CN102912400A - 不锈钢多色电泳涂装工艺 - Google Patents
不锈钢多色电泳涂装工艺 Download PDFInfo
- Publication number
- CN102912400A CN102912400A CN201210413241XA CN201210413241A CN102912400A CN 102912400 A CN102912400 A CN 102912400A CN 201210413241X A CN201210413241X A CN 201210413241XA CN 201210413241 A CN201210413241 A CN 201210413241A CN 102912400 A CN102912400 A CN 102912400A
- Authority
- CN
- China
- Prior art keywords
- color
- color electrophoresis
- stainless steel
- pattern
- electrophoresis
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种表面涂装工艺，具体涉及一种不锈钢多色电泳涂装工艺。该工艺包括以下步骤：S1.清洗待涂装不锈钢材料；S2.第一次彩色电泳，在材料表面涂装基色并生成绝缘的涂装层；S3.第一次激光雕刻，在材料表面雕刻第一图案的同时去除第一图案对应的涂装层；S4.第二次彩色电泳，为第一图案涂装颜色；其中，第一次彩色电泳、第二次彩色电泳涂装的颜色不相同。本发明通过将激光雕刻技术与彩色电泳涂装两种工艺相结合，在第一次彩色电泳涂装后的绝缘涂层上使用激光雕刻生成图案的同时去除了对应的绝缘涂层，之后进行第二次彩色电泳涂装即可在材料表面形成不同的颜色，使不锈钢产品表面呈现绚丽多彩的效果，同时具有环保高效的特点。
Description
技术领域
本发明涉及一种表面涂装工艺，具体涉及一种不锈钢多色电泳涂装工艺。
背景技术
目前在我们日常生活之中使用的电子产品外观装饰件大多数为金属或塑胶材料经过成型—喷涂—丝印等相关表面生产工艺制作加工而成。这些传统的生产工艺技术在人们日常使用的电子产品外观装饰件上已获得广泛的应用。
但是，这些工艺技术在生产时产生大量的粉尘以及气体，对环境造成污染，不是很环保；同时生产的产品颜色单一，表面缺少金属质感。随着人们审美观和环保意识的提升，传统的生产工艺技术已不能完全满足人们对电子产品外观装饰件要求。
现有的电泳涂装工艺具有涂层丰满、均匀、平整、光滑等优点，且电泳涂层的硬度、附着力、耐腐、冲击性能、渗透性能明显优于其它涂装工艺，同时非常环保。但是现有的电泳涂装工艺在工件表面形成的颜色单一，无法获得多种颜色的涂层。
发明内容
（一）要解决的技术问题
本发明的目的在于提供一种不锈钢多色电泳涂装工艺，用以解决现有表面涂装工艺生产的产品表面颜色单一的问题。
（二）技术方案
本发明技术方案如下：
一种不锈钢多色电泳涂装工艺，包括以下步骤：
S1.清洗待涂装不锈钢材料；
S2.第一次彩色电泳，在材料表面涂装基色并生成绝缘的涂装层；
S3.第一次激光雕刻，在材料表面雕刻第一图案的同时去除第一图案对应的涂装层；
S4.第二次彩色电泳，为第一图案涂装颜色；
其中，第一次彩色电泳、第二次彩色电泳涂装的颜色不相同。
优选的，所述不锈钢多色电泳涂装工艺在步骤S4之后还包括以下步骤：
S5.第二次激光雕刻，在材料表面雕刻第二图案的同时去除第二图案对应的涂装层；
S6.第三次彩色电泳，为第二图案涂装颜色；
其中，第一次彩色电泳、第二次彩色电泳、第三次彩色电泳涂装的颜色各不相同。
