CN102952977A - 一种温室工程用铝型材的制备方法 - Google Patents

一种温室工程用铝型材的制备方法 Download PDF

Info

Publication number
CN102952977A
CN102952977A CN2011102465048A CN201110246504A CN102952977A CN 102952977 A CN102952977 A CN 102952977A CN 2011102465048 A CN2011102465048 A CN 2011102465048A CN 201110246504 A CN201110246504 A CN 201110246504A CN 102952977 A CN102952977 A CN 102952977A
Authority
CN
China
Prior art keywords
casting
aluminium
magnesium
boron
titanium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011102465048A
Other languages
English (en)
Inventor
杨德富
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2011102465048A priority Critical patent/CN102952977A/zh
Publication of CN102952977A publication Critical patent/CN102952977A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种温室工程用铝型材的制备方法，它包括以下步骤：步骤一，进行成份计算：根据合金成份含量进行计算，确定各种合金元素添加量，其中镁的含量为0.6％，硅的含量为0.41％，钛为0.1％，硼为0.1％，杂质为0.29％，其余为铝；步骤二，根据计算结果准确投料，由于各个合金元素的熔点不同，首先投放铝锭，当铝锭融化后再通过特殊加镁，将镁加入到铝水中，最后将钛和硼加入进行精炼，其精炼的方法是通入高纯氮气，以及钾盐或钠盐，应用化学反应及分压原理，达到造渣、除渣的目的，最后静置；步骤三，将静置后的合金材料进行热顶铸造工艺制得温室工程用铝型材，热顶铸造工艺的铸造温度为720-740℃、铸造速度为100-120mm/min，铸造时采用泡沫陶瓷过滤。

Description

一种温室工程用铝型材的制备方法
技术领域
本发明涉及一种温室工程用铝型材的制备方法。
背景技术
随着能源短缺，节能减排已成为我国的一项基本国策；另一方面，随着科学技术的发展，太阳能的利用越来越广泛，尤其是温室工程逐步被人们所认识，而且被应用于各个领域，如农业科技、医疗健身、花卉种殖、水产养殖等。对于传统的温室工程所用的材料为毛竹、钢管等，这些材料耐腐蚀性能差、抗风压能力差、装饰性较差，且温室工程主要应用在蔬菜大棚等粗放结构上。
发明内容
本发明涉及一种温室工程用铝型材的制备方法，它采用优越的表面处理技术，材料经阳极氧化后，表面色泽光亮，细腻柔和、美观大方，装饰性好。而且它选择最佳的成份配方，控制合金的成份含量，既显著提高了材料的强度，又大大提高了材料的塑性。
本发明采用了以下技术方案：一种温室工程用铝型材的制备方法，它包括以下步骤：步骤一，进行成份计算：根据合金成份含量进行计算，确定各种合金元素添加量，其中镁的含量为0.6％，硅的含量为0.41％，钛为0.1％，硼为0.1％，杂质为0.29％，其余为铝；步骤二，根据计算结果准确投料，由于各个合金元素的熔点不同，首先投放铝锭，当铝锭融化后再通过特殊加镁，将镁加入到铝水中，最后将钛和硼加入进行精炼，其精炼的方法是通入高纯氮气，以及钾盐或钠盐，应用化学反应及分压原理，达到造渣、除渣的目的，最后静置；步骤三，将静置后的合金材料进行热顶铸造工艺制得温室工程用铝型材，热顶铸造工艺的铸造温度为720-740℃、铸造速度为100-120mm/min，铸造时采用泡沫陶瓷过滤。
本发明的步骤三中铸造温度为720℃、铸造速度为100mm/min。
本发明具有以下有益效果：本发明的合金材料中加入镁，在加入的同时采用特殊加镁工具进行添加，这样从而有效地减少镁的烧损，提高金属镁的利用率，确保成份控制准确。本发明的工艺采用热顶铸造，这样可以使材料的内部组织、晶粒细化均匀、性能稳定一致。本发明在铝材中添加镁、硅和微量钛、硼，镁在金属中的作用，具有形成强化相，提高强度，增加金属材料的表面处理性能，硅在金属中的作用具有形成强化相，提高强度，增加金属的流动性，提高金属材料的内部组织，钛及硼起到细化晶粒作用，改善金属材料的内部组织晶粒大小，以及内部组织结构的均匀性，这样不但选择最佳的成份配方，控制合金的成份含量，既显著提高了材料的强度，又大大提高了材料的塑性，同时采用优越的表面处理效果，材料经阳极氧化后，表面色泽光亮，细腻柔和、美观大方，装饰性好。
具体实施方式
本发明还公开了一种温室工程用铝型材的制备方法，它包括以下步骤：步骤一，进行成份计算：根据合金成份含量进行计算，确定各种合金元素添加量，其中镁的含量为0.6％，硅的含量为0.41％，钛为0.1％，硼为0.1％，杂质为0.29％，其余为铝；步骤二，根据计算结果准确投料，由于各个合金元素的熔点不同，首先投放铝锭，当铝锭融化后再通过特殊加镁，将镁加入到铝水中，最后将钛和硼加入进行精炼，其精炼的方法是通入高纯氮气，以及钾盐或钠盐，应用化学反应及分压原理，达到造渣、除渣的目的，最后静置；步骤三，将静置后的合金材料进行热顶铸造工艺制得温室工程用铝型材，热顶铸造工艺的铸造温度为720℃、铸造速度为：100mm/min，铸造时采用泡沫陶瓷过滤。

Claims (2)

1.一种温室工程用铝型材的制备方法，它包括以下步骤：
步骤一，进行成份计算：根据合金成份含量进行计算，确定各种合金元素添加量，其中镁的含量为0.6％，硅的含量为0.41％，钛为0.1％，硼为0.1％，杂质为0.29％，其余为铝；
步骤二，根据计算结果准确投料，由于各个合金元素的熔点不同，首先投放铝锭，当铝锭融化后再通过特殊加镁，将镁加入到铝水中，最后将钛和硼加入进行精炼，其精炼的方法是通入高纯氮气，以及钾盐或钠盐，应用化学反应及分压原理，达到造渣、除渣的目的，最后静置；
步骤三，将静置后的合金材料进行热顶铸造工艺制得温室工程用铝型材，热顶铸造工艺的铸造温度为720-740℃、铸造速度为100-120mm/min，铸造时采用泡沫陶瓷过滤。
2.根据权利要求1所述的温室工程用铝型材的制备方法，其特征是步骤三中铸造温度为720℃、铸造速度为100mm/min。
CN2011102465048A 2011-08-26 2011-08-26 一种温室工程用铝型材的制备方法 Pending CN102952977A (zh)