CN102876259A - 电梯金属部件用防腐胶 - Google Patents

电梯金属部件用防腐胶 Download PDF

Info

Publication number
CN102876259A
CN102876259A CN2012103630723A CN201210363072A CN102876259A CN 102876259 A CN102876259 A CN 102876259A CN 2012103630723 A CN2012103630723 A CN 2012103630723A CN 201210363072 A CN201210363072 A CN 201210363072A CN 102876259 A CN102876259 A CN 102876259A
Authority
CN
China
Prior art keywords
parts
modified polystyrene
metal component
elevator
elevator metal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103630723A
Other languages
English (en)
Inventor
徐再忠
双华
屠永其
芦伟荣
顾军
吴春荣
计小红
徐洪生
徐晨宇
陈晓东
朱雪林
吕凤娟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Fen Lake Elevator Co Ltd
Original Assignee
Suzhou Fen Lake Elevator Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Fen Lake Elevator Co Ltd filed Critical Suzhou Fen Lake Elevator Co Ltd
Priority to CN2012103630723A priority Critical patent/CN102876259A/zh
Publication of CN102876259A publication Critical patent/CN102876259A/zh
Pending legal-status Critical Current

Abstract

电梯金属部件用防腐胶，其特征在于包括以重量份计的以下组分：异氰酸酯改性的聚苯乙烯5-10、纳米陶土1-5、硬脂酸盐1-5、二氯甲烷10-20、酚醛树脂1.5-3.5、防老剂1-5。将改性聚苯乙烯、酚醛树脂溶于二氯甲烷，加热至50-65℃，反应1-2h，加入其他的组份，混合均匀、研磨机研磨，即可。本发明的密封胶，具有耐腐蚀、耐磨、耐燃烧、耐老化，机械强度高、具有较好的弹性和优异的耐磨耗性，机械性能优越，且价格便宜。

Description

电梯金属部件用防腐胶
技术领域
    本发明涉及一种电梯装饰面板用涂料，具体地讲是涉及一种防腐密封胶。
背景技术
电梯安装后期和完成后一段时间内，因为调试与使用不能长时间停在顶层，而且现场通水一般较迟不能提前杜绝管网因施工质量而造成的漏水，电梯轿厢在组装时，轿厢操作面板底盒的接缝处、底盒两侧和背面的孔，等部位需要用胶密封，最好是采用具有防腐功能的密封胶。
发明内容
    本发明所要解决的技术问题是提供一种电梯金属部件用防腐胶。
为解决上述技术问题，本发明是这样实现的 ：
电梯金属部件用防腐胶，包括以重量份计的以下组分：改性聚苯乙烯50-100、纳米陶土10-50、硬脂酸盐 1-5、二氯甲烷10-20、酚醛树脂1.5-3.5、防老剂1-5 。
所述的改性聚苯乙烯是异氰酸酯改性的聚苯乙烯。
电梯金属部件用防腐胶的制备方法：将改性聚苯乙烯、酚醛树脂溶于二氯甲烷，加热至50-65℃，反应1-2h，加入其他的组份，混合均匀、研磨机研磨，即可。
本发明的密封胶，具有耐腐蚀、耐磨、耐燃烧、耐老化，机械强度高、具有较好的弹性和优异的耐磨耗性，机械性能优越，且价格便宜。
具体实施方式
下面结合具体实施方式对本发明做进一步的详细说明。
实施例1-4制电梯金属部件用防腐胶采用的组分的含量如表1（单位：g）： 异氰酸酯改性的聚苯乙烯自制，制备方法参照雷闰盈等，改性聚苯乙烯系列涂料，《涂料工业》1992年第04期。
表1
  实施例1 实施例2 实施例3 实施例4
异氰酸酯改性的聚苯乙烯 50 60 80 100
纳米陶土 10 50 20 40
硬脂酸盐 1 1.5 2.5 5
二氯甲烷 10 20 15 18
酚醛树脂 1.5 2.0 3.0 3.5
防老剂 1 5 4 3
断裂伸长率% 460 470 485 469
拉伸强度% 2.8 2.9 3.1 3.0
恢复率% 96 95 97 98
邵A硬度 48.0 49.0 50.0 50.1
外观 白色 白色 白色 白色
将改性聚苯乙烯、酚醛树脂溶于二氯甲烷，加热至50-65℃，反应1-2h，加入其他的组份，混合均匀、研磨机研磨，即可。
上述具体实施方式不以任何形式限制本发明的技术方案，凡是采用等同替换或等效变换的方式所获得的技术方案均落在本发明的保护范围。   

Claims (3)

1.电梯金属部件用防腐胶，其特征在于包括以重量份计的以下组分：改性聚苯乙烯5-10、纳米陶土1-5、硬脂酸盐 1-5、二氯甲烷10-20、酚醛树脂1.5-3.5、防老剂1-5。
2.根据权利要求1所述的电梯金属部件用防腐胶，其特征在于所述的改性聚苯乙烯是异氰酸酯改性的聚苯乙烯。
3.基于权利要求1或2所述的电梯金属部件用防腐胶的制备方法：将改性聚苯乙烯、酚醛树脂溶于二氯甲烷，加热至50-65℃，反应1-2h，加入其他的组份，混合均匀、研磨机研磨，即可。
CN2012103630723A 2012-09-26 2012-09-26 电梯金属部件用防腐胶 Pending CN102876259A (zh)