 2～6, dimethyl formamide: 3～5,
Acetone: 40～60, MALEIC ANHYDRIDE: 3～6, chlorinated polyvinyl chloride: 5～8.
2. a kind of textile machinery insulation paste according to claim 1 is characterized in that, and is in weight part, composed of the following components:
Supervinyi chloride resin: 10, Resins, epoxy: 6, polysulfones: 3,
Zinc sulphide: 1, barium sulfate: 2, dimethyl formamide: 3,
Acetone: 40, MALEIC ANHYDRIDE: 3, chlorinated polyvinyl chloride: 5.
3. a kind of textile machinery insulation paste according to claim 1 is characterized in that, and is in weight part, composed of the following components:
Supervinyi chloride resin: 20, Resins, epoxy: 8, polysulfones: 5,
Zinc sulphide: 3, barium sulfate: 6, dimethyl formamide: 5,
Acetone: 60, MALEIC ANHYDRIDE: 6, chlorinated polyvinyl chloride: 8.
4. a kind of textile machinery insulation paste according to claim 1 is characterized in that, and is in weight part, composed of the following components:
Supervinyi chloride resin: 16, Resins, epoxy: 7, polysulfones: 4,
Zinc sulphide: 2, barium sulfate: 4, dimethyl formamide: 4,
Acetone: 50, MALEIC ANHYDRIDE: 5, chlorinated polyvinyl chloride: 6.
5. the preparation method of a kind of textile machinery insulation paste claimed in claim 1 is characterized in that, comprises the steps:
(1) by proportioning, supervinyi chloride resin and Resins, epoxy are placed container, add acetone and make its dissolving;
(2) zinc sulphide and barium sulfate are ground to form finely powdered, add in the product of step (1), mix;
(3) product with step (2) adds in the product of step (1), stirs;
(4) add all the other components, get final product to get finished product after the mixing and stirring.