CN106380725A - Flame retardation material for motor wire - Google Patents
Flame retardation material for motor wire Download PDFInfo
- Publication number
- CN106380725A CN106380725A CN201610763683.5A CN201610763683A CN106380725A CN 106380725 A CN106380725 A CN 106380725A CN 201610763683 A CN201610763683 A CN 201610763683A CN 106380725 A CN106380725 A CN 106380725A
- Authority
- CN
- China
- Prior art keywords
- parts
- flame retardation
- retardation material
- motor
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a flame retardation material for a motor wire. The flame retardation material comprises, by weight, 100 parts of PVC resin powder, 43 parts of trioctyl trimellitate, 6 parts of epoxy soybean oil, 30 parts of light active nanometer calcium carbonate, 6 parts of an eco-friendly calcium-zinc composite stabilizing agent, 0.8 parts of polyethylene wax, 5 parts of silicone master batches, 10 parts of chlorinated polyethylene, 4 parts of antimony oxide, 4 parts of phosphorus benzene flame retardation oil and 0.5-3 parts of a pigment. The flame retardation material has scratch resistance and insulating varnish corrosion resistance and is a good choice of a motor private wire.
Description
Technical field:
The present invention relates to a kind of cable material, it is especially a kind of motor lines flame-proof material.
Background technology:
It is that electrical machinery plant produces and scraps the main of motor and want one of factor that motor lead damages, and is in particular in:1st, motor
Lead wire and insullac react, and are caused motor lead to damage by insullac corrosion.2nd, motor lead is due to not scratch-resistant
Directly damage this electric wire.
Content of the invention:
The technical problem to be solved is to provide a kind of not only scratch-resistant but also the motor lines resistance of anti-insullac corrosion
Fuel.
The technical solution of the present invention is to provide a kind of motor lines flame-proof material, in terms of parts by weight, by following component
Composition:
100 parts of PVC resin powder;
43 parts of trioctyl trimellitate (TOTM);
6 parts of epoxy soybean oil;
30 parts of lightweight active nano-calcium carbonate;
6 parts of calcium zinc environmental protection complex stabilizer;
0.8 part of Tissuemat E;
5 parts of silicone master batch;
10 parts of chlorinated polyethylene;
4 parts of antimony oxide;
4 parts of phosphorus benzene flame retardant oil;
Pigment 0.5-3 part.
The invention has the beneficial effects as follows:The flame-proof material that this proportioning is obtained not only scratch-resistant but also the corrosion of anti-insullac, is that motor is special
Preferable selection with line.
Specific embodiment:
With reference to specific embodiment, the invention will be further described:
A kind of motor lines flame-proof material, in terms of parts by weight, is made up of following component:
100 parts of PVC resin powder;
43 parts of trioctyl trimellitate (TOTM);
6 parts of epoxy soybean oil;
30 parts of lightweight active nano-calcium carbonate;
6 parts of calcium zinc environmental protection complex stabilizer;
0.8 part of Tissuemat E;
5 parts of silicone master batch;
10 parts of chlorinated polyethylene;
4 parts of antimony oxide;
4 parts of phosphorus benzene flame retardant oil;
Pigment 0.5-3 part.
The cable materials being obtained by this components by weight percent not only scratch-resistant but also the corrosion of anti-insullac.
Claims (1)
1. a kind of motor lines flame-proof material it is characterised in that:In terms of parts by weight, it is made up of following component:
100 parts of PVC resin powder;
43 parts of trioctyl trimellitate (TOTM);
6 parts of epoxy soybean oil;
30 parts of lightweight active nano-calcium carbonate;
6 parts of calcium zinc environmental protection complex stabilizer;
0.8 part of Tissuemat E;
5 parts of silicone master batch;
10 parts of chlorinated polyethylene;
4 parts of antimony oxide;
4 parts of phosphorus benzene flame retardant oil;
Pigment 0.5-3 part.