CN102977531B - 一种膨胀珍珠岩改性的复合吸音材料及其制备方法 - Google Patents
一种膨胀珍珠岩改性的复合吸音材料及其制备方法 Download PDFInfo
- Publication number
- CN102977531B CN102977531B CN201210477962.7A CN201210477962A CN102977531B CN 102977531 B CN102977531 B CN 102977531B CN 201210477962 A CN201210477962 A CN 201210477962A CN 102977531 B CN102977531 B CN 102977531B
- Authority
- CN
- China
- Prior art keywords
- parts
- absorbing material
- pearlstone
- sound absorbing
- modification
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种膨胀珍珠岩改性的复合吸音材料,其由下列重量份的原料制成:重晶石粉 100-120、陶粒50-60、膨胀珍珠岩 40-50、丙烯酸乳液80-90、改性树木灰烬55-65、滑石粉15-20、涤纶纤维20-30、纳米碳10-20、EVA 20-30、CPE 15-20、聚异丁烯 5-10、环氧硬脂酸辛酯 5-8、磷酸甲苯二苯酯4-6、硬脂酸钙2-3、二盐基邻苯二甲酸铅1-2。本发明解决了目前急吸音材料的研发问题,制造出了满足需求的能够经受严酷环境考验,具有拉伸强度高、伸长率高、断裂强度高、吸音效果好等优点的新型吸音材料。
Description
技术领域
本发明涉及一种膨胀珍珠岩改性的复合吸音材料及其制备方法,属于材料研究与生产技术领域。
背景技术
随着工业生产、交通运输、城市建筑的发展,以及人口密度的增加,家庭设施(音响、空调、电视机等)的增多,环境噪声日益严重,它已成为污染人类社会环境的一大公害。噪声不仅会影响听力,而且还对人的心血管系统、神经系统、内分泌系统产生不利影响。
现有吸音材料也有复合型的,但是无机物料与有机物料复合的性能指标优异的较少。从整体上看,我国吸音材料行业产品加工能力不足,在高端吸音材料的研发和生产上与发达国家相比存在着较大的差距,如:各种类型交通工具(客车、地铁、高铁),尤其是近年载人航天器等吸音材料的需求,与产品最大的市场—建筑业也缺乏衔接,缺乏市场意识和建筑产品加工能力。因此,目前急需研究开发一种能够经受严酷环境考验,具有拉伸强度高、伸长率高、断裂强度高、吸音效果好并且制造成本低等优点的新型吸音材料。
发明内容
本发明的目的在于,提供一种膨胀珍珠岩改性的复合吸音材料及其制备方法,解决复合材料的配方,降低采用单种或多种原料的生产成本,同时提高材料的吸音效果和材料的拉伸强度,伸长率、断裂强度。用于喷丝制作吸音棉。
本发明采用的技术方案如下:
一种膨胀珍珠岩改性的复合吸音材料,其由下列重量份的原料制成:重晶石粉 100-120、陶粒50-60、膨胀珍珠岩 40-50、丙烯酸乳液80-90、改性树木灰烬55-65、滑石粉15-20、涤纶纤维20-30、纳米碳10-20、EVA 20-30、CPE 15-20、聚异丁烯 5-10、环氧硬脂酸辛酯 5-8、磷酸甲苯二苯酯4-6、硬脂酸钙2-3、二盐基邻苯二甲酸铅1-2。
所述的改性树木灰烬由以下方法制得:先用10-15%盐酸浸泡树木灰烬3-4h,去离子水洗涤干净,再用10-12%氢氧化钠溶液浸泡3-4h,再用去离子水洗涤至中性,烘干,加入相当于树木灰烬重量2-3%的木质素磺酸钠、1-2%的甲基三乙氧基硅烷、2-3%的环氧化甘油三酸酯、3-5%的陶瓷粉,高速1200-1500r/min搅拌20-30min,烘干粉碎研磨成超细粉末即可。
膨胀珍珠岩改性的复合吸音材料的制备方法,包括以下步骤:
(1)将重晶石粉、陶粒、膨胀珍珠岩分别干燥除水分,干燥温度为110-120℃,干燥时间为2-3h,按后按配方配比将重晶石粉 、陶粒、膨胀珍珠岩、滑石粉、丙烯酸乳液加入高速混合机中,在150-160℃下以500-800rpm的速度搅拌混合3-5min,再加入改性树木灰烬继续共混5-8min,物料冷却至常温待用;
(2)将EVA、聚异丁烯、CPE、环氧硬脂酸辛酯、磷酸甲苯二苯酯、硬脂酸钙、二盐基邻苯二甲酸铅加入多向运动混合机进行初混,初混4-6min,然后进入高速混合机,加入纳米碳、涤纶纤维,在105-110℃下以1500-2000rpm的速度搅拌2-5min,物料冷却至常温待用;
