CN102911608A - Dyeing and polishing wax - Google Patents
Dyeing and polishing wax Download PDFInfo
- Publication number
- CN102911608A CN102911608A CN 201210426887 CN201210426887A CN102911608A CN 102911608 A CN102911608 A CN 102911608A CN 201210426887 CN201210426887 CN 201210426887 CN 201210426887 A CN201210426887 A CN 201210426887A CN 102911608 A CN102911608 A CN 102911608A
- Authority
- CN
- China
- Prior art keywords
- dyeing
- polishing
- cured
- saponification liquor
- artwork
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to dyeing and polishing wax, of which components in mix proportions by weight are respectively: 2-4 saponified liquid, 4-6 alcohol, 1-3 carbon black and 4-6 graphite powder, wherein components in the saponified liquid in mix proportions by weight are respectively: 4-6 vegetable fat and 0.5-1.5 sodium hydroxide. According to the invention, the components adopt green and environment-friendly raw materials and have no pollution and toxic side effect, the preparation technology is simple and easy, and the preparation cost is low; when the dyeing and polishing wax is used, production can be carried out by people by only using a brush and a towel, the use is convenient and practical, the production efficiency is high, the product quality of handicraft articles after being dyed and polished is good, the external appearance and the colour and lustre are beautiful, and the production cost is approximately 2 RMB Yuan/m2*2 (calculation of two sides) by adopting the invention.
Description
Technical field
The invention belongs to the building decoration engineering technology field, relate to a kind of dyeing polishing that is applied in the metal such as copper, zinc, lead, iron and tin and the nonmetal inlaid technique cured.
Background technology
In building decoration engineering, adopt inlay with metal and nonmetal inlaid together, with the grace that improves artistic pattern and practical.Because the nonmetallic existence such as glass, jewel and pearl, traditional manufacture craft all are that the product color of producing like this is single take the metal primary colors as the main pattern that forms, competitive power is poor.For solving this problem of appearance, producer's active research adopts methods such as electroplating, spray paint both at home and abroad, makes product color that larger selection arranged, but because the existence of nonmetallic substance, scrap rate is high in electroplating process, and is of low grade, spray paint because of the existence of soldering opening can't the assumed appearance pool consistent.
As everyone knows, electroplating and spraying paint is the rich and influential family of contaminate environment, can make nonmetal coming off in electroplating process, and production cost is about 60 yuan/square metre; When spraying paint, owing to nonmetallic existence, be easy to the nonmetal pollution of being inlayed, and front need to the covering nonmetal by a large amount of manpower of cost of spraying paint, this explained hereafter cost is heavy, yields poorly, and production efficiency is low, is eliminated by industry already.
Summary of the invention
In order to overcome the above-mentioned shortcoming of prior art
,The dyeing polishing of the invention provides a kind of formulation green environmental protection, simple for process, cost of manufacture is low, practicality easy to use, production efficiency are high, good product quality and appearance luster are beautiful is cured.
The technical solution adopted for the present invention to solve the technical problems is: a kind of dyeing polishing is cured, and its component and weight proportion are respectively: saponification liquor 2~4, alcohol 4~6, carbon black 1~3 and Graphite Powder 99 4~6; Component in the described saponification liquor and weight proportion are respectively Vegetable oil lipoprotein 4~6, sodium hydroxide 0.5~1.5.
Preparing the cured method of above-mentioned dyeing polishing is: according to said components and proportioning, adopt first Vegetable oil lipoprotein, sodium hydroxide to add water and carry out saponification, make saponification liquor; After getting again saponification liquor and adding the water heating for dissolving, add respectively alcohol, carbon black, Graphite Powder 99 mixing and emulsifying, making the cured product of dyeing polishing.
The cured using method of above-mentioned dyeing polishing is: first with the boutique made through the clean airing of pickling, again according to selected color and luster, the cured product of dyeing polishing is added an amount of water be coated in and inlay on the good artwork, wipe to fat liquid with sisal hemp and parch, just finish polishing and dyeing.
During batch production, the artwork after the dyeing polishing is put into baking box be heated to 45~55 ℃ of fixation; When family produces, the artwork after the dyeing polishing put tan by the sun in the sun fixation.
