CN102911420B - Ldpe用复合环保阻燃剂及ldpe阻燃塑料 - Google Patents

Ldpe用复合环保阻燃剂及ldpe阻燃塑料 Download PDF

Info

Publication number
CN102911420B
CN102911420B CN201210410912.7A CN201210410912A CN102911420B CN 102911420 B CN102911420 B CN 102911420B CN 201210410912 A CN201210410912 A CN 201210410912A CN 102911420 B CN102911420 B CN 102911420B
Authority
CN
China
Prior art keywords
ldpe
friendly
retardant
flame retardant
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210410912.7A
Other languages
English (en)
Other versions
CN102911420A (zh
Inventor
宋国新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai huge rock mysorethorn industry Co., Ltd
Original Assignee
Shanghai Taohong Chemical Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Taohong Chemical Technology Co Ltd filed Critical Shanghai Taohong Chemical Technology Co Ltd
Priority to CN201210410912.7A priority Critical patent/CN102911420B/zh
Publication of CN102911420A publication Critical patent/CN102911420A/zh
Application granted granted Critical
Publication of CN102911420B publication Critical patent/CN102911420B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种LDPE用复合环保阻燃剂及LDPE阻燃塑料，所述LDPE用复合环保阻燃剂，由下述重量份的组分组成：三甲硅基甲基膦酸二甲酯10-20份、氰尿酸三聚氰胺30-50份、三氧化二锑10-20份、氢氧化铝40-60份。所述LDPE阻燃塑料，由下述组分按重量份组成：LDPE树脂100份，LDPE用复合环保阻燃剂20-40份。本发明的LDPE用复合环保阻燃剂，不含卤素，具有良好的阻燃功能，主要用作薄膜产品，还用于注塑制品，医疗器具，药品和食品包装材料，吹塑中空成型制品等。