优选的，激光雕刻的第一图案以及第二图案没有重叠的部分。
优选的，所述步骤S1包括：
除油：除去材料表面油脂；
中和：使用稀硫酸溶液浸润材料；
纯水洗：去除材料表面的杂质离子，降低材料表面的电导率。
优选的，所述步骤S2、步骤S4以及步骤S6中所述的彩色电泳中电泳液固体份为9%至11%，PH值为7.4至8.5，电导率为600us/cm至800us/cm。
优选的，所述步骤S4以及步骤S6还分别包括在彩色电泳前对材料进行纯水洗。
优选的，所述步骤S2、步骤S4以及步骤S6还分别包括在彩色电泳后对材料进行纯水洗。
优选的，所述步骤S2、步骤S4以及步骤S6还包括对纯水洗后的材料进行烘干。
优选的，所述烘干的温度控制在150℃至180℃之间的任一温度。
优选的，所述步骤S4以及步骤S6还分别包括在烘干前使用脱水剂对纯水洗后的材料进行脱水处理。
（三）有益效果
本发明通过将激光雕刻技术与彩色电泳涂装两种工艺相结合，在第一次彩色电泳涂装后的绝缘涂层上使用激光雕刻生成图案的同时去除了对应的绝缘涂层，之后进行第二次彩色电泳涂装即可在材料表面形成不同的颜色，使不锈钢产品表面呈现绚丽多彩的效果，同时具有环保高效的特点。
附图说明
图1是本发明的一种不锈钢多色电泳涂装工艺的流程图。
具体实施方式
下面结合附图和实施例，对发明的具体实施方式做进一步描述。以下实施例仅用于说明本发明，但不用来限制本发明的范围。
如图1所示的一种不锈钢多色电泳涂装工艺，包括以下步骤：
S1.清洗待涂装不锈钢材料；
冲压成型后的产品表面有少量油污和杂质，这些会严重影响电泳效果，因此在电泳前必须要进行清洗处理，目的是除去残留在产品表面的油污和杂质，使产品表面干净，同时调整产品表面的电导率。
清洗过程主要包括
除油：除去材料表面油脂；
中和：使用稀硫酸溶液浸润材料；
纯水洗：去除材料表面的杂质离子，降低材料表面的电导率。
具体作业步骤、工艺参数以及作业细节如表1中所示。
表1 清洗待涂装不锈钢材料
S2.第一次彩色电泳，在材料表面涂装灰色基色并生成绝缘的涂装层,之后对材料进行纯水洗，然后使用脱水剂对纯水洗后的材料进行脱水处理，最后在150℃至180℃之间的任一温度的恒温条件下对材料进行烘干，同时使涂装层固化；具体作业步骤、工艺参数以及作业细节如表2中所示。
表2 第一次彩色电泳以及后续处理
S3.第一次激光雕刻，在材料表面雕刻第一图案的同时去除第一图案对应的涂装层，使第一图案部分可以导电，从而进行电泳涂装。
实际作业步骤为：首先在激光雕刻机输入端中输入第一图案的CAD图档；然后将烘干后的材料定位在激光雕刻机工作台面上，调整激光雕刻机的参数：功率为85%-95%、频率为28-38KHz、速度为1500±100mm/s、填充线间距为0.05-0.08mm，完成参数调整后启动激光雕刻开关，激光雕刻机自动完成在材料表面的雕刻任务同时去除了第一图案对应的涂装层。
S4.首先对完成第一次激光雕刻的材料进行纯水洗，去除激光雕刻过程中产生的杂质，同时调整第一图案部分的电导率；其次进行第二次彩色电泳，为第一图案涂装蓝色并生成绝缘的涂装层,然后对材料进行纯水洗，然后使用脱水剂对纯水洗后的材料进行脱水处理，最后在150℃180℃之间的任一温度的恒温条件下对材料进行烘干，同时使涂装层固化；具体作业步骤、工艺参数以及作业细节如表3中所示。
表3 第二次彩色电泳以及后续处理
进一步的，不锈钢多色电泳涂装工艺在步骤S4之后还包括以下步骤：
S5.第二次激光雕刻，在材料表面雕刻第二图案的同时去除第二图案对应的涂装层，使第一图案部分可以导电，从而进行电泳涂装；在激光雕刻过程中要确保的第一图案以及第二图案没有重叠的部分，避免损伤第一次彩色电泳的效果。