Positively effect of the present invention is: component is selected the environmental protection raw material, pollution-free, have no side effect, preparation is simple, cost of manufacture is low, only need a wiping and a towel just can produce during use, practicality easy to use, production efficiency are high, and the handicraft product quality after the dyed polishing is good, appearance luster is beautiful, selects production cost of the present invention to be about the two-sided calculating of 2 yuan/square metre * 2(), because wax liquid penetrates into metal surface through friction, so prolonged colour-fast.
Embodiment
The present invention is further described below in conjunction with embodiment.
A kind of dyeing polishing is cured, and its component and weight proportion are respectively: saponification liquor 2~4, alcohol 4~6, carbon black 1~3 and Graphite Powder 99 4~6; Component in the described saponification liquor and weight proportion are respectively Vegetable oil lipoprotein 4~6, sodium hydroxide 0.5~1.5.
Preparing the cured method of above-mentioned dyeing polishing is: according to said components and proportioning, adopt first Vegetable oil lipoprotein, sodium hydroxide to add water and carry out saponification, make saponification liquor, after getting again saponification liquor and adding the water heating for dissolving, add respectively alcohol, carbon black, Graphite Powder 99 mixing and emulsifying, make the cured product of dyeing polishing.
The cured using method of above-mentioned dyeing polishing is: first with the boutique made through the clean airing of pickling, again according to selected color and luster, the cured product of dyeing polishing is added an amount of water to be coated in and to inlay on the good artwork, wipe to fat liquid with sisal hemp and to parch, just finish polishing and dyeing, the artwork that will dye during batch production after the polishing is put into baking box and is heated to 50 ℃ of left and right sides fixation, and will dye when producing artwork after polishing of family is put and tanned by the sun in the sun fixation.
Component of the present invention is selected the environmental protection raw material, pollution-free, have no side effect, preparation is simple, cost of manufacture is low, only need a wiping and a towel just can produce during use, practicality easy to use, production efficiency are high, handicraft product quality after the dyed polishing is good, appearance luster is beautiful, because wax liquid penetrates into metal surface through friction, so prolonged colour-fast.
Embodiment 1:
A kind of dyeing polishing is cured, and its component and weight proportion are respectively: saponification liquor 3, alcohol 5, carbon black 2 and Graphite Powder 99 5; Component in the described saponification liquor and weight proportion are respectively Vegetable oil lipoprotein 5, sodium hydroxide 1.
The preparation method is: adopt first Vegetable oil lipoprotein 50 grams, sodium hydroxide 10 grams, water 500 grams to carry out saponification; Get again saponification liquor 30 grams and add water 500 grams, add alcohol 50 grams, carbon black 20 grams, Graphite Powder 99 50 gram mixing and emulsifyings after the heating for dissolving, make the cured product of dyeing polishing.During use, wipe to fat liquid with sisal hemp and to parch, just finish polishing and dyeing (boutique needs the clean airing of pickling can wipe cured), batch production can be put into baking box and is heated to 50 ℃ of left and right sides fixation, family produces to put tans by the sun fixation in the sun, and product color is naturally beautiful.Select production cost of the present invention to be about the two-sided calculating of 2 yuan/square metre * 2().
Claims (4)
1. a dyeing polishing is cured, it is characterized in that component and weight proportion are respectively: saponification liquor 2~4, alcohol 4~6, carbon black 1~3 and Graphite Powder 99 4~6; Component in the described saponification liquor and weight proportion are respectively Vegetable oil lipoprotein 4~6, sodium hydroxide 0.5~1.5.
2. preparation is dyeed as claimed in claim 1 and is polished cured method, it is characterized in that processing step is: according to said components and proportioning, adopt first Vegetable oil lipoprotein, sodium hydroxide to add water and carry out saponification, make saponification liquor; After getting again saponification liquor and adding the water heating for dissolving, add respectively alcohol, carbon black, Graphite Powder 99 mixing and emulsifying, making the cured product of dyeing polishing.
3. as claimed in claim 1 cured application of dyeing polishing, it is characterized in that: first with the boutique made through the clean airing of pickling, again according to selected color and luster, the cured product of dyeing polishing is added an amount of water to be coated in and to inlay on the good artwork, wipe to fat liquid with sisal hemp and to parch, just finish polishing and dyeing.
4. the as claimed in claim 3 cured application of dyeing polishing is characterized in that: when batch production, the artwork after the dyeing polishing is put into baking box be heated to 45~55 ℃ of fixation; When family produces, the artwork after the dyeing polishing put tan by the sun in the sun fixation.