Description

LDPE用复合环保阻燃剂及LDPE阻燃塑料
技术领域
本发明涉及一种阻燃剂及LDPE塑料，尤其涉及一种LDPE用复合环保阻燃剂及LDPE阻燃塑料。
背景技术
火是人类文明的象征，它在人类生活中的应用曾推动了历史的进步，但同时它又能在顷刻间吞噬大量社会财富，危害人们的生命安全。据统计，全世界每年发生火灾约为500余万起，近10万人丧生于火海之中，数以亿计的财产遭到破坏，无数人们失去了他们的亲人。
在我国，火灾形势同样不容乐观，一些重大火灾事故频频发生。例如，2010年11月15日，上海市静安区的一栋28层公寓大楼发生重大火灾。官方调查起因为无证电焊工违章操作、引起住宅脚手架上各种尼龙网、聚氨酯泡沫等易燃材料迅速燃烧，酿成58人遇难，70人受伤的惨剧。
绝大多数的塑料都是可燃性物质，而塑料的建筑材料、交通运输材料、家用电器材料等都需要塑料制品不燃烧，有良好的阻燃性能，要求塑料在大火中的发烟度要小。为此，在塑料配方中，选择添加阻燃剂就变得非常重要了。
对阻燃剂的要求：
（1）要有良好的阻燃功能，用量很少就能明显起到阻燃作用；
（2）阻燃剂加入后不能影响塑料的机械强度，特别是不能降低塑料制品的热变形温度、力学温度及电绝缘性能；
（3）同树脂的相容性要好，在塑料制品中不迁移、不析出、不被萃取；
（4）在高温熔融成型及热成型加工工程中，不发生分解，也不与其他材料发生反应；
（5）在塑料中易于分散均匀，耐候性好，持久性好，使塑料具有长期阻燃性。
可见，塑料中阻燃剂的选择，是一个非常复杂的过程，必须综合考虑上述各项因素。在现有的教科书中给出了例如：保护膜机理、不然气体机理、冷却机理和终止链锁反应机理等机理，这些可以对阻燃剂进行选择提供一个模糊的方向，但是却无法提供真正有效的帮助。
发明内容
针对现有技术中存在的上述不足，本发明所要解决的技术问题之一是提供一种LDPE用复合环保阻燃剂。
本发明所要解决的技术问题之二是提供一种LDPE阻燃塑料。
本发明所要解决的技术问题，是通过如下技术方案实现的：
一种LDPE用复合环保阻燃剂，由下述重量份的组分组成：三甲硅基甲基膦酸二甲酯10-20份、氰尿酸三聚氰胺30-50份、三氧化二锑10-20份、氢氧化铝40-60份。
将三甲硅基甲基膦酸二甲酯、氰尿酸三聚氰胺、三氧化二锑和氢氧化铝搅拌混合均匀，即可制得该LDPE用复合环保阻燃剂。
本发明还提供了一种LDPE阻燃塑料，由下述组分按重量份组成：LDPE树脂100份，LDPE用复合环保阻燃剂20-40份。
按配比称取LDPE树脂和LDPE用复合环保阻燃剂，混合均匀后，采用本行业通用方法熔融混炼、挤出造粒，即获得LDPE阻燃塑料。
LDPE，中文名称：低密度聚乙烯英文名称：low density polyethylene。低密度聚乙烯度聚乙烯是一种塑料材料，它适合热塑性成型加工的各种成型工艺，成型加工性好。LDPE主要用途是作薄膜产品，还用于注塑制品，医疗器具，药品和食品包装材料，吹塑中空成型制品等。
本发明的LDPE阻燃塑料的耐热性及阻燃性较优异，且制备工艺简单，产品成本低，产品的综合性能较优异。
本发明的LDPE用复合环保阻燃剂具有良好的阻燃功能，与LDPE的相容性好，在LDPE中不迁移、不析出、不被萃取，易于分散均匀，耐候性好，持久性好，高温熔融成型及热成型加工工程中，不发生分解，制得的LDPE阻燃塑料热变形温度、力学温度及电绝缘性能等性能并未受到影响，塑料具有长期阻燃性。
具体实施方式
三甲硅基甲基膦酸二甲酯，CAS号：13433-42-6。其英文名称为：Phosphonic acid,P-[(trimethylsilyl)methyl]-,dimethyl ester。
氰尿酸三聚氰胺，英文名称melamine cyanurate，中文别名：三聚氰胺焦磷酸盐；无卤阻燃剂MPP；三聚氰胺氰尿酸；MCA；无卤阻燃润滑剂，CAS号：37640-57-6。
实施例1LDPE用复合环保阻燃剂的制备
称取：三甲硅基甲基膦酸二甲酯15公斤、氰尿酸三聚氰胺40公斤、三氧化二锑15公斤、氢氧化铝50公斤。
将三甲硅基甲基膦酸二甲酯、氰尿酸三聚氰胺、三氧化二锑和氢氧化铝搅拌混合均匀，即可制得该LDPE用复合环保阻燃剂。
实施例2LDPE阻燃塑料的制备
称取LDPE树脂100公斤和实施例1制备的LDPE用复合环保阻燃剂30公斤，混合均匀后，采用本行业通用方法熔融混炼、挤出造粒，即获得LDPE阻燃塑料。
比较例
称取：磷酸三(2-氯丙基)酯15公斤、氰尿酸三聚氰胺40公斤、三氧化二锑15公斤、氢氧化铝50公斤，混合均匀，制得复合环保阻燃剂。
称取LDPE树脂100公斤和上述复合环保阻燃剂30公斤，混合均匀后，采用本行业通用方法熔融混炼、挤出造粒，即获得LDPE阻燃塑料。
测试例
对空白例，实施例2和比较例进行测试，具体数据见表1。其中，空白例为纯LDPE，未添加任何阻燃剂。
表1：LDPE阻燃塑料阻燃性能测试表
本发明的LDPE阻燃塑料的耐热性及阻燃性较优异，且制备工艺简单，产品成本低，产品的综合性能较优异。
本发明的LDPE用复合环保阻燃剂，不含卤素，具有良好的阻燃功能，与LDPE的相容性好，在LDPE中不迁移、不析出、不被萃取，易于分散均匀，耐候性好，持久性好，高温熔融成型及热成型加工工程中，不发生分解，制得的LDPE阻燃塑料热变形温度、力学温度及电绝缘性能等性能并未受到影响，塑料具有长期阻燃性。
空白例、实施例2和比较例中的LDPE均选用中石化茂名生产的DFDA-7042LLDPE。

Claims (2)

1.一种LDPE用复合环保阻燃剂，其特征在于，由下述重量份的组分组成：三甲硅基甲基膦酸二甲酯10-20份、氰尿酸三聚氰胺30-50份、三氧化二锑10-20份、氢氧化铝40-60份。
2.一种LDPE阻燃塑料，其特征在于，由下述组分按重量份组成：LDPE树脂100份，权利要求1所述的LDPE用复合环保阻燃剂20-40份。
CN201210410912.7A 2012-10-25 2012-10-25 Ldpe用复合环保阻燃剂及ldpe阻燃塑料 Expired - Fee Related CN102911420B (zh)