CN104974446A - Environmental protection cable material - Google Patents
Environmental protection cable material Download PDFInfo
- Publication number
- CN104974446A CN104974446A CN201510355993.9A CN201510355993A CN104974446A CN 104974446 A CN104974446 A CN 104974446A CN 201510355993 A CN201510355993 A CN 201510355993A CN 104974446 A CN104974446 A CN 104974446A
- Authority
- CN
- China
- Prior art keywords
- parts
- cable material
- pvc resin
- polyvinyl chloride
- calcium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environmental protection cable material which comprises the following ingredients, by weight, 100 parts of PVC resin, 45 parts of polyvinyl chloride, 22 parts of dioctyl terephthalate, 21.5 parts of a filler, 8.45 parts of a modifier, 0.5 part of a colouring agent, 0.1 part of an antioxidant, 0.05 part of an ultraviolet ray absorber, 2 parts of a Ca-Zn composite stabilizer, 0.4 part of a lubricant, 1.5 parts of dicapryl phthalate, 0.8 part of an antioxidant, 25 parts of calcium carbonate, 5 parts of magnesium oxide, 3 parts of calcium oxide and 2.6 parts of paraffin. According to the cable material, PVC resin is used as a main material, and a small amount of linear low density polyethylene is added. The compatibility between PVC resin and linear low density polyethylene is good. As an environment-friendly type fire retardant is selected in the preparation of the cable material, application amount of the fire retardant is greatly reduced. Meanwhile, flame resistance is raised. Thus, the cable material is nontoxic and environmentally friendly.
Description
Technical field
The invention belongs to technical field of electric wires and cables, specifically a kind of environment-friendly cable material.
Background technology
Wire cable insulating and sheath plastics are commonly called as CABLE MATERIALS, which includes the multiple kinds such as rubber, plastics, nylon.In recent years, CABLE MATERIALS manufacturing enterprise of China had a great development, particularly some private enterprises, the market requirement is complied with in industrial scale, product restructuring and new product development, improves a lot.But it is inadequate to there is flame retardant resistance in the CABLE MATERIALS of prior art, and the problems such as heavy metals exceeding standard, hinder its application.
Summary of the invention
The object of the invention is to overcome prior art defect, a kind of environment-friendly cable material is provided.
Object of the present invention can be achieved through the following technical solutions:
A kind of environment-friendly cable material, by weight, following component is comprised: polyvinyl chloride resin 100 parts, polyvinyl chloride 45 parts, dioctyl terephthalate 22 parts, weighting agent 21.5 parts, properties-correcting agent 8.45 parts, tinting material 0.5 part, 0.1 part, oxidation inhibitor, UV light absorber 0.05 part, calcium-zinc composite stabilizing agent 2 parts, lubricant 0.4 part, dioctyl phthalate (DOP) 1.5 parts, 0.8 part, oxidation inhibitor, 25 parts, calcium carbonate, 5 parts, magnesium oxide, 3 parts, calcium oxide, 2.6 parts, paraffin.
Beneficial effect of the present invention: CABLE MATERIALS of the present invention adopts polyvinyl chloride resin to be major ingredient, and add a small amount of linear low density polyethylene, the two consistency is good, has synergy; CABLE MATERIALS of the present invention selects environment friendly flame retardant, greatly reduces the usage quantity of fire retardant, makes flame retardant properties be improved, environment-protecting asepsis simultaneously.
Embodiment
For the ease of it will be appreciated by those skilled in the art that the present invention is further illustrated below in conjunction with specific embodiment.
Embodiment 1
A kind of environment-friendly cable material, by weight, following component is comprised: polyvinyl chloride resin 100 parts, polyvinyl chloride 45 parts, dioctyl terephthalate 22 parts, weighting agent 21.5 parts, properties-correcting agent 8.45 parts, tinting material 0.5 part, 0.1 part, oxidation inhibitor, UV light absorber 0.05 part, calcium-zinc composite stabilizing agent 2 parts, lubricant 0.4 part, dioctyl phthalate (DOP) 1.5 parts, 0.8 part, oxidation inhibitor, 25 parts, calcium carbonate, 5 parts, magnesium oxide, 3 parts, calcium oxide, 2.6 parts, paraffin.
Above content is only citing made for the present invention and explanation; affiliated those skilled in the art make various amendment to described specific embodiment or supplement or adopt similar mode to substitute; only otherwise depart from invention or surmount this scope as defined in the claims, protection scope of the present invention all should be belonged to.
Claims (1)
1. an environment-friendly cable material, it is characterized in that, by weight, following component is comprised: polyvinyl chloride resin 100 parts, polyvinyl chloride 45 parts, dioctyl terephthalate 22 parts, weighting agent 21.5 parts, properties-correcting agent 8.45 parts, tinting material 0.5 part, 0.1 part, oxidation inhibitor, UV light absorber 0.05 part, calcium-zinc composite stabilizing agent 2 parts, lubricant 0.4 part, dioctyl phthalate (DOP) 1.5 parts, 0.8 part, oxidation inhibitor, 25 parts, calcium carbonate, 5 parts, magnesium oxide, 3 parts, calcium oxide, 2.6 parts, paraffin.