CN102903963A - 一种复合盐电解液 - Google Patents

一种复合盐电解液 Download PDF

Info

Publication number
CN102903963A
CN102903963A CN2012104240791A CN201210424079A CN102903963A CN 102903963 A CN102903963 A CN 102903963A CN 2012104240791 A CN2012104240791 A CN 2012104240791A CN 201210424079 A CN201210424079 A CN 201210424079A CN 102903963 A CN102903963 A CN 102903963A
Authority
CN
China
Prior art keywords
content
percent
salt electrolyte
salt
complex salt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012104240791A
Other languages
English (en)
Inventor
秦飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2012104240791A priority Critical patent/CN102903963A/zh
Publication of CN102903963A publication Critical patent/CN102903963A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种复合盐电解液，其特征在于：包括以下组份，各组分重量百分比为：镁盐，含量6.7%～8.1%；铝盐，含量：5.8%～7.5%；钠盐，含量：0.5%～2.0%；硫酸亚锡，含量：0.01%～1.0%；聚四氟乙烯乳液，含量：0.05%～0.5%；气相二氧化硅，含量：0.5%～5.0%；聚乙烯乳液，含量：0.02%～0.2%；硫酸，含量：39.2%～48.3%；余量为去离子水。本发明的优点是：克服了铅酸电池的阴极极板板结和因硫酸铅化所致的容量早衰等问题，始终保持极板较高的比容量，亦能使用在普通铅酸电池中，起到相同作用。

Description

一种复合盐电解液
技术领域
本发明涉及一种复合盐电解液。
背景技术
常规的铅酸电池使用硫酸电解液，为了防止阴极硫酸铅化和板结，采取在阴极膏中添加硫酸钡和腐植酸、木素磺酸等添加剂。这些添加剂起到了应有的效果，但也造成一些不良影响，如化成比较困难，化成效果差，电池的低温性能不佳等。因此，需要一种新的技术方案来解决上述技术问题。
发明内容
本发明的目的在于提供一种复合盐电解液，其能够克服铅酸电池的阴极极板板结和因硫酸铅化所致的容量早衰等问题，始终保持极板较高的比容量，亦能使用在普通铅酸电池中，起到相同作用。
为解决上述技术问题，本发明是通过以下技术方案来实现的：
一种复合盐电解液，包括以下组份，各组分重量百分比为：镁盐，含量6.7%～8.1%；铝盐，含量：5.8%～7.5%；钠盐，含量：0.5%～2.0%；硫酸亚锡，含量：0.01%～1.0%；聚四氟乙烯乳液，含量：0.05%～0.5%；气相二氧化硅，含量：0.5%～5.0%；聚乙烯乳液，含量：0.02%～0.2%；硫酸，含量：39.2%～48.3%；余量为去离子水。
所述镁盐为碳酸镁或硝酸镁；所述铝盐为硝酸铝或氢氧化铝；所述钠盐为无水硫酸钠。
所述电解液中还可以加入总重量1.5%～3.5%的缓蚀剂。
所述缓蚀剂为膦羧酸或琉基苯并噻唑。
所述硫酸的重量百分比浓度为38%～50%。
本发明根据铅酸蓄电池的充放电原理，极板始终在海绵铅和硫酸铅，二氧化铅和硫酸铅之间转化，上述的技术方案始终围绕着如何使生成的硫酸铅晶粒细化疏松，并且能够有效地可逆转化来进行。采用本发明的电解液可在海绵铅颗粒表面形成带正电荷的离子包覆层，在离子的静电力作用下，就可以克服阴极极板海绵铅的团聚作用，使极板保持应有的较大的容量，从而提高电池的性能。
本发明的优点是：克服了铅酸电池的阴极极板板结和因硫酸铅化所致的容量早衰等问题，始终保持极板较高的比容量，亦能使用在普通铅酸电池中，起到相同作用。
具体实施方式
实施例1
一种复合盐电解液，包括以下组份，各组分重量百分比为：碳酸镁，含量6.7%；硝酸铝，含量：7.5%；无水硫酸钠，含量：2.0%；硫酸亚锡，含量：0.01%；聚四氟乙烯乳液，含量：0.05%；气相二氧化硅，含量： 5.0%；聚乙烯乳液，含量： 0.2%；38%的硫酸，含量： 48.3%；膦羧酸，含量：1.5%；余量为去离子水。
实施例2
一种复合盐电解液，包括以下组份，各组分重量百分比为：硝酸镁，含量8.1%；氢氧化铝，含量：5.8%；无水硫酸钠，含量：2.0%；硫酸亚锡，含量： 1.0%；聚四氟乙烯乳液，含量：0.05%；气相二氧化硅，含量：0.5%；聚乙烯乳液，含量：0.02%；50%的硫酸，含量：39.2%；余量为去离子水。
实施例3
一种复合盐电解液，包括以下组份，各组分重量百分比为：硝酸镁，含量7.0%；硝酸铝，含量：6.5%；无水硫酸钠，含量：1.5%；硫酸亚锡，含量：0.5%；聚四氟乙烯乳液，含量：0.25%；气相二氧化硅，含量：2.2%；聚乙烯乳液，含量：0.12%；45%的硫酸，含量：42.3%；琉基苯并噻唑，含量：2.1%，余量为去离子水。

Claims (5)

1.一种复合盐电解液，其特征在于：包括以下组份，各组分重量百分比为：镁盐，含量6.7%～8.1%；铝盐，含量：5.8%～7.5%；钠盐，含量：0.5%～2.0%；硫酸亚锡，含量：0.01%～1.0%；聚四氟乙烯乳液，含量：0.05%～0.5%；气相二氧化硅，含量：0.5%～5.0%；聚乙烯乳液，含量：0.02%～0.2%；硫酸，含量：39.2%～48.3%；余量为去离子水。
2.根据权利要求1所述的一种复合盐电解液，其特征在于：所述镁盐为碳酸镁或硝酸镁；所述铝盐为硝酸铝或氢氧化铝；所述钠盐为无水硫酸钠。
3.根据权利要求1所述的一种复合盐电解液，其特征在于：所述电解液中还可以加入总重量1.5%～3.5%的缓蚀剂。
4.根据权利要求3所述的一种复合盐电解液，其特征在于：所述缓蚀剂为膦羧酸或琉基苯并噻唑。
5.根据权利要求1所述的一种复合盐电解液，其特征在于：所述硫酸的重量百分比浓度为38%～50%。
CN2012104240791A 2012-10-31 2012-10-31 一种复合盐电解液 Pending CN102903963A (zh)