CN102977598A - PBT modified nylon PA66 particle material, as well as its preparation method and application in vehicles - Google Patents
PBT modified nylon PA66 particle material, as well as its preparation method and application in vehicles Download PDFInfo
- Publication number
- CN102977598A CN102977598A CN2012102954119A CN201210295411A CN102977598A CN 102977598 A CN102977598 A CN 102977598A CN 2012102954119 A CN2012102954119 A CN 2012102954119A CN 201210295411 A CN201210295411 A CN 201210295411A CN 102977598 A CN102977598 A CN 102977598A
- Authority
- CN
- China
- Prior art keywords
- nylon
- powder
- pbt
- injection
- particle material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a PBT modified nylon PA66 particle material, which is obtained by mixing a material A of the PBT modified nylon PA66 and a material B of the PBT modified nylon PA66, and then carrying out extrusion granulation. The present invention further discloses applications of the obtained modified nylon PA66 particle material in vehicle parts. The preparation method mainly comprises adding the dried modified material to a heated injection molding machine, setting injection pressures, speeds, injection times and glue injection amounts at different segments of the injection molding machine, and setting a final packing pressure and a packing speed to achieve an optimal injection molding process so as to obtain the final qualified product. After the modified nylon PA66 particle material is used for plastic connection devices of vehicles in the injection molding manner, advantages of high surface finish, good toughness, high strength and the like are provided, demolding is easily performed during injection molding, product quality is stable, a qualification rate is high, production efficiency is improved and production cost is reduced.
Description
Technical field
The present invention relates to the engineering plastics field, nylon PA66 particle material that is specifically related to a kind of PBT modification of modification and preparation method thereof reaches application.
Background technology
Along with social progress, the usage quantity of automobile is in continuous increase, a lot of junctors on automobile, connecting plug-in unit is obtained by the nylon manufacture, existing plastics connect plug-in unit and mainly adopt common nylon material, by adding, toughner is composite to be formed, after various material mixing, it is not good that each component is melted in process dispersiveness altogether, each group partition inter-capacitive is poor, intensity, toughness, the erosion resistance deficiency, material cost is higher, demoulding difficulty, surface gloss is poor, processing characteristics is bad, cause unstable product quality, conforming product rate is low, reduced economical efficiency, thereby affected the performance of automobile.
Summary of the invention
In order to alleviate shortcomings and deficiencies of the prior art, nylon PA66 particle material that the object of the present invention is to provide a kind of PBT modification and preparation method thereof reaches the application on auto parts machinery.The plastic connector for the production of automobile with the nylon PA66 particle material injection moulding of modification of the present invention, connect plug-in unit, there is easy-formation, the easily demoulding, the surface smoothness of product is high, good toughness, intensity is high, Shooting Technique stability, products obtained therefrom steady quality, improve production efficiency, reduced production cost.
The present invention adopts following technical scheme to achieve these goals:
A kind of nylon PA66 particle material of PBT modification, it is mixed in proportion extrusion molding by A material and B material and forms, and the A material is 1-2:1 with the mixed weight ratio of B material, and described A material, B material are obtained by the raw material extrusion granulating of following weight part respectively:
The A material:
Nylon PA66 50-60, ASA resin 15-20, PBT 10-15,3-aminopropyl trimethoxysilane 0.2-0.5, Union carbide A-162 0.3-0.5, antioxidant 1010 0.1-0.6, anti ultraviolet agent 0.1-0.4, polycaprolactone 2-5, polyethylene wax 1-2, modified Nano powder 5-10
Described modified Nano powder is made by following method: after calcium carbonate, celestite powder, feldspar in powder equal proportion are mixed, at 600-700 ℃ of lower scaling loss 4-5 hour, then grind to form nanometer powder, admix the Di(dioctylpyrophosphato) ethylene titanate agitating that is equivalent to powder weight 3-5% even, dry, be ground into powder;
The B material:
Nylon PA66 60-70, ASA resin 10-15, oxidation inhibitor 1035 0.1-0.3, polycaprolactone 2-5, vinyl three ('beta '-methoxy oxyethyl group) silane 0.20-0.4, phenyl triethoxysilane 0.3-0.7, two Lauryl Alcohol ester 0.5-1, ethylene bis stearamide 1-2, modified meerschaum 5-10
Described modified meerschaum is made by following method: first use 15-20% salt acid soak attapulgite 1-2 hour, and standing, clarification, centrifugal, solid washes with water to neutrality, after oven dry, add the vinyltriethoxysilane agitating that is equivalent to solid weight 3-5% even, dry, be ground into powder.
The preparation method of the nylon PA66 particle material of described PBT modification, is characterized in that, comprises the following steps:
The first step prepares the A material:
(1) take each formula material by formula rate;
(2) by the starting material that weigh up, after mixing, suck dry bucket, under 90-100 ℃, dry 4-6 hour;
(3) when the water content of compound is less than 0.3%, the dry end;
(4) adopt twin screw extruder to carry out extruding pelletization dried mixture, the barrel zone temperature 230-260 ℃ of forcing machine, screw speed is 190-550rpm;
Second step prepares the B material: adopt with the identical technique of A material and carry out granulation;
The 3rd step A material and B material mixing granulation:
A that first two steps are made material and B material, after the weight ratio mixing according to 1-2:1, extrusion granulating, obtain the high-impact nylon particle material of final PBT modification.
