CN102923945B - 复合废渣玻璃澄清助熔剂 - Google Patents
复合废渣玻璃澄清助熔剂 Download PDFInfo
- Publication number
- CN102923945B CN102923945B CN201210435572.3A CN201210435572A CN102923945B CN 102923945 B CN102923945 B CN 102923945B CN 201210435572 A CN201210435572 A CN 201210435572A CN 102923945 B CN102923945 B CN 102923945B
- Authority
- CN
- China
- Prior art keywords
- waste residue
- glass
- compound waste
- metallurgical slag
- sio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种复合废渣玻璃澄清助熔剂,属于玻璃生产技术领域。该助熔剂原材料配方中去掉白砒、氧化锑硫酸盐、氟化物、氧化铈,及上述澄清剂的复合物等有害原料,利用化工废渣和冶金废渣为主要原料,添加少量NaCL以及微量氧化剂和还原剂,获得无毒、低成本的玻璃澄清剂;其原料组分配比为:化工废渣45%-58%、冶金废渣35%-49%、NaCL6%-10%、硝酸盐1%-2%、碳粉0.5%-1%。助熔剂的化学成分组成为:SiO2?3%-6%、AL2O3?2%-3%、CaO?35%-50%、SO2SO3O2?45%-52%、R2O?3%-5%。按上述各实施例原料配比,采用常规配料工艺均可获得本发明所述的玻璃澄清助熔剂。本发明的积极效果是澄清效果良好,玻璃无气泡,可取代白砒、氧化锑、氧化铈和硫酸盐澄清剂,不含有毒化合物及对耐火材料侵蚀性物质,可延长窑炉的使用寿命。
Description
技术领域
本发明属于玻璃生产技术领域。
背景技术
玻璃生产需要一种消除气泡的玻璃澄清剂。目前玻璃厂使用的传统澄清剂有白砒、氧化锑硫酸盐、氟化物、氧化铈,及以上述澄清剂的复合物。白砒、氧化锑澄清剂效果好,但属剧毒化合物,熔制时砷、锑挥发,是人的呼吸系统吸收而中毒并污染环境。在制造和使用过程中,砷、锑与人体接触,通过皮肤和粘膜的吸收而中毒。氧化铈澄清剂效果好,但价格昂贵。开发一种无毒低成本复合玻璃澄清剂不仅有显著的社会效益,而且有较大的经济效益。
发明内容
本发明的目的是提一种复合废渣玻璃澄清助熔剂,以解决现有技术毒性大、价格昂贵、生产成本高等问题。
本发明解决其技术问题所采用的技术方案是助熔剂原材料配方中去掉白砒、氧化锑硫酸盐、氟化物、氧化铈,及以上述澄清剂的复合物等有害原料,利用化工废渣和冶金废渣为主要原料,添加少量NaCL以及微量氧化剂和还原剂,获得无毒、低成本的玻璃澄清剂。
化工废渣含如下成分:SiO2、CaO、AL2O3、Na2O、P2O5、SO3Fe2O3。
冶金废渣含如下成分:SiO2、CaO、Al2O3、R2O、SO3、Fe2O3。
复合废渣玻璃澄清助熔剂的原料组分配比为:(重量百分比)化工废渣45%-58%,冶金废渣35%-49%,NaCL6%-10%,硝酸盐1%-2%,碳粉0.5%-1%。
所述氧化剂为硝酸盐;
所述还原剂为碳粉;
复合废渣玻璃澄清助熔剂的化学成分组成为:SiO23%-6%、AL2O32%-3%、CaO35%-50%、SO2SO3O245%-52%、R2O3%-5%。
按上述各实施例原料配比,采用常规配料工艺均可获得本发明所述的玻璃澄清助熔剂。
应用对比试验结果表明,采用上述复合废渣配制的玻璃澄清剂,澄清效果良好,玻璃无气泡,安全,可以取代白砒、氧化锑、氧化铈和硫酸盐澄清剂,同时可减少5%-6%的纯碱用量,澄清剂成本降低,澄清剂的成本仅为原来使用的澄清剂的45%左右。
因复合废渣玻璃澄清助熔剂中不含有毒化合物,减少了对大气的污染,不含对耐火材料侵蚀性物质,可延长窑炉的使用寿命。
该复合废渣玻璃澄清助熔剂适用于白料、颜色料等玻璃产品的生产,可在日用玻璃、平板玻璃、玻璃纤维生产中使用。
具体实施方式
下面以不同的原料配比量、澄清剂不同的化学成分含量分别提供具体实施例:
实施例1(取幅度值低值)
复合废渣玻璃澄清助熔剂的原料组分配比为:化工废渣45%,冶金废渣35%,NaCL6%,硝酸盐1%,碳粉0.5%。
复合废渣玻璃澄清助熔剂的化学成分组成为:
SiO23%、AL2O32%、CaO35%、SO2SO3O245%、R2O3%。
按上述各实施例原料配比,采用常规配料工艺均可获得本发明所述的玻璃澄清助熔剂。
实施例2(取幅度值高值)
复合废渣玻璃澄清助熔剂的原料组分配比为:化工废渣58%,冶金废渣49%、NaCL10%、硝酸盐2%、碳粉1%。
复合废渣玻璃澄清助熔剂的化学成分组成为:
SiO26%、AL2O33%、CaO50%、SO2SO3O252%、R2O5%。
按上述各实施例原料配比,采用常规配料工艺均可获得本发明所述的玻璃澄清助熔剂。
实施例3(取幅度值中值)
复合废渣玻璃澄清助熔剂的原料组分配比为:化工废渣52%、冶金废渣42%、NaCL7%、硝酸盐1.5%、碳粉0.8%。
复合废渣玻璃澄清助熔剂的化学成分组成为:
SiO25%、AL2O32.5%、CaO45%、SO2SO3O240%、R2O4%。
按上述各实施例原料配比,采用常规配料工艺均可获得本发明所述的玻璃澄清助熔剂。
Claims (3)
1.一种复合废渣玻璃澄清助熔剂,其特征是助熔剂原材料配方中去掉白砒、氧化锑、硫酸盐、氟化物、氧化铈,及上述澄清剂的复合物的有害原料,利用化工废渣和冶金废渣为主要原料,添加少量NaCl以及微量氧化剂和还原剂,获得无毒、低成本的玻璃澄清剂;其原料组分配比为:重量百分比化工废渣45%-58%、冶金废渣35%-49%、NaCl6%-10%、硝酸盐1%-2%、碳粉0.5%-1%,各组分含量之和为100%;其化学成分组成为:SiO23%-6%、Al2O32%-3%、CaO35%-50%、SO2SO3O245%-52%、R2O3%-5%,各组分含量之和为100%;其中,
化工废渣含如下成分:SiO2、CaO、Al2O3、Na2O、P2O5、SO3、Fe2O3;
冶金废渣含如下成分:SiO2、CaO、Al2O3、R2O、SO3、Fe2O3。
2.根据权利要求1所述的复合废渣玻璃澄清助熔剂,其特征是氧化剂为硝酸盐。
3.根据权利要求1所述的复合废渣玻璃澄清助熔剂,其特征是还原剂为碳粉。