CN102961896A - 以粉煤灰空心玻璃微珠为填充料的粉末消泡剂 - Google Patents

以粉煤灰空心玻璃微珠为填充料的粉末消泡剂 Download PDF

Info

Publication number
CN102961896A
CN102961896A CN2011103660461A CN201110366046A CN102961896A CN 102961896 A CN102961896 A CN 102961896A CN 2011103660461 A CN2011103660461 A CN 2011103660461A CN 201110366046 A CN201110366046 A CN 201110366046A CN 102961896 A CN102961896 A CN 102961896A
Authority
CN
China
Prior art keywords
hollow glass
bead
glass micro
inserts
flyash hollow
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011103660461A
Other languages
English (en)
Other versions
CN102961896B (zh
Inventor
李军伟
田东奎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHAANXI JIANKE ENERGY SAVING DEVELOPMENT CO., LTD.
Original Assignee
Tianjin Pharmacn Medical Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin Pharmacn Medical Technology Co Ltd filed Critical Tianjin Pharmacn Medical Technology Co Ltd
Priority to CN201110366046.1A priority Critical patent/CN102961896B/zh
Publication of CN102961896A publication Critical patent/CN102961896A/zh
Application granted granted Critical
Publication of CN102961896B publication Critical patent/CN102961896B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及以粉煤灰空心玻璃微珠为填充料的粉末消泡剂，原料的质量组成为：消泡活性物质5～30份，乳化剂1～8份，填充料94～62份。消泡活性物质为有机硅氧烷和疏水白炭黑，乳化剂为非离子型的硅聚醚乳化剂，填充料为粉煤灰空心玻璃微珠。其制备方法是先将有机聚硅氧烷和疏水白炭黑在高温制得硅脂，所得硅脂再与乳化剂和粉煤灰空心玻璃微珠搅拌混合均匀，制得粉末消泡剂。该消泡剂可应用于混凝土消泡，也可应用于煤浮选过程消泡。