The nylon PA66 particle material of described PBT modification is applied on automobile, prepares connector sheet type plug boot DJ7061-6.0-21.
The nylon PA66 particle material of described PBT modification is applied on automobile, prepares the preparation method of connector sheet type plug boot DJ7061-6.0-21, it is characterized in that, comprises the following steps:
(1) after the nylon PA66 particle material of PBT modification and yellowish green toner are mixed in proportion, add dryer, dry 4-6h under 100-120 ℃, nylon PA66 particle material with yellow powder, titanium dioxide is pro rata mixes, mixed weight is than being (kg/g/g) 24-26:30:10;
(2) temperature of injection moulding machine heating zone is set: 275 ± 5 ℃ of first paragraphs, 270 ± 5 ℃ of second segments, the 3rd section 260 ± 5 ℃, the 4th section 255 ± 5 ℃, the 5th section 250 ± 5 ℃;
(3) by dried starting material, join in injection moulding machine, injection moulding, moulding, the demoulding, obtain product, injection moulding section molding technique parameter is set:
A, first paragraph adopt the middle pressure of 45-50 Mpa, the medium velocity injection of 45-55m/s, and be 1.0-1.5 second inject time, and injection glue amount is to the 78-80% of product;
B, second segment adopt the middle pressure of 55-60Mpa, the medium velocity injection of 45-55m/s, and be 0.5-1.0 second inject time, and injection glue amount is to 100% of water port of product.
Beneficial effect of the present invention:
The nylon PA66 particle material of PBT modification prepared by the inventive method, have good fluidity, easily processing, especially easily demoulding during injection moulding, the surface smoothness high of product, the plastic connector for automobile with the nylon PA66 particle material injection moulding of modification of the present invention, have surface smoothness high, good toughness, the intensity advantages of higher, insulativity is good, and heat-resistant aging is good, constant product quality, qualification rate is high, has improved production efficiency, has reduced production cost.
Embodiment
Embodiment 1
The nylon PA66 particle material of preparation PBT modification, concrete steps are:
The first step: preparation A material (kg):
Take nylon PA66 50, ASA resin 15, PBT 15,3-aminopropyl trimethoxysilane 0.2, Union carbide A-162 0.4, antioxidant 1010 0.2, anti ultraviolet agent 0.3, polycaprolactone 2, polyethylene wax 1.5, modified Nano powder 8,
Wherein, the modified Nano powder is made by following method: after calcium carbonate, celestite powder, feldspar in powder equal proportion are mixed, at 600-700 ℃ of lower scaling loss 4-5 hour, then grind to form nanometer powder, admix the Di(dioctylpyrophosphato) ethylene titanate agitating that is equivalent to powder weight 3-5% even, dry, be ground into powder
By the starting material that weigh up, after mixing, suck dry bucket, under 90-100 ℃ ℃, dry 4-6 hour;
When the water content of compound is less than 0.3%, the dry end;
Adopt twin screw extruder to carry out extruding pelletization dried mixture, obtain the A material, the barrel zone temperature 230-260 ℃ of forcing machine, screw speed is 480rpm;
Second step prepares B material (kg):
Take nylon PA66 65, ASA resin 10, oxidation inhibitor 1,035 0.2, polycaprolactone 2, vinyl three ('beta '-methoxy oxyethyl group) silane 0.2, phenyl triethoxysilane 0.4, two Lauryl Alcohol ester 0.6, ethylene bis stearamide 1.5, modified meerschaum 8
Wherein, modified meerschaum is made by following method: first use 15% salt acid soak attapulgite 2 hours, and standing, clarification, centrifugal, collect the solid material, the solid material washes with water to neutrality again, after oven dry, add the vinyltriethoxysilane agitating that is equivalent to solid weight 4% even, dry, be ground into powder, can obtain modified meerschaum
By the starting material that weigh up, after mixing, suck dry bucket, under 90-100 ℃, dry 4-6 hour;
When the water content of compound is less than 0.3%, the dry end;
Adopt twin screw extruder to carry out extruding pelletization dried mixture, obtain the B material, the barrel zone temperature 240-270 ℃ of forcing machine, screw speed is 450rpm;
The 3rd step: the A of the above-mentioned 50kg made material is mixed with the B material of 40kg, through main spout, add in twin screw extruder, the controlled working temperature is at 245-270 ℃, and the screw rod revolution is at 500rpm, and after melting, extruding pelletization obtains the nylon PA66 particle material of PBT modification.