实际作业步骤为：首先在激光雕刻机输入端中输入第二图案的CAD图档；然后将烘干后的材料定位在激光雕刻机工作台面上，调整激光雕刻机的参数：功率为60%-70%、频率为32-40KHz、速度为900±50mm/s、填充线间距为0.06-0.08mm，完成参数调整后启动激光雕刻开关，激光雕刻机自动完成在材料表面的雕刻任务同时去除了第二图案对应的涂装层。
S6.首先对完成第二次激光雕刻的材料进行纯水洗，去除激光雕刻过程中产生的杂质，同时调整第二图案部分的电导率；其次进行第三次彩色电泳，为第二图案涂装红色并生成绝缘的涂装层,然后对材料进行纯水洗，然后使用脱水剂对纯水洗后的材料进行脱水处理，最后在150℃至180℃之间的任一温度的恒温条件下对材料进行烘干，同时使涂装层固化；具体作业步骤、工艺参数以及作业细节如表4中所示。
表4 第三次彩色电泳以及后续处理
本发明的不锈钢多色电泳涂装工艺具有以下优点：
1.该工艺操作方便，很容易使不锈钢产品表面呈现绚丽多彩的彩色电泳效果。
2.该工艺使不锈钢表面金属质感增强，产品外观比使用其他涂装工艺更加光滑、美观、色彩多样。
3.使用该工艺加工的不锈钢多色电泳产品具有很好的耐磨性、抗腐蚀性和耐指纹效果。
4.该工艺生产过程环保无粉尘以及气体污染。
以上实施方式仅用于说明本发明，而并非对本发明的限制，有关技术领域的普通技术人员，在不脱离本发明的精神和范围的情况下，还可以做出各种变化和变型，因此所有等同的技术方案也属于本发明的保护范畴。
Claims (10)
1.一种不锈钢多色电泳涂装工艺，其特征在于，包括以下步骤：
S1.清洗待涂装不锈钢材料；
S2.第一次彩色电泳，在材料表面涂装基色并生成绝缘的涂装层；
S3.第一次激光雕刻，在材料表面雕刻第一图案的同时去除第一图案对应的涂装层；
S4.第二次彩色电泳，为第一图案涂装颜色；
其中，第一次彩色电泳、第二次彩色电泳涂装的颜色不相同。
2.根据权利要求1所述的不锈钢多色电泳涂装工艺，其特征在于，所述不锈钢多色电泳涂装工艺在步骤S4之后还包括以下步骤：
S5.第二次激光雕刻，在材料表面雕刻第二图案的同时去除第二图案对应的涂装层；
S6.第三次彩色电泳，为第二图案涂装颜色；
其中，第一次彩色电泳、第二次彩色电泳、第三次彩色电泳涂装的颜色各不相同。
3.根据权利要求2所述的不锈钢多色电泳涂装工艺，其特征在于，激光雕刻的第一图案以及第二图案没有重叠的部分。
4.根据权利要求1所述的不锈钢多色电泳涂装工艺，其特征在于，所述步骤S1包括：
除油：除去材料表面油脂；
中和：使用稀硫酸溶液浸润材料；
纯水洗：去除材料表面的杂质离子，降低材料表面的电导率。
5.根据权利要求2所述的不锈钢多色电泳涂装工艺，其特征在于，所述步骤S2、步骤S4以及步骤S6中所述的彩色电泳中电泳液固体份为9%至11%，PH值为7.4至8.5，电导率为600us/cm至800us/cm。
6.根据权利要求2所述的不锈钢多色电泳涂装工艺，其特征在于，所述步骤S4以及步骤S6还分别包括在彩色电泳前对材料进行纯水洗。
7.根据权利要求6所述的不锈钢多色电泳涂装工艺，其特征在于，所述步骤S2、步骤S4以及步骤S6还分别包括在彩色电泳后对材料进行纯水洗。
8.根据权利要求7所述的不锈钢多色电泳涂装工艺，其特征在于，所述步骤S2、步骤S4以及步骤S6还包括对纯水洗后的材料进行烘干。
9.根据权利要求8所述的不锈钢多色电泳涂装工艺，其特征在于，所述烘干的温度控制在150℃至180℃之间的任一温度。
10.根据权利要求8所述的不锈钢多色电泳涂装工艺，其特征在于，所述步骤S4以及步骤S6还分别包括在烘干前使用脱水剂对纯水洗后的材料进行脱水处理。