(3)将上述步骤(1)和步骤(2)制得的物料加入双螺杆混合挤出机进行处理,依据产品指标要求温度设定范围180-280℃,然后将挤出的物料投入造粒机造粒,即得复合吸音材料。
本发明的有益效果如下:
本发明通过对配方调整和工艺改进,利用改性树木灰烬包覆膨胀珍珠岩、重晶石粉等无机粉体,从而提高吸音材料的吸音效果和强度,很好地解决了吸音材料强度和吸音性能不能兼得的矛盾。本发明解决了目前急吸音材料的研发问题,制造出了满足需求的能够经受严酷环境考验,具有拉伸强度高、伸长率高、断裂强度高、吸音效果好等优点的新型吸音材料。由于采用了较大比例的无机物料,因此降低了生产成本,同时由于无机物料的强度较高,提高了材料的力学性能。
具体实施方式
一种膨胀珍珠岩改性的复合吸音材料,其由下列重量份的原料制成:重晶石粉 110份、陶粒55份、膨胀珍珠岩48份、丙烯酸乳液86份、改性树木灰烬60份、滑石粉18份、涤纶纤维24份、纳米碳16份、EVA 30份、CPE 15份、聚异丁烯6份、环氧硬脂酸辛酯5份、磷酸甲苯二苯酯5份、硬脂酸钙1.5份、二盐基邻苯二甲酸铅1.5份。
其中,所述的改性树木灰烬由以下方法制得:先用10%盐酸浸泡树木灰烬4h,去离子水洗涤干净,再用12%氢氧化钠溶液浸泡3h,再用去离子水洗涤至中性,烘干,加入相当于树木灰烬重量2.5%的木质素磺酸钠、1.5%的甲基三乙氧基硅烷、3%的环氧化甘油三酸酯、5%的陶瓷粉,高速1200r/min搅拌30min,烘干粉碎研磨成超细粉末即可。
膨胀珍珠岩改性的复合吸音材料的制备方法,包括以下步骤:
(1)将重晶石粉、陶粒、膨胀珍珠岩分别干燥除水分,干燥温度为115℃,干燥时间为2h,按后按配方配比将重晶石粉 、陶粒、膨胀珍珠岩、滑石粉、丙烯酸乳液加入高速混合机中,在160℃下以800rpm的速度搅拌混合3min,再加入改性树木灰烬继续共混5min,物料冷却至常温待用;
(2)将EVA、聚异丁烯、CPE、环氧硬脂酸辛酯 、磷酸甲苯二苯酯、硬脂酸钙、二盐基邻苯二甲酸铅加入多向运动混合机进行初混,初混5min,然后进入高速混合机,加入纳米碳、涤纶纤维,在105℃下以1600rpm的速度搅拌4min,物料冷却至常温待用;
(3)将上述步骤(1)和步骤(2)制得的物料加入双螺杆混合挤出机进行处理,依据产品指标要求温度设定为235℃,然后将挤出的物料投入造粒机造粒,即得复合吸音材料。
检测指标:吸声系数1.28,拉伸强度1396kPa,伸长率51%,断裂强度4898N/m。成本4356元/吨。
Claims (1)
1.一种膨胀珍珠岩改性的复合吸音材料,其特征在于,其由下列重量份的原料制成:重晶石粉 100-120、陶粒50-60、膨胀珍珠岩 40-50、丙烯酸乳液80-90、改性树木灰烬55-65、滑石粉15-20、涤纶纤维20-30、纳米碳10-20、EVA 20-30、CPE 15-20、聚异丁烯 5-10、环氧硬脂酸辛酯5-8、磷酸甲苯二苯酯4-6、硬脂酸钙2-3、二盐基邻苯二甲酸铅1-2;
所述的改性树木灰烬由以下方法制得:先用10-15%盐酸浸泡树木灰烬3-4h,去离子水洗涤干净,再用10-12%氢氧化钠溶液浸泡3-4h,再用去离子水洗涤至中性,烘干,加入相当于树木灰烬重量2-3%的木质素磺酸钠、1-2%的甲基三乙氧基硅烷、2-3%的环氧化甘油三酸酯、3-5%的陶瓷粉,高速1200-1500r/min搅拌20-30min,烘干粉碎研磨成超细粉末即可;
所述的膨胀珍珠岩改性的复合吸音材料的制备方法,包括以下步骤:
(1)将重晶石粉、陶粒、膨胀珍珠岩分别干燥除水分,干燥温度为110-120℃,干燥时间为2-3h,按后按配方配比将重晶石粉 、陶粒、膨胀珍珠岩、滑石粉、丙烯酸乳液加入高速混合机中,在150-160℃下以500-800rpm的速度搅拌混合3-5min,再加入改性树木灰烬继续共混5-8min,物料冷却至常温待用;
(2)将EVA、聚异丁烯、CPE、环氧硬脂酸辛酯 、磷酸甲苯二苯酯、硬脂酸钙、二盐基邻苯二甲酸铅加入多向运动混合机进行初混,初混4-6min,然后进入高速混合机,加入纳米碳、涤纶纤维,在105-110℃下以1500-2000rpm的速度搅拌2-5min,物料冷却至常温待用;
(3)将上述步骤(1)和步骤(2)制得的物料加入双螺杆混合挤出机进行处理,依据产品指标要求温度设定范围180-280℃,然后将挤出的物料投入造粒机造粒,即得复合吸音材料。