Embodiment 2
The nylon PA66 particle material of the PBT modification made with embodiment 1, prepare the connector sheet type plug boot DJ7061-6.0-21 on automobile, comprises the following steps:
(1) after the yellow powder of the nylon PA66 particle material of 25kgPBT modification and 30g, 10 titanium dioxides are mixed, add dryer, under 100-120 ℃, dry 5h,
(2) temperature of injection moulding machine heating zone is set: 285 ± 5 ℃ of first paragraphs, 280 ± 5 ℃ of second segments, the 3rd section 270 ± 5 ℃, the 4th section 265 ± 5 ℃, the 5th section 260 ± 5 ℃;
(3) join in injection moulding machine by dried starting material, injection moulding section molding technique parameter be set:
A, first paragraph adopt the middle pressure of 45-50 Mpa, the medium velocity injection of 45-55m/s, and be 1.0-1.5 second inject time, and injection glue amount is to the 78-80% of product;
B, second segment adopt the middle pressure of 55-60Mpa, the medium velocity injection of 45-55m/s, and be 0.5-1.0 second inject time, and injection glue amount is to 100% of water port of product, and then injection moulding, moulding, the demoulding, obtain the finished product plug boot DJ7061-6.0-21,
Testing data
The Performance Detection for the plug boot DJ7061-6.0-21 on automobile that the present invention makes:
Claims (4)
1. the nylon PA66 particle material of a PBT modification, is characterized in that, it is mixed in proportion extrusion molding by A material and B material and forms, and the A material is 1-2:1 with the mixed weight ratio of B material, and described A material, B material are obtained by the raw material extrusion granulating of following weight part respectively:
The A material:
Nylon PA66 50-60, ASA resin 15-20, PBT 10-15,3-aminopropyl trimethoxysilane 0.2-0.5, Union carbide A-162 0.3-0.5, antioxidant 1010 0.1-0.6, anti ultraviolet agent 0.1-0.4, polycaprolactone 2-5, polyethylene wax 1-2, modified Nano powder 5-10
Described modified Nano powder is made by following method: after calcium carbonate, celestite powder, feldspar in powder equal proportion are mixed, at 600-700 ℃ of lower scaling loss 4-5 hour, then grind to form nanometer powder, admix the Di(dioctylpyrophosphato) ethylene titanate agitating that is equivalent to powder weight 3-5% even, dry, be ground into powder;
The B material:
Nylon PA6 60-70, ASA resin 10-15, oxidation inhibitor 1035 0.1-0.3, polycaprolactone 2-5, vinyl three ('beta '-methoxy oxyethyl group) silane 0.20-0.4, phenyl triethoxysilane 0.3-0.7, two Lauryl Alcohol ester 0.5-1, ethylene bis stearamide 1-2, modified meerschaum 5-10
Described modified meerschaum is made by following method: first use 15-20% salt acid soak attapulgite 1-2 hour, and standing, clarification, centrifugal, solid washes with water to neutrality, after oven dry, add the vinyltriethoxysilane agitating that is equivalent to solid weight 3-5% even, dry, be ground into powder
.
2. the preparation method of the nylon PA66 particle material of PBT modification as claimed in claim 1, is characterized in that, comprises the following steps:
The first step prepares the A material:
Take each formula material by formula rate;
By the starting material that weigh up, after mixing, suck dry bucket, under 90-100 ℃, dry 4-6 hour;
When the water content of compound is less than 0.3%, the dry end;
Adopt twin screw extruder to carry out extruding pelletization dried mixture, the barrel zone temperature 230-260 ℃ of forcing machine, screw speed is 190-550rpm;
Second step prepares the B material: adopt with the identical technique of A material and carry out granulation;
The 3rd step A material and B material mixing granulation:
A that first two steps are made material and B material, after the weight ratio mixing according to 1-2:1, extrusion granulating, obtain the nylon particle material of final PBT modification.
3. the nylon PA66 particle material of PBT modification according to claim 1 is applied on automobile, prepares connector sheet type plug boot DJ7061-6.0-21.
4. the nylon PA66 particle material of PBT modification according to claim 3 is applied on automobile, prepares the preparation method of connector sheet type plug boot DJ7061-6.0-21, it is characterized in that, comprises the following steps:
(1) after the nylon PA66 particle material of PBT modification and yellowish green toner are mixed in proportion, add dryer, dry 4-6h under 100-120 ℃, nylon PA66 particle material with yellow powder, titanium dioxide is pro rata mixes, mixed weight is than being (kg/g/g) 24-26:30:10;
(2) temperature of injection moulding machine heating zone is set: 275 ± 5 ℃ of first paragraphs, 270 ± 5 ℃ of second segments, the 3rd section 260 ± 5 ℃, the 4th section 255 ± 5 ℃, the 5th section 250 ± 5 ℃;
(3) by dried starting material, join in injection moulding machine, injection moulding, moulding, the demoulding, obtain product, injection moulding section molding technique parameter is set:
A, first paragraph adopt the middle pressure of 45-50 Mpa, the medium velocity injection of 45-55m/s, and be 1.0-1.5 second inject time, and injection glue amount is to the 78-80% of product;
B, second segment adopt the middle pressure of 55-60Mpa, the medium velocity injection of 45-55m/s, and be 0.5-1.0 second inject time, and injection glue amount is to 100% of water port of product.