Description

以粉煤灰空心玻璃微珠为填充料的粉末消泡剂
技术领域
本发明涉及粉煤灰空心玻璃微珠的高附加值利用领域，特别是涉及一种以粉煤灰空心玻璃微珠为填充料的粉末消泡剂。具体涉及一种以有机硅氧烷、疏水白炭黑、硅聚醚乳化剂和粉煤灰空心玻璃微珠为主要原料，制备粉末消泡剂的方法。
背景技术
粉煤灰空心玻璃微珠是从电厂固体废弃物粉煤灰中提取出的一种轻质中空微型球状物质，它具有密度低、熔点高、电绝缘性好、流动性好、收缩率小、稳定性强、隔热、隔音、耐高温、导热系数和热收缩系数小等一系列优点，目前被广泛应用于高档建材、塑料、橡胶、电绝缘材料、汽车、航空航天，以及军事特种高分子复合材料等领域。但应用于消泡剂中尚未见有关报道。将其应用于消泡剂中，突出其轻质和于其他无机材料相容性好的特点，是对粉煤灰的一种高附加值利用。本发明提供一种以粉煤灰空心玻璃微珠为填充料的粉末消泡剂。该消泡剂可应用于混凝土消泡，也可应用于煤浮选过程消泡。
发明内容
本发明的目的在于提供一种新型的以粉煤灰空心玻璃微珠为填充料的粉末消泡剂。具体为一种以有机硅氧烷、疏水白炭黑、硅聚醚乳化剂和粉煤灰空心玻璃微珠为主要原料，制备粉末消泡剂的方法。该方法工艺简单，可大规模制备，可应用于混凝土和煤浮选过程消泡，具有较高的实际应用价值
本发明采用的技术方案为：
本发明提供了以粉煤灰空心玻璃微珠为填充料的粉末消泡剂，它由下列组份组成：
消泡活性物质5～30份
乳化剂      1～8份
填充料      94～62份
优选地，所述的消泡活性物质为有机硅氧烷和疏水白炭黑，有机硅氧烷为聚二甲基硅氧烷，其粘度为50～500cst，疏水白炭黑为经过有机硅偶联剂疏水处理的白炭黑。
优选地，所述的乳化剂为非离子型的硅聚醚乳化剂。
优选地，所述的填充料为粉煤灰空心玻璃微珠，其平均粒径为20～40μm，密度为0.4～0.6g/cc。
本发明还提供了以粉煤灰空心玻璃微珠为填充料的粉末消泡剂的制备方法，它包括以下步骤：
(1)将有机聚硅氧烷和疏水白炭黑按计量加入反应釜中，200℃下保温8h，所得硅脂产品经过胶体磨研磨；
(2)将(1)所得硅脂在60～90℃下与乳化剂按计量充分混合，再加入粉煤灰空心玻璃微珠，搅拌均匀即得粉末消泡剂。
本发明所具有的有益效果：
本发明涉及一种以粉煤灰空心玻璃微珠为填充料的粉末消泡剂。以有机硅氧烷、疏水白炭黑、硅聚醚乳化剂和粉煤灰空心玻璃微珠为主要原料，制备粉末消泡剂。制备方法是先将有机聚硅氧烷和疏水白炭黑在高温制得硅脂，所得硅脂再与乳化剂和粉煤灰空心玻璃微珠搅拌混合均匀，制得粉末消泡剂。该消泡剂可应用于混凝土消泡，也可应用于煤浮选过程消泡。
具体实施方式
下面结合具体实施例对本发明作进一步说明，但不限定本发明的保护范围。
实施例1
将100cst二甲基硅油95g、疏水白炭黑5g加入反应釜中，200℃下保温8h，得硅脂产品过胶体磨研磨；将上述硅脂10g与硅聚醚乳化剂5g在70℃下充分混合，将85g粉煤灰空心玻璃微珠加入上述混合物中，搅拌均匀，即得粉末消泡剂。
实施例2
将100cst二甲基硅油95g、疏水白炭黑5g加入反应釜中，200℃下保温8h，得硅脂产品过胶体磨研磨；将上述硅脂10g与硅聚醚乳化剂10g在75℃下充分混合，将80g粉煤灰空心玻璃微珠加入上述混合物中，搅拌均匀，即得粉末消泡剂。
实施例3
将100cst二甲基硅油95g、疏水白炭黑5g加入反应釜中，200℃下保温8h，得硅脂产品过胶体磨研磨；将上述硅脂15g与硅聚醚乳化剂15g在75℃下充分混合，将70g粉煤灰空心玻璃微珠加入上述混合物中，搅拌均匀，即得粉末消泡剂。
以上所述，仅是本发明的较佳实施例而已，并非对本发明的技术方案作任何形式上的限制。凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明的技术方案的范围内。

Claims (7)

1.一种以粉煤灰空心玻璃微珠为填充料的粉末消泡剂，它由下列组份组成：
消泡活性物质5～30份
乳化剂      1～8份
填充料      94～62份
2.根据权利要求1所述的以粉煤灰空心玻璃微珠为填充料的粉末消泡剂，其特征在于所述的消泡活性物质为有机硅氧烷和疏水白炭黑。
3.根据权利要求1、2所述的以粉煤灰空心玻璃微珠为填充料的粉末消泡剂，其特征在于所述的有机硅氧烷为聚二甲基硅氧烷，其粘度为50～500cst。
4.根据权利要求1、2所述的以粉煤灰空心玻璃微珠为填充料的粉末消泡剂，其特征在于所述的疏水白炭黑为经过有机硅偶联剂疏水处理的白炭黑。
5.根据权利要求1所述的以粉煤灰空心玻璃微珠为填充料的粉末消泡剂，其特征在于所述的乳化剂为非离子型的硅聚醚乳化剂。
6.根据权利要求1所述的以粉煤灰空心玻璃微珠为填充料的粉末消泡剂，其特征在于所述的填充料为粉煤灰空心玻璃微珠，其平均粒径为20～40μm，密度为0.4～0.6g/cc。
7.一种权利要求1所述以粉煤灰空心玻璃微珠为填充料的粉末消泡剂，其特征在于它包括以下步骤：
(1)将有机聚硅氧烷和疏水白炭黑按计量加入反应釜中，200℃下保温8h，所得硅脂产品经过胶体磨研磨；
(2)将(1)所得硅脂在60～90℃下与乳化剂按计量充分混合，再加入粉煤灰空心玻璃微珠，搅拌均匀即得产品。
CN201110366046.1A 2011-11-17 2011-11-17 以粉煤灰空心玻璃微珠为填充料的粉末消泡剂 Active CN102961896B (zh)