CN102977504A - 一种pvc双壁胶管配方 - Google Patents

一种pvc双壁胶管配方 Download PDF

Info

Publication number
CN102977504A
CN102977504A CN 201210526568 CN201210526568A CN102977504A CN 102977504 A CN102977504 A CN 102977504A CN 201210526568 CN201210526568 CN 201210526568 CN 201210526568 A CN201210526568 A CN 201210526568A CN 102977504 A CN102977504 A CN 102977504A
Authority
CN
China
Prior art keywords
parts
pvc
double
rubber tube
wall rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201210526568
Other languages
English (en)
Inventor
李盼盼
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QINGDAO XINWANTONG PLASTIC INDUSTRY DEVELOPMENT Co Ltd
Original Assignee
QINGDAO XINWANTONG PLASTIC INDUSTRY DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINGDAO XINWANTONG PLASTIC INDUSTRY DEVELOPMENT Co Ltd filed Critical QINGDAO XINWANTONG PLASTIC INDUSTRY DEVELOPMENT Co Ltd
Priority to CN 201210526568 priority Critical patent/CN102977504A/zh
Publication of CN102977504A publication Critical patent/CN102977504A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种PVC双壁胶管配方，其特征在于：由以下重量份数的原料制成：PVC树脂40-60份，葵二酸二辛酯5-10份，丁苯橡胶10-15份，聚乙烯蜡3-6份，稀土稳定剂5-8份，碳酸钙5-15份，稳定剂3-7份，硬脂酸6-10份，热稳定剂3-5份。本发明提供一种加工性能优异、产品质量好、安全性高的PVC双壁胶管配方。上述PVC双壁胶管，采用PVC树脂为主要原料，经高温高压挤压成型，抗冲击，耐高温，耐寒，使用寿命长，用于地下通信管道的铺设，对通信光缆、电缆起到保护作用。

Description

一种PVC双壁胶管配方
技术领域
本发明涉及PVC管材技术领域，具体涉及一种PVC双壁胶管配方。
背景技术
近年来，我国对PVC 的总需求量仍出现稳定的二位数增长态势。但由于PVC分子链存在结构缺陷，加热至110℃时会脱出氯化氢，放出的氯化氢又会加速PVC 的分解，因此PVC 在加工温度160℃ -200℃时会发生明显降解，引起产品的变色和制品机械性能等下降，影响使用寿命。
目前，国内生产PVC关键的厂家和文献报道几乎全部采用偶联剂处理木粉的方法，如采用硅烷、酞酸酯、铝酸酯、铝钛复合偶联剂等偶联剂处理木粉，以改善木粉与PVC树脂的结合，忽略了复合材料成型加工过程中木粉在PVC中分散等问题。这种方法存在木粉填充量小、木粉在PVC中分散不良、熔体流动困难、加工性能差、制品外观粗糙等缺点。
发明内容
针对现有技术的不足，本发明所要解决的技术问题是，提供一种加工性能优异、产品质量好、安全性高的PVC双壁胶管配方。
为解决上述技术问题，本发明所采取的技术方案是：一种PVC双壁胶管配方，由以下重量份数的原料制成：PVC树脂40-60份，葵二酸二辛酯5-10份，丁苯橡胶10-15份，聚乙烯蜡3-6份，稀土稳定剂5-8份，碳酸钙5-15份，稳定剂3-7份，硬脂酸6-10份，热稳定剂3-5份。
上述的PVC双壁胶管配方，所述的稳定剂为铅盐复合稳定剂。
本发明PVC双壁胶管配方优点是：
1、本发明PVC双壁胶管配方，上述PVC 双壁胶管，采用PVC 树脂为主要原料，经高温高压挤压成型，抗冲击，耐高温，耐寒，使用寿命长，用于地下通信管道的铺设，对通信光缆、电缆起到保护作用。
2、本发明PVC双壁胶管配方，加工性能优异、产品质量好、安全性高。
具体实施方式
下面结合实施例对本发明作进一步说明。
实施例1，一种PVC双壁胶管配方，由以下重量份数的原料制成：PVC树脂40份，葵二酸二辛酯5份，丁苯橡胶10份，聚乙烯蜡3份，稀土稳定剂5份，碳酸钙5份，稳定剂3份，硬脂酸6份，热稳定剂3份。
上述的稳定剂为铅盐复合稳定剂。  
实施例2，一种PVC双壁胶管配方，由以下重量份数的原料制成：PVC树脂50份，葵二酸二辛酯8份，丁苯橡胶12份，聚乙烯蜡5份，稀土稳定剂6份，碳酸钙10份，稳定剂5份，硬脂酸8份，热稳定剂4份。
上述的稳定剂为铅盐复合稳定剂。
实施例3，一种PVC双壁胶管配方，由以下重量份数的原料制成：PVC树脂60份，葵二酸二辛酯10份，丁苯橡胶15份，聚乙烯蜡6份，稀土稳定剂8份，碳酸钙15份，稳定剂7份，硬脂酸10份，热稳定剂5份。
上述的稳定剂为铅盐复合稳定剂。
当然，上述说明并非是对本发明的限制，本发明也并不限于上述举例，本技术领域的普通技术人员，在本发明的实质范围内，作出的变化、改变、添加或替换，都应属于本发明的保护范围。

Claims (2)

1.一种PVC双壁胶管配方，其特征在于：由以下重量份数的原料制成：PVC树脂40-60份，葵二酸二辛酯5-10份，丁苯橡胶10-15份，聚乙烯蜡3-6份，稀土稳定剂5-8份，碳酸钙5-15份，稳定剂3-7份，硬脂酸6-10份，热稳定剂3-5份。
2.根据权利要求1所述的PVC双壁胶管配方，其特征在于：所述的稳定剂为铅盐复合稳定剂。
CN 201210526568 2012-12-10 2012-12-10 一种pvc双壁胶管配方 Pending CN102977504A